Photopolymerization synthesis of polyacrylic acid dispersant with methoxysilicon end groups and its application in a nano‐SiO2 aqueous system

In order to improve the dispersity and stability of the nano‐SiO₂ aqueous system with high solid content, a kind of polyacrylic acid dispersant with methoxysilicon end groups (KH590‐PAA) was synthesized by photopolymerization of acrylic acid (AA) initiated with (3‐mercaptopropyl)trimethoxysilane (KH590). After adding KH590‐PAA into the nano‐SiO₂ aqueous dispersion system (20 wt% solid content), the viscosity and the curing time of the system were measured with a rotational viscometer and the inverted bottle method. Moreover, the dispersion mechanism of KH590‐PAA for the nano‐SiO₂ aqueous system was researched by measuring the adsorption capacity, the particle size and the zeta potential of the nanoparticles with a conductivity meter, dynamic light scattering, SEM and TEM, respectively. The results showed that the methoxysilicon groups in KH590‐PAA could react with hydroxyl groups on the surface of nano‐SiO₂ in the process of stirring, which enhanced the adsorption capacity of the dispersant and then increased the surface charge of the particles. Therefore, electrostatic repulsion and steric hindrance effects between the SiO₂ nanoparticles could be further enhanced by adding the KH590‐PAA dispersant, and then the nano‐SiO₂ aqueous system exhibited better dispersity and stability. Besides, the dispersion properties of SiO₂ nanoparticles in water were closely related to the addition amount and the molecular weight of the KH590‐PAA dispersant. © 2018 Society of Chemical Industry     

Manganese ferrite-polyaniline hybrid materials: Electrical and magnetic properties

Magnetic MnFe₂O₄ nanopowders were synthesized by an original solvothermal method in the absence and in the presence of tetra-n-butylammonium bromide (TBAB) and Tween 80 (TW) as surfactants. Manganese ferrite/polyaniline (PANI) hybrid materials were synthesized by in situ polymerization of aniline on the surface of MnFe₂O₄ using ammonium persulfate as oxidant. The purpose of the study was to investigate the influence of the two surfactants on the properties of the MnFe₂O₄ powders and of their composites with PANI. The specific surface area, the cumulative surface area of pores and the cumulative volume of pores are influenced by the nature of surfactant in case of MnFe₂O₄ powders and are higher by comparison to those of the MnFe₂O₄/PANI hybrid materials. The values of saturation magnetization in case of MnFe₂O₄ powders are higher than those of the hybrid materials and are not influenced by the surfactant nature. These features revealed that MnFe₂O₄ powders can be efficiently used as adsorbents for the purification of wastewaters. The values of the electrical conductivity of the composites exhibit a significant increase in comparison to the MnFe₂O₄ powders and depend on the surfactant nature. The highest value of electrical conductivity was achieved by the composite obtained using Tween 80 as surfactant (σ_DC = 54.5·10^?5S?m^?1) which was close to that of PANI (σ_DC = 61.2·10^?5 S?m^?1). The fact that the magnetic and electric properties of the synthesized MnFe₂O₄/PANI composites can be changed by design, demonstrate the high potential of these materials to be used in magneto-electric applications.     

Effect of hyperbranched poly(citric polyethylene glycol) with various polyethylene glycol chain lengths on starch plasticization and retrogradation

A series of hyperbranched poly(citric polyethylene glycol) (PCPEG) materials with varied polyethylene glycol (PEG) chain lengths as plasticizers were mixed with maize starch (MS) via cooking and film‐forming. The structure, pasting property, plasticization, aging property, moisture absorption and compatibility of plasticized starches were studied by means of Fourier transform infrared spectroscopy, X‐ray diffraction, rapid viscosity analysis, tension testing, moisture absorption measurements and scanning electron microscopy. Compared with PEG and citric acid, PCPEG was more effective in promoting starch chain movement and inhibiting the retrogradation of starch film. Also, PCPEG/MS had smaller moisture content. The longer the plasticizer chain, the better were the aging resistance and moisture resistance of starch. But with an increase of PEG chain length, mechanical properties of PCPEG/MS deteriorated and the compatibility between PCPEG and MS decreased. The hyperbranched derivative of PEG with longer chain exhibited improved plasticization and compatibility with starch. © 2019 Society of Chemical Industry