Calorimetric study of ytterbium orthovanadate YbVO4 polycrystalline ceramics

The heat capacity of ytterbium orthovanadate was first measured by adiabatic calorimetry in the temperature range T?=?12.28–344.06?K. No obvious anomalies were observed on the curve obtained. The values of standard thermodynamic functions in the temperature range T?=?0–400 K were calculated. Based on low-temperature calorimetry data obtained, previously published data on the high-temperature heat capacity of ytterbium orthovanadate were corrected. The anomalous contribution to heat capacity for YbVO₄ was compared with the data known for YbPO₄.     

Preparation of nanocrystalline nickel oxide from nickel hydroxide using spark plasma sintering and inverse Hall-Petch related densification

Nanocrystalline nickel oxide (NiO) was prepared from nickel hydroxide by Spark plasma sintering (SPS) and the mechanisms involved in the densification of NiO were studied. Reverse precipitated nickel hydroxide powders were SPS processed at 400, 600 and 700?°C with 70?MPa pressure. Pure NiO with 12?nm crystallite size formed after 400?°C sintering process. However NiO grains had grown to 18 and 38?nm after 600 and 700?°C sintering respectively. NiO pellets prepared using 600 and 700?°C SPS sintering schedules had relative densities of 83% and 94% respectively. Two displacement rate regimes were observed during densification of NiO in both 600 and 700?°C sintering processes. Decomposition of nickel hydroxide and particle sliding of NiO led to first displacement rate maximum while inverse Hall-Petch based plastic deformation facilitated densification during the constant second displacement rate regime. No densification occurred during sintering holding times indicating the limited role that diffusion played during densification.     

Similarities and differences between male and female novice designers on color‐concept associations for warnings,action required,and signs and equipment status messages

This research examined the male and female novice designers toward color associations for the concepts used for ‘warnings’, ‘action required’, and ‘signs and equipment status’ through a questionnaire‐based study. A total of 178 Hong Kong Chinese final year undergraduate design students (89 males and 89 females) participated in the study. The test used required the participants to indicate their choice of one of nine colors to associations with each of 38 concepts in a color‐concept table, so that any one color could be associated with any one of the concepts. For both male and female groups of novice designers, chi‐square tests revealed a strong color association for each concept tested in this study (P < .05). The results showed males and females agreed on some color‐concept association stereotypes which were therefore gender neutral. The male and female novice designers had the same color associations and similar levels of stereotype strengths for 21 concepts. The nine strongest and therefore most useful color‐concept association stereotypes for both male and female novice designers were: red‐danger, red‐fire, red‐hot, red‐stop, red‐emergency, red‐error, blue‐cold, blue‐male, and green‐exit. However, the male and female novice designers had different color association stereotypes for the standby (green vs. yellow), emergency exit (green vs. red), and toxic (purple vs. black) concepts, and the strengths of the 14 remaining associations for both groups were not at equivalent levels. Overall, it is anticipated that the findings of this study will act as a useful reference for novice designers and other design practitioners to optimize color coding in the design of ‘warnings’, ‘action required’, and ‘signs and equipment status’ messages.     

CuInS2/SiNWs/Si composite material for application as potential photoelectrode for photoelectrochemical hydrogen generation

This work aims at developing a new composite material based on nanosized semiconducting CuInS₂ (CIS) particles combined with silicon nanowires grown on a silicon substrate (SiNWs/Si) for photoelectrochemical (PEC)-splitting of water. The CIS particles were prepared via a colloidal method using N-methylimidazole (NMI) as the solvent and an annealing treatment. The SiNWs were obtained by chemical etching of silicon (100) substrates assisted by a metal. The CIS/SiNWs/Si composite material was obtained by deposition of an aliquot of a suspension of CIS particles onto the SiNWs/Si substrate, using spin coating followed by a drying step. The XRD pattern demonstrated that CuInS₂ grows in the tetragonal/chalcopyrite phase, while SiNWs/Si presents a cubic structure. The SEM images show semi-spherical particles (～10 nm) distributed on the surface of silicon nanowires (～10 μm). The EIS measurements reveal n-type conductivity for CIS, SiNWs/Si and CIS/SiNWs/Si materials, which could favour the oxidation reaction of water molecules.     

Effects of anion and cation doping on the thermoelectric properties of n-type PbS

The PbCl_xS_1-x and Pb_1-xBi_xS (x? =?0–0.05) bulks were fabricated with a facile method of hydrothermal synthesis and microwave sintering, and the effect of anionic and cationic donors on the thermoelectric performance of PbS was investigated. Although Cl^? and Bi³⁺ both effectively improved the thermoelectric properties of n-type PbS, more excellent thermoelectric performance was obtained from Cl^? doped samples because of higher electrical property and lower thermal conductivity at higher temperature (T? >?600?K). The thermoelectric figure of merit (ZT) reaches 1.04 for PbCl_0.015S_0.985 at 800?K and increases with temperature increasing without sign of saturation, which is probably the highest value ever reported for single-phase polycrystalline n-type PbS. The results also indicate that the hydrothermal synthesis and microwave sintering can realize anion doping as well as cation doping for n-type PbS at low cost, and PbS should be a robust alternative for PbTe thermoelectric materials.     

Strain Concentration Effect in Cu–Al–Ni Single Crystals under a Longitudinal Bending Force

The behavior of a superelastic Cu?14.2% Al?4%Ni single crystal in the case of high reversible strains under a longitudinal bending force was investigated. The effect of strain confinement along the crystal length was revealed and studied. The highest reversible strains (up to 10%) were shown to be confined within the central part of the bent crystal.     

Technical and economic analysis of solvent-based lithium-ion electrode drying with water and NMP

Processing lithium-ion battery (LIB) electrode dispersions with water as the solvent during primary drying offers many advantages over N-methylpyrrolidone (NMP). An in-depth analysis of the comparative drying costs of LIB electrodes is discussed for both NMP- and water-based dispersion processing in terms of battery pack $/kWh. Electrode coating manufacturing and capital equipment cost savings are compared for water vs. conventional NMP organic solvent processing. A major finding of this work is that the total electrode manufacturing costs, whether water- or NMP-based, contribute about 8–9% of the total pack cost. However, it was found that up to a 2?×?reduction in electrode processing (drying and solvent recovery) cost can be expected along with a $3–6?M savings in associated plant capital equipment (for a plant producing 100,000 10-kWh Plug-in Hybrid Electric Vehicle (PHEV) batteries) using water as the electrode solvent. This paper shows a different perspective in that the most important benefits of aqueous electrode processing actually revolve around capital equipment savings and environmental stewardship and not processing cost savings.     

Microstructures and mechanical properties of B4C-TiB2-SiC composites fabricated by ball milling and hot pressing

B₄C-TiB₂-SiC composites were fabricated via hot pressing using ball milled B₄C, TiB₂, and SiC powder mixtures as the starting materials. The impact of ball milling on the densification behaviors, mechanical properties, and microstructures of the ceramic composites were investigated. The results showed that the refinement of the powder mixtures and the removal of the oxide impurities played an important role in the improvement of densification and properties. Moreover, the formation of the liquid phases during the sintering was deemed beneficial for densification. The typical values of relative density, hardness, bending strength, and fracture toughness of the composites reached 99.20%, 32.84?GPa, 858?MPa and 8.21?MPa?m^1/2, respectively. Crack deflection, crack bridging, crack branching, and microcracking were considered to be the potential toughening mechanisms in the composites. Furthermore, numerous nano-sized intergranular/intragranular phases and twin structures were observed in the B₄C-TiB₂-SiC composite.     

Preparation of ZrC/SiC porous self-supporting monoliths via sol-gel process using polyethylene glycol as phase separation inducer

We present a straightforward method via sol-gel process using polyethylene glycol (PEG) as phase separation inducer to prepare zirconium carbide/silicon carbide (ZrC/SiC) porous monoliths. Organic/inorganic hybrid gels are prepared using zirconium oxychloride, furfuryl alcohol, and tetraethyl orthosilicate as major starting materials. In the presence of PEG, crack-free hybrid monoliths are obtained by drying the wet gels under ambient pressure, whereas in the absence of PEG, the wet gels break into pieces as expected. PEG plays a key role in maintaining the macroscopic shape of the monoliths. After ceramization at 1300–1500?°C, ZrC/SiC porous monoliths are obtained. SEM and mercury intrusion porosimetry data show that PEG also has strong influence on the microstructures of the monoliths. The compressive strengths of the ceramic monoliths are in the range of 0.3 to 0.7?MPa. And their compressive behavior starts to differ due to the changes in their microstructures, especially the pore structure.     

Molten salt synthesis of MAX phases in the Ti-Al-C system

The molten salt method was used to synthesise the MAX phase compounds Ti₂AlC and Ti₃AlC₂ from elemental powders. Between 900–1000?°C, Ti₂AlC was formed alongside ancillary phases TiC and TiAl, which decreased in abundance with increasing synthesis temperature. Changing the stoichiometry and increasing the synthesis temperature to 1300?°C resulted in formation of Ti₃AlC₂ alongside Ti₂AlC and TiC. The type of salt flux used had little effect on the product formation. The reaction pathway for Ti₂AlC was determined to be the initial formation of TiC_1-x templating on the graphite and titanium aluminides.