1,5-己二烯交联烯烃聚合物的合成及其抗剪切稳定性

以金属配合物为催化剂、1,5-己二烯为交联剂,采用本体聚合法合成了交联超高相对分子质量烯烃类聚合物(简称交联聚合物)。用傅里叶变换红外光谱、核磁共振、凝胶渗透色潜表征交联聚合物的结构和相对分子质量。用旋转黏度计和超声波仪研究了1,5-己二烯用量对交联聚合物溶液表观黏度的影响及交联聚合物的相对分子质量对交联聚合物溶液抗剪切稳定性的影响。实验结果表明,在最佳聚合条件(单体80mL、助催化剂0．4mL、CS-1催化剂0．090g、1,5-己二烯0．40mL、0℃、24 b)下所合成的交联聚合物的重均相对分子质量为7．7×106,数均相对分子质量3．6×106。加入少量1,5-己二烯能提高交联聚合物的抗剪切能力,同时也能提高交联聚合物的相对分子质量。交联聚合物的相对分子质量越大,抗剪切稳定性越好。1,5-己二烯用量约为0．1 mL时(单体40 mL),交联聚合物溶液的表观黏度达到最大值(16．8 mPa·s)。     

Small‐Sized High‐Power PIN Diode Switch with Defected Ground Structure for Wireless Broadband Internet

This letter presents a small‐sized, high‐power single‐pole double‐throw (SPDT) switch with defected ground structure (DGS) for wireless broadband Internet application. To reduce the circuit size by using a slow‐wave characteristic, the DGS is used for the quarter‐wave (°/4) transmission line of the switch. To secure a high degree of isolation, the switch with DGS is composed of shunt‐connected PIN diodes. It shows an insertion loss of 0.8 dB, an isolation of 50 dB or more, and power capability of at least 50 W at 2.3 GHz. The switch shows very similar performance to the conventional shunt‐type switch, but the circuit size is reduced by about 50% simply with the use of DGS patterns.     

水泥浆失水制约下套管与井眼间隙的研究

通过对水泥浆失水规律的室内试验分析以厦对注水泥顶替过程中水泥浆失水桥堵套管与井眼间隙问题的研究，建立了顶替过程中滤失层不发生水泥浆失水而桥堵环形空间的临界失水量计算模型，提出了调配水泥浆失水性能和确定合理套管井眼间隙的具体方法，对注水泥现场施工和井身结构设计具有一定的指导意义。     

Corrosion morphology of AZ91D exposed in an atmospheric environment

The focused ion beam technique was employed to investigate the atmospheric corrosion morphology of AZ91D. It was found that the α matrix of the alloy was preferentially corroded in the areas adjacent to intermetallic phases. The most interesting finding was that the corrosion products in corrosion cavities were pelletlike, which has never been reported before.     

Structure, properties, and thermal stability of nanocrystallite Fe-Ti-N soft magnetic films

We deposited Fe-Ti-N magnetic films with a high sputtering power of 7 W/cm/sup 2/. When the composition of the films was in the range of Fe-Ti(3.9 at.%)-N(8.8 at.%) to Fe-Ti(3.3 at.%)-N(13.5 at.%), the films were composed of /spl alpha/' and Ti/sub 2/N precipitates. With the addition of nitrogen, 4/spl pi/M/sub s/ became higher than that of pure iron, reaching a maximum of 23.8 kG. At the same time, H/sub c/ was reduced to a minimum of 1.12 Oe. The best films can meet the needs of the recording head in dual-element giant magnetoresistive/inductive heads, yielding high storage density (10 Gb/in/sup 2/). The incorporation of N in /spl alpha/-Fe brought about the /spl alpha/' phase with its higher saturation magnetization. Ti additions inhibited the equilibrium decomposition /spl alpha/'/spl rarr//spl alpha/+/spl gamma/'. Because H/sub C//sup D//spl prop/D/sup 6/, where D is average grain diameter, grain size control is very important. The nitrogen induces severe distortion of the /spl alpha/' lattice, which can cause the grains to break into pieces and reduce the grain size. High sputtering power also led to the formation of fine grains, with diameter in the order of 14 nm. Probably Ti/sub 2/N is preferentially precipitated on the grain boundary, pinning the grain boundary and stabilizing the grain size during high-temperature heat treatment. The temperature limit for stability of the structure and its associated low coercivity was not less than 520/spl deg/C.     

Inhibition of microbial growth in ready‐to‐eat food stored at ambient temperature by modified atmosphere packaging

This study was undertaken to develop a modified atmosphere package to control microbial growth in ready‐to‐eat (RTE) products stored at ambient temperature. Ethanol and/or limonene associated with modified atmosphere (CO₂ : O₂ : N₂ = 30% : 5% : 65%) was used to inhibit the growth of total air‐borne microorganisms and Escherichia coli in RTE products stored at 25°C. The results indicated that 0.05% ethanol vapour in the headspace was effective to inhibit the growth of air‐borne microorganisms and E. coli at 25°C for 72 h in a model study, and the effectiveness was related to ethanol content. Both 73 ppm limonene and 0.05% ethanol vapour enhanced the bacteriostatic effect of modified atmosphere in RTE sushi roll products, and no off‐flavour was detected using this formulated gas; however, no significant inhibitory effect was observed for RTE cold noodle products. This study concludes that combinations of carbon dioxide, ethanol or limonene vapours are effective to inhibit microbial growth in RTE food at ambient temperature, and the outcome may be due to the hurdle effect. Copyright © 2003 John Wiley & Sons, Ltd.     

Synthesis of amphiphilic magnetic microspheres by dispersion copolymerization of styrene and poly(ethylene oxide) macromonomer

Amphiphilic magnetic microspheres ranging in diameter from 5 to 100 µm were prepared by dispersion copolymerization of styrene and poly(ethylene oxide) vinylbenzyl (PEO‐VB) macromonomer (MPEO) in the presence of Fe₃O₄ magnetic fluid. The effects of various polymerization parameters on the average particle size were systematically investigated. The average particle size was found to increase with increasing styrene concentration and initiator concentration. It also increased with decreasing stabilizer concentration and molecular weight of MPEO. The content of the hydroxyl groups localized in the microspheres ranged from 0.01 to 0.2 mmol g^?1. © 2003 Society of Chemical Industry