Floating-island TFT leakage caused by process step reduction

The leakage mechanism for a top-gate thin-film transistor (TFT) produced using the fewest process steps in the industry is analyzed in order to achieve a high-contrast liquid crystal display (LCD). Using a T-shaped TFT structure, the OFF and ON channel lengths are defined independently, so that the leakage can be reduced with no ON current decrease     

A Varshamov-Gilbert bound for a class of formally self-dual codesand related quantum codes

It is proved that a class of q-ary (2n,n) formally self-dual codes obtained from symmetric matrices over GF (q), contains codes that meet the Varshamov-Gilbert bound. The codes are self-dual with respect to the symplectic inner product and yield quantum codes encoding one state with n q-ary qubits and having minimum distance proportional to n     

Intermetallic compounds formed at the interface between liquid indium and copper substrates

The interfacial reactions between liquid In and Cu substrates at temperatures ranging from 175°C to 400°C are investigated for the applications in bonding recycled sputtering targets to their backing plates. Experimental results show that a scallop-shaped Cu₁₆In₉ intermetallic compound is found at the Cu/In interface after solder reactions at temperatures above 300°C. A double-layer structure of intermetallic compounds containing scallop-shaped Cu₁₁In₉ and continuous CuIn is observed after the Cu/In interfacial reaction at temperatures below 300°C. The growth of all these intermetallic compounds follows the parabolic law, which implies that the growth is diffusion-controlled. The activation energies for the growth of Cu₁₆In₉, Cu₁₁In₉, and CuIn intermetallic compounds calculated from the Arrhenius plot of growth reaction constants are 59.5, 16.9, and 23.5 kJ/mole, respectively.     

The influence of viewing distance on subjective impairment assessment

In this paper, the influence of viewing distance on subjective assessment of the impairment in video sequences is investigated. Subjective tests using the double-stimulus impairment scale variant II (DSIS II) method have been conducted at viewing distances of 5H (where H stands for the screen height) and 3H, respectively. Several statistical measures have been used to analyze the influence, including correlations and ANOVA (analysis of variance) tests. The results reveal that there is a very high correlation between the subjective scores, the variances are similar under the two viewing distances, the means of subjective data at these two viewing distances are the same, and there is no interaction between the viewing distance and the other two factors, i.e., the codec system and the source sequence. Throughout the tests, there is no evidence that a closer viewing distance such as 3H will vary the subjective test result statistically significantly.     

Nondestructive evaluation of the characteristics of degraded materials using backward radiated ultrasound

The frequency dependency of Rayleigh surface wave is investigated indirectly by measuring the angular dependency of the backward radiation of the incident ultrasonic wave in two kinds of degraded specimens by scuffing or corrosion. Then, the frequency dependency is compared with the residual stress distribution or the corrosion-fatigue characteristics for the scuffed or corroded specimens, respectively. The width of the backward radiation profile increases with the increase of the variation in residual stress distribution for the scuffed specimens. In the corroded specimens, the profile width decreases with the increase of the effective aging layer thickness and is inversely proportional to the exponent, m, in the Paris’ law that can predict the crack size increase due to fatigue. The result observed in this study demonstrates high potential of backward radiated ultrasound as a tool for nondestructive evaluation of subsurface gradient of material degradation generated by scuffing or corrosion.     

Interface stability during displacement reactions between Cu<Subscript>2</Subscript>O and Co<Subscript>1−<Emphasis Type="Italic">X</Emphasis></Subscript>Fe<Subscript><Emphasis Type="Italic">X</Emphasis></Subscript> alloys at 1223 K

The stability of the reactive interface during the solid-state displacement reaction, Cu₂O+Co_1−X Fe _X =2Cu+(Co_1−X Fe _X )O, is studied as a function of Co-Fe alloy composition at 1223 K. For X≤0.03, the reaction zone has a layered structure, and the cation diffusion in (Co, Fe)O is the rate-limiting step. The interface is unstable in the early stages of the reaction; the instability decreases with time as the oxide thickness increases, and the interface becomes planar at long times. The time required for the attainment of interface planarity increases with the value of X. The reaction kinetics are consistent with the available cation-diffusion data in (Co, Fe)O. For X≥0.045, the product zone is a composite of Cu+(Co, Fe)O, and the rate is limited by the oxygen transport in copper. The transition to interface instability occurs when the oxide can support a cation flux that exceeds the maximum possible oxygen flux in copper. During the reaction, composition gradients develop in (Co, Fe)O because of higher diffusion rates for iron than for cobalt.     

On the development of a direct method of determining the microcrack resistance curve

This report deals with direct observations of microcrack linkage at the crack tip prior to macroscopic crack initiation. It is shown that this process is directly linked to the inclusion distribution in the material and can be considered in terms of an R curve to describe microcrack development.     

Using motion from orthographic views to verify 3-D point matches

The specific problem addressed by the authors is how to detect the true match of a fourth point from among candidate matches in a situation in which three points have already been matched. The two sets of points to be matched are both subject to measurement errors. The depth error is more dominant than errors in the other two coordinates; however, the exact statistical distribution of the measurement errors is not known. The authors present a new method for solving the problem. The method is based on the technique of motion analysis using orthographic views. It discards the noisy z (depth) coordinates and uses only the x and y coordinates of the points to verify the match. The effect of depth errors on the motion estimate is completely prevented. Results show that this method is substantially more effective than previous methods that use all three coordinates     

Verification of a model for estimating the void fraction in a three-component randomly packed bed

The void fraction in a three-component randomly packed bed was calculated from the authors' model, and the calculated values were compared with published experimental data for spherical and irregularly shaped particles and with results from computer simulations. Results from the model were in good agreement with simulated and published experimental data.