Summary: Polyacrylonitrile (PAN) particles with micro‐size ranges (0.15–2 μm) were prepared by emulsion and dispersion polymerizationa and in supercritical carbon dioxide media. The PAN particles were blended with Nylon 6 (PA6) at 220 °C by using a miniature mixer; it was found that melt‐mixing was possible for PAN‐rich compositions as high as 70 wt.‐%. Blends were characterized by scanning electron microscopy, IR, viscosity measurements, differential scanning calorimetry, and dynamic mechanical thermal analysis (DMTA). The size and shape of original PAN particles were retained in PAN/PA6 blends. The useful range to blend PAN particles size was less than 1 μm in terms of shape retention of the PAN particles in blends. Blends with 40 wt.‐% PAN content were found to be melt‐processable. The elastic modulus was higher for PAN/PA6 blends than pure PA6.
SEM photograph of PAN‐SC/PA6 blend with a 40/60 weight ratio. 相似文献
High thermoelectric figure of merit semiconducting ceramics of n -type iron disilicide with modified local compositions have been developed. Sintering and annealing of the composite powder composed of iron disilicide and precipitated cobalt (II) hydroxide resulted in the dissolution of excess Co and oxygen into the iron disilicide phase. Excess Co segregated to the grain boundary region, while interstitially incorporated oxygen was distributed homogeneously in the microstructure. The maximum figure of merit achieved was 5.2 × 10−4/K at 673 K. 相似文献
Effects of hydrostatic extrusion on the thermal properties of polycarbonate (PC) and of high-impact polystyrene (HIPS) were studied using differential scanning calorimeter (DSC) measurements. A glass transition temperature (Tg) and a peak temperature were determined from the DSC curves for both PC and HIPS extrudates. The Tg values of the PC extrudates, with a percentage reduction in area, R, from 40 to 50%, change appreciably from the value for the as–received PC. The results of the hydrostatic extrusion of the PC billets suggest that a two stage deformation process of molecular chains may be involved. Shear-banding is observed for HIPS extrudates with R = 30 to 60%; this fact indicates that a sub-glass transition (β-transition) occurs at temperatures below Tg. It is suggested that the molecular chains of the HIPS extrudate with R = 70% are oriented in the direction of hydrostatic extrusion. The deformation mechanism of molecular chains caused by the hydrostatic extrusion is discussed. 相似文献
The catalytic activity of LaCoO3–-based mixed oxides for the oxidative coupling of methane has been tested by TPR and cyclic reaction. Characterization has been done by XRD, TGA and Mössbauer spectrometry. It is likely that the perovskite-crystal structure containing hypervalent metal ions has an important role and that unique structural oxygen species in the perovskite contribute to the partial oxidation of methane. 相似文献
The miscibility of poly(methyl methacrylate) (PMMA) and styrene-acrylonitrile random copolymers (SAN) blends was investigated on the basis of the Flory—Orwoll—Vrij equation of state theory. To obtain the equation of state parameters (P*, V*sp, T*: characteristic parameters), the pressure—volume—temperature (PVT) behaviour was measured for PMMA and a series of SANs with various acrylonitrile contents. The exchange energy parameter Xij was also calculated by fitting the theory to some phase diagrams of PMMA/SAN blends. The Flory—Huggins interaction parameter χ was separated into two contributions based on the equation of state theory for mixtures: the exchange energy term χinter and the free volume term χfree. Both the temperature and copolymer composition dependences of χinter and χfree were estimated by calculations using the equation of state parameters. There exists a region in which χinter is negative, leading to a miscibility window in PMMA/SAN blends. However, the immiscibility at high temperatures in the blends cannot be explained only by χinter; it is caused by the free volume contribution, χfree. The miscibility window behaviour in PMMA/SAN blends may be explained within the framework of the equation of state theory. 相似文献
Polymer blends of transparent poly(methyl methacrylate) and polystyrene become opaque due to light scattering at the boundaries of the two polymers. The polymer blend is light brown when it is illuminated by white light. The coloring depends on the spherical domain structures existing in the polymer blend. The coloring was analyzed by using the rigorous Mie theory. The Mie results were compared with the semiempirical results previously reported by the authors. The wavelength dependence of theoretical scattering efficiencies on radii of scattering spheres from 0.05 to 1.2 μm was obtained for polystyrene spheres in poly(methyl methacrylate) matrix, and vice versa. The scattering at the short wavelength region is stronger than at the long wavelength region. The scattering efficiencies become almost constant in the visible wavelength region for sufficiently large spheres. 相似文献
Hydrogel prepared by repetitive freezing and thawing of poly(vinyl alcohol) aqueous solution was chemically crosslinked with glutaraldehyde. The chemically crosslinked hydrogel hardly changed its physical appearance, and showed good elasticity and strength as original gel. However, after treating in boiling water, it swelled a little, depending on the condition of the chemical treatment. The melted gel thus obtained showed shape memorizing property, that is, it could firmly hold nearly 200% of strain, keeping its original high elasticity. The strain could be released very quickly (< 1 s) in boiling water, and the gel was suggested to be applied to a new type of gel actuator. X-ray diffraction study revealed that the melted gel does not necessarily reform the physical crosslinks in exactly the same manner as the original gel in the process of shape restoring, but the distribution of the physical crosslinks can be restored as they were. It was suggested that the chemical crosslinks which remember the distribution of the physical crosslinks plays a critical roll in the shape restoring process. 相似文献
Structure of x PbO–(100− x )SiO2 ( x =25–89) glasses has been investigated by means of the X-ray and neutron diffraction and 29Si MAS NMR measurements. In the radial distribution functions of all the glasses, the Pb–O correlation was observed at 0.23 nm, indicating that the PbO3 trigonal pyramids units do exist in the whole glass forming composition range. Furthermore the existence of the first Pb–Pb correlation at ∼0.385 nm in the whole composition range suggests that the basic structural unit is considered to be a Pb2O4 unit, which consists of the edge-shared PbO3 trigonal pyramids. These results strongly imply that the Pb2O4 units participate in the glass network constructed by SiO4 tetrahedra even at low PbO content. Differing from other lead-containing glass systems, these structural characteristics of Pb ions in the PbO–SiO2 glass system are responsible for the extremely wide glass-forming region. 相似文献
Flat packages (FPs) were formed from epoxy molding compounds with various physical properties using a transfer molding machine. The compounds were prepared by changing kinds and amounts of additives and addition methods. The thermal shock test was carried out by the following procedures. The plastic package was soaked alternately in liquid nitrogen (?196°) and in liquid solder (200°) in the cycle of 140s. The median life to crack initiation was defined to be the cycles when half of the specimens exhibited crack initiation. According to linear fracture mechanics, the following expression was obtained relating the median life N, thermal stress σt, and strength σb; N = C/σ·(σb/σt)m. We found the linear relation between logarithm of Nσ and logarithm of σb/σt for various packages, and estimated the values of C and m as 5 × 104 MPa2 and 5.5, respectively. The value of m was the same as that obtained for a dual-in-line package. 相似文献
The strength, S , of ceramic and glass fibers often can be estimated from fractographic investigation using the fracture mirror radius, r m, and the relationship S = A m/( r m)1/2, where A mis the "mirror constant." The present work estimates the value of A mfor Tyranno® Si-Ti-C-O fibers in situ in a three-dimensional woven SiC/SiC-based composite to be 2.50 ± 0.09 MPa·m1/2. This value is within the range of 2–2.51 MPa·m1/2 previously obtained for nominally similar Nicalon® Si-C-O fibers. 相似文献