Phase formation,structure and properties of light-weight aluminosilicate proppants based on clay-diabase and clay-granite binary mixes

One of the drawbacks of fusible clays is the narrow sintering interval due to a sharp increase in the amount of iron-silicate melt at a temperature of 1000–1100 °C, which hardens in the form of a glass phase upon cooling. This leads to a relatively low mechanical strength of the calcined samples and causes the danger of melting the granular material surface from such clays during the firing process. To increase the strength of samples of fusible clays, the influence of diabase and granitoid rocks was considered. It was found that the strengthening effect of diabase and granitoid rock additives in an amount of 20–50% in a mixture with fusible clay is due to an increase of total content of the crystalline phase (mullite, cristobalite and residual quartz) from 18–20% in clays without additives to 22–28 % - in mixtures with diabase and to 28–34% - with granitoid additives) at a temperature of 1050–1100 °C. This increase is due to the activation of synthesis processes of secondary mullite and crystallization from alkali-rich feldspar melt of amorphous silica, released from the structure of clay minerals. The established influence of the igneous rocks used made it possible to develop compositions and propose process flow sheet for producing aluminosilicate proppants based on fusible clays. The use of granitoid and diabase rocks in an amount of 20–70% with fusible clays produces lightweight aluminosilicate proppants with bulk density of 1.40–1.46 g/cm³ at temperature range of 1050–1100 °C, which can endure destructive pressures up to 34.5–52 MPa.     

Graphical Methodology to Study the Corona Onset Voltage for Electrostatic Precipitation of Nanoparticles

Theoretical Foundations of Chemical Engineering - The corona onset voltage is an important operating parameter in the electrostatic precipitation of nanoparticulate, however, its experimental...     

Some Molecular and Cellular Stress Mechanisms Associated with Neurodegenerative Diseases and Atherosclerosis

Chronic stress is a combination of nonspecific adaptive reactions of the body to the influence of various adverse stress factors which disrupt its homeostasis, and it is also a corresponding state of the organism’s nervous system (or the body in general). We hypothesized that chronic stress may be one of the causes occurence of several molecular and cellular types of stress. We analyzed literary sources and considered most of these types of stress in our review article. We examined genes and mutations of nuclear and mitochondrial genomes and also molecular variants which lead to various types of stress. The end result of chronic stress can be metabolic disturbance in humans and animals, leading to accumulation of reactive oxygen species (ROS), oxidative stress, energy deficiency in cells (due to a decrease in ATP synthesis) and mitochondrial dysfunction. These changes can last for the lifetime and lead to severe pathologies, including neurodegenerative diseases and atherosclerosis. The analysis of literature allowed us to conclude that under the influence of chronic stress, metabolism in the human body can be disrupted, mutations of the mitochondrial and nuclear genome and dysfunction of cells and their compartments can occur. As a result of these processes, oxidative, genotoxic, and cellular stress can occur. Therefore, chronic stress can be one of the causes forthe occurrence and development of neurodegenerative diseases and atherosclerosis. In particular, chronic stress can play a large role in the occurrence and development of oxidative, genotoxic, and cellular types of stress.     

Mechanisms and Kinetics of Separation of Impurities of Large and Small Particles in Gravity Flow of Granular Material

Chemical and Petroleum Engineering - The processes of separation of impurities of particles of different sizes are analyzed under conditions of irregularity of structural and kinematic parameters...     

Novel pearl millet couscous process for West African markets using a low-cost single-screw extruder

Traditional West African pearl millet couscous products are popular; however, their preparation is laborious, time-consuming and energy-demanding, involving agglomeration, steaming, drying and sieving steps. In this study, a process was developed to produce millet couscous using a high pressure, high temperature and low-cost single-screw extruder. The innovation was to directly process the cooked low-moisture extrudate to a couscous product by drying and milling to the appropriate particle size (ranging between 1 and 2 mm). Throughput for the traditional process as prepared for commercial sale is 50 kg per day, but with the same amount of labour, the extrusion process yields ~350 kg per day. A consumer sensory study held in Niamey (Niger) showed that the extruded millet couscous was comparable to traditional couscous, though this was dependent on selection of the proper millet variety. This novel extrusion process could stimulate small- to medium-scale manufacturing of couscous and couscous-type products in West Africa.     

Spray pressure variation effect on the properties of CdS thin films for photodetector applications

Herein, we report the photosensing property of CdS thin films. CdS thin films were coated onto glass substrates via a spray pyrolysis method using different spray pressures. Prepared films were characterized using X-ray diffraction (XRD), scanning electron microscopy (SEM), and optical and photoluminescence spectroscopy. XRD analysis demonstrated the growth of crystalline CdS films with crystallite sizes varying from 26 to 29 nm depending on the pressure. The SEM and EDAX analyses revealed nearly-stoichiometric CdS films with smooth surfaces and slight variation in grain morphology due to pressure changes. Optical measurements showed a direct bandgap varying from 2.37 eV to 2.42 eV due to pressure changes. A photodetector was also fabricated using the grown CdS films; the fabricated photodetector exhibited good performance depending on the spray pressure. A spray pressure of 1.5 GPa resulted in high photoresponsivity and external quantum efficiency.     

Corrosion behavior of T24, T92, VM12, and AISI 304 steels exposed to KCl–NaCl–K2SO4–Na2SO4 salt mixtures

The corrosion mechanisms of T24, T92, VM12, and AISI 304 steels are studied under the influence of NaCl–KCl, NaCl–Na₂SO₄, and KCl–K₂SO₄ salt mixtures in a dry air atmosphere at 650°C for 15 days. NaCl–KCl was the most aggressive deposit and AISI 304 stainless steel exhibited the highest corrosion resistance. There was no relation between the Cr content of the ferritic steels and their corrosion resistance in NaCl–KCl. In contrast, the resistance of high-Cr steels was better when exposed to NaCl–Na₂SO₄ and KCl–K₂SO₄. The high-Cr and the low-Cr steels were more susceptible to NaCl–Na₂SO₄ and to KCl–K₂SO₄, respectively.     

Photoluminescence of Gallate Glass-Ceramics: Al2O3 Influence

Glass and Ceramics - The influence of Al2O3 as an additive and the heat-treatment regime on the luminescence spectra of gallate glass-ceramics was investigated. It is shown that its luminescence...     

Predicting the Operational Efficiency of High-Pressure Roller Crushers

Russian Engineering Research - Models based on regression analysis for predicting the operational efficiency of high-pressure roller crushers are considered. A systematized and structured...     

Safety Devices Based on Smart Alloys

Journal of Machinery Manufacture and Reliability - A device based on smart alloys has been designed for use in machine building items, in particular, in nuclear engineering, for preventing...