Effect of doped Ni2+ on the dielectric properties of NiO-BaTiO3 composites

NiO-BaTiO₃ composites were prepared by sintering BaTiO₃ together with NiO in air at 1300°C. Microstructure and morphology of the composites were detected by XRD and SEM, and the dielectric properties were measured by LCZ meter. The results indicate that the perovskite phase is formed in fact in status of solid solution doped with Ni²⁺, although only a small amount of Ni ions can dissolve into the perovskite phase. Ni doping decreases the formation temperature of the composite without inhibiting the grain growth of the crystalline phase. The dielectric constant decreases sharply and the dielectric loss decreases smoothly with increasing Ni²⁺ below NiO addition of 0.5 wt.%. When NiO addition increases above 0.5 wt.%, the dielectric constant and loss correlate with mixing rule of the two phases. Meanwhile, the replacement of Ni²⁺ for Ti⁴⁺ decreases the Curie temperature of perovskite phase by 30°C.     

Adaptive robust control of uncertain time delay systems

The problem of adaptive robust control for uncertain linear systems with multiple delays occurring in the state variables is studied in this paper. The essential requirement for the uncertainties is that they satisfy matching conditions and are norm-bounded, but the bounds of the uncertainties are not necessarily known. An adaptive controller is developed based on linear matrix inequality technique and it is shown that the controller can guarantee the state variables of the closed loop system to converge, globally, uniformly and exponentially, to a ball in the state space with any pre-specified convergence rate. The effectiveness of our approach has been verified by its application in the control of river pollution process for the purpose of preserving standards of water constituents in streams.     

体外震波碎石术治疗中病人所受的体表剂量

在体外震波碎石术(ESWL)治疗中,需要用X线透视来判断结石的位置、大小及其粉碎情况,因此使患者受到X射线的照射。本文对在上海某医院接受ESWL治疗的134例肾脏结石患者所 受的体表剂量进行了调查测量。结果表明,患者受到的皮肤剂量当量平均为162mSv;所受剂量的大小与结石的大小与位置等因素有关。     

微波活化对橡胶沥青粘度及分子量的影响

为了探究胶粉微波辐射后对改性沥青粘度和分子量分布的影响,采用5种不同的微波时间对废胎胶粉进行活化处理,并制备胶粉改性沥青。通过布氏粘度和凝胶渗透色谱试验,得到胶粉改性沥青的粘度和分子量分布。结果表明:胶粉经过微波活化后,橡胶沥青粘度和大分子含量均有所下降,当胶粉活化时间为90s时,胶粉改性沥青的粘度和大分子含量均最小;橡胶沥青的粘度与其大分子含量有较强的相关性,随着大分子含量越高,沥青粘度越大。     

巷道开挖效应下围岩损伤演化规律及试验研究

为了研究巷道开挖卸荷引起的围岩损伤演化规律及力学响应机制,采用RMT-150试验机开展了白砂岩试件三轴加载-卸载-单轴再加载力学特性试验,建立了岩石三维损伤本构模型。根据损伤岩石单轴加载应力-应变曲线,分析其破坏模式,确定了单轴再加载强度、波速与初始轴压加载比的非线性关系。结果表明:(1)三轴应力作用下,岩石损伤演化过程分为5个阶段,即损伤稳定减小阶段、无损伤阶段、损伤稳定增长阶段、损伤加速增长阶段、损伤破坏阶段;(2)单轴再加载强度、波速与初始轴压加载比呈现3次非线性相关关系,从环向应变规律来看,损伤岩石表现出塑性硬化和塑性软化两种状态;(3)损伤岩石以张拉破坏为主,随着损伤变量值增加,破坏形式逐渐向剪切滑移破坏转化。通过对岩石损伤演化规律的研究,为工程围岩稳定性判别及预警提供理论依据。     

过硫磷石膏矿渣水泥路面基层材料微观结构及力学性能

在以大掺量湿磨改性磷石膏浆体、粒化高炉矿渣粉为主要原料制备过硫磷石膏矿渣水泥（PPSC）的基础上,以力学性能为导向,设计制备了过硫磷石膏矿渣水泥路面基层材料（PGBM）,并对其微观结构及力学性能进行了研究.结果发现：PPSC含有矿物相石英（α-SiO₂）、二水石膏（CaSO₄·2H₂O）和水化产物钙矾石（Ettringite）3种主要矿物成分;PPSC的矿物成分和微观结构特点影响着PGBM的无侧限抗压强度,进而影响PGBM的水稳性,但PGBM与PPSC的无侧限抗压强度增长率保持一致,且PGBM的抗冲刷能力与其无侧限抗压强度发展规律也具有一致性;不同配比的各组基层试件水稳性较好,其软化系数均大于90%;PPSC掺量为5%时,PGBM的7 d无侧限抗压强度即可满足路面基层强度的规范要求,而PPSC掺量为15%的PGBM在28 d龄期时出现无侧限抗压强度下降和冲刷量升高现象,分析原因是由于PPSC内部过量钙矾石的形成导致试件膨胀开裂所致.     

转子在线动平衡嵌入式控制系统开发与验证

为了快速、有效抑制由于质量不平衡引起的转子振动并在线监测转子的实时平衡状态,基于模块化设计思想设计了一种针对电磁式主动平衡装置的嵌入式在线自动平衡控制系统。使用数字信号处理器(digital signal processor,简称DSP)和现场可编程门阵列(field programmable gate array,简称FPGA)构建了一种快速平衡控制器,基于影响系数法建立了自适应平衡控制模型,采用C和C#语言分别开发了多线程的平衡控制软件和人机交互界面,针对某国产电主轴完成了整个系统功能的试验验证。结果表明:当主轴在3kr/min平稳运行时,通过该自平衡系统可将其振动大约降低43%。     

现代视角下探析建构的诗学表达

以肯尼斯·弗兰姆普敦的《建构文化研究》一书为理论背景,从"建构"与"建造的诗学"两者关系思考建构的内在意义,提出"理论"与"反理论"、"建构"与"非建构"两对看似悖论的主题并进行探讨,以此剖析"建构"的诗学表达,激发设计者对现代建筑的重新思辨,以期促进建筑理论的良性发展.     

铝锂合金晶间腐蚀敏感性与时效阶段的相关性

研究了不含Zn及0.72%Zn微合金化的Al-3.7Cu-1.15Li-0.5Mg合金T6态时效(150及175℃)不同时间后的晶间腐蚀行为,建立了其腐蚀-时效进程状态图。结果表明,Zn微合金化铝锂合金晶间腐蚀敏感性略低于不含Zn微合金化的铝锂合金。随时效进程的发展,铝锂合金腐蚀类型变化规律为:孔蚀或局部晶间腐蚀(时效早期),全面晶间腐蚀(欠时效阶段),局部晶间腐蚀(近峰时效阶段),孔蚀(过时效阶段)。晶间腐蚀深度随时效时间延长呈先增加而后降低的规律。时效时间延长,一方面晶界析出相逐渐粗化并且呈不连续分布,另一方面晶内T1相及θ相析出,晶内电位降低,晶界及晶内电位差减小,从而导致上述腐蚀类型的变化。     

MgO/SiO_2摩尔比对金刚石砂轮用陶瓷结合剂性能的影响

研究了Na-B-Al-Si-O系陶瓷结合剂中MgO/SiO2摩尔比对其性能的影响。研究表明,随着MgO/SiO2摩尔比从0.09增加到0.35,结合剂的耐火度从800℃降低到725℃,热膨胀系数先减小后增大,但MgO的加入能有效控制结合剂热膨胀系数只在小范围内变化。制备的砂轮试样抗折强度最高值达到95MPa,利用所研究的结合剂制备的砂轮比市售砂轮使用寿命提高25%。研究结果证明:减少碱金属氧化物含量、增大碱土金属氧化物含量是获得低耐火度、低热膨胀系数结合剂的一种有效方法。