Effect of hyperbranched poly(citric polyethylene glycol) with various polyethylene glycol chain lengths on starch plasticization and retrogradation

A series of hyperbranched poly(citric polyethylene glycol) (PCPEG) materials with varied polyethylene glycol (PEG) chain lengths as plasticizers were mixed with maize starch (MS) via cooking and film‐forming. The structure, pasting property, plasticization, aging property, moisture absorption and compatibility of plasticized starches were studied by means of Fourier transform infrared spectroscopy, X‐ray diffraction, rapid viscosity analysis, tension testing, moisture absorption measurements and scanning electron microscopy. Compared with PEG and citric acid, PCPEG was more effective in promoting starch chain movement and inhibiting the retrogradation of starch film. Also, PCPEG/MS had smaller moisture content. The longer the plasticizer chain, the better were the aging resistance and moisture resistance of starch. But with an increase of PEG chain length, mechanical properties of PCPEG/MS deteriorated and the compatibility between PCPEG and MS decreased. The hyperbranched derivative of PEG with longer chain exhibited improved plasticization and compatibility with starch. © 2019 Society of Chemical Industry     

餐饮废油生物柴油低温流动性的改进研究

使用气-质联用仪测定餐饮废油生物柴油(WCME)和-10号柴油(-10PD)的组成,使用冷滤点试验器和运动黏度试验器测定WCME的低温流动性,同时使用调合、添加低温流动性改进剂的方法改进WCME的低温流动性。实验结果表明,WCME主要由饱和脂肪酸甲酯和不饱和脂肪酸甲酯组成,质量分数分别为27.63%和71.81%;WCME冷滤点为0℃,运动黏度(40℃)为4.41mm2/s;WCME与-10PD调合后,冷滤点降低,其中B20的冷滤点最低,为-13℃,运动黏度随着WCME的体积分数的减少,逐渐接近-10PD的运动黏度。通过添加低温流动性改进剂,WCME,B10,B20的冷滤点分别从0,-8,-13℃降至-4,-26,-25℃。     

核电厂中间量程保护定值标定方法改进

基于目前中国改进型三环路压水堆（CPR1000）部分机组存在因中间量程电流饱和导致无法在48%额定功率（Pn）完成定值标定及核电厂大修经济性考虑，采用MCNP程序及核设计软件包SCIENCE，研究分析中间量程保护定值标定的新方法。分析结果表明，中间量程保护定值标定调整至30%Pn功率平台实施，采用改进方法标定的保护定值更接近于设计值。      

Improving the initialization speed for long-range NRTK in network solution mode

Initialization speed is one of the most important factors in network real time kinematic (NRTK) performance. Owing to the low correlation among the error s     

Effects of Prior Annealing on the Spark Plasma Sintering of Nanostructured Y2O3 Powders

The effects produced by annealing Y₂O₃ nanopowders on their spark plasma sintering (SPS) behavior are systematically investigated in this work. It is found that the annealed powders display higher sinterability with respect to the as‐received ones. Indeed, the maximum densification level reached from pristine powders is about 97.5%, whereas density decreases when further increasing either the sintering temperature or the dwell time. In contrast, the density of SPS products obtained from pretreated powder monotonically increases with temperature and processing time, thus leading to fully dense materials in 30 min at 1050°C and 60 MPa. Correspondingly, it is found that the annealing treatment markedly inhibits grain coarsening during SPS. Thus, dense translucent samples with grain size below 100 nm can be attained from annealed powders. On the other hand, white‐opaque specimens with significantly coarser microstructures (up to 1‐μm‐sized grains) are obtained when pristine powders are directly processed under the same sintering conditions. Furthermore, it is observed that the annealing treatment of SPS samples in air allows for graphite contamination removal, whereas no improvement in term of light transmittance is produced.