On the Feasibility of Growing Pb[(Zn1/3Nb2/3)0.91Ti0.09]O3 Single Crystals

Pb[(Zn_1/3Nb_2/3)_0.91Ti_0.09]O₃ (PZNT91/9) single crystals were grown by two methods: from solution using PbO as a self‐fluxing agent (SC method) and directly from the melt without fluxing (MC method). In both growth methods, an allomeric Pb[(Mg_1/3‐Nb_2/3)_0.69Ti_0.31]O₃ (PMNT69/31) single crystal was used as a seed. X‐ray diffraction patterns of ground crystals showed that phase‐pure perovskite PZNT91/9 single crystals were successfully fabricated by the above two methods. The composition of the crystals obtained by both the SC and MC methods was analyzed using X‐ray fluorescence, which confirmed that the crystal composition is close to the nominal value, although volatilization of PbO and segregation during crystal growth are inevitable. The MC PZNT91/9 crystals exhibit excellent piezoelectric properties, with the piezoelectric constant, d₃₃, in the range of 1800–2200 pC N^–1. This value is comparable to that of the SC crystals. However, the MC crystals show an abnormal dielectric behavior. In contrast with the SC crystals, in the MC crystals a much broader dielectric peak appears in the dielectric response curves, accompanied by a much lower peak temperature of around 105 °C. Furthermore, frequency dispersion is apparent over a much wider temperature range (even more apparent than in pure relaxors), where a large, i.e., about 70 °C, full width at half maximum (FWHM) for the dielectric peaks is observed in the dielectric response. It is speculated that such an unusual phenomenon correlates with defects, microinhomogeneities, and polar regions in the as‐grown MC crystals. The origins of this abnormality have not been interpreted in detail until now. However, optical observation of the domain structure confirms that both the SC and MC crystals possess complex structural states.     

Formation and inhibition of free radicals in electrically stressed and aged insulating polymers

Previous work has shown that prebreakdown, electrical aging, and breakdown phenomena are directly associated with charge carriers injected from electrical contacts and their subsequent dissociative trapping and recombination. In addition, the energy released from each trapping or recombination event is dissipated in the breaking of the bonds of macromolecules, thus forming free radicals and new traps in the electrically stressed insulating polymers, as predicted by Kao's model. It is this gradual degradation process that leads to electrical aging and destructive breakdown. New experimental results are presented to confirm previous findings and a new approach to inhibit the degradation process by the incorporation of suitable dopants into the polymer. The concentration of free radicals in the polymer increases with an increasing electric field at a fixed stress time of 250 h and with increasing stress time at a fixed electric field of 833 kV cm^?1. The concentration of free radicals is directly related to the concentration of new traps created by stress. However, when suitable dopants are incorporated, the initiation voltage for the occurrence of electrical treeing and the breakdown strength are both increased. The dopants tend to create shallow traps and have little effect on the deep trap concentration. This implies that the dopants act as free‐radical scavengers that tend to satisfy the unpaired electrons of the broken bonds, which create new acceptor‐like electron traps and new shallow traps. By doing so, the shallow traps screen the deep traps, thereby reducing the energy released during trapping and recombination and the probability of breaking the macromolecular bonds and causing structural degradation. © 2003 Wiley Periodicals, Inc. J Appl Polym Sci 89: 3416–3425, 2003     

Formulation of a ceramic ink for a wide-array drop-on-demand ink-jet printer

This paper describes the methodology for simulating a reprographic ink with a ceramic ink based on a commercially available zirconia powder for direct ceramic ink-jet printing. Of over-riding importance was matching viscosity and this was tested systematically by using a mineral oil–hexane binary system. Of secondary importance was adjustment of the pressure defect behind the nozzle to compensate for small differences in surface tension. The inks tested in the wide array print-head were based on low electrical conductivity liquids to avoid damage to the electroding system. The organic binder for the zirconia ink was paraffin wax and the dispersant was a hydroxystearic acid based polyester.     

Quantum mechanical effects on noise properties of nanoelectronic devices: application to Monte Carlo simulation

A discussion about the quantum mechanical effects on noise properties of ballistic (phase-coherent) nanoscale devices is presented. It is shown that quantum noise can be understood in terms of quantum trajectories. This interpretation provides a simple and intuitive explanation of the origin of quantum noise that can be very salutary for nanoelectronic engineers. In particular, an injection model is presented that, coupled with a standard Monte Carlo algorithm, provides an accurate modeling of quantum noise. As a test, the standard results of noise in tunneling junction devices are reproduced within this approach.     

面积坐标法构造含转角自由度的四结点膜元

以四边形面积坐标作为工具,构造了两个含转角自由度的广义协调四边形单元AQ4和lAQ4。它们通过强式分片检验,与同类单元相比,具有很高的计算精度,能消除梯形闭锁现象,有很强的抗网格畸变的能力。     

Nd3+:Y0.5Gd0.5VO4晶体生长和基本特性

Nd^3 :Y0.5Gd0.5VO4晶体作为一种新的激光材料，可以用中频感应加热提拉法生长。X射线粉末衍射分析表明它的结构与Nd^3 :YVO4晶体结构相同，它的晶格常数介于YVO4和NdVO4晶格常数之间。用ICP光谱法测定晶体中Nd^3 含量为0．8at％，分凝系数为0．8，与Nd^3 :GdVO4晶体中Nd^3 的分凝系数0．78相当；用称重法测定其密度为5．00g／cm^3；用稳态纵向热流法测出其室温热导率为12．5W／mK。实验表明Nd^3 :Y0.5Gd0.5VO4晶体有希望作为高功率ID泵浦激光晶体材料。     

Analysis of the Scattering Characteristic of Several Waveguide Components Using Boundary Element Method

Several kinds of waveguide components such as curved waveguide bends, arbitrary angle waveguide bends and T-junctions have been analyzed with boundary element method in this paper. A new discretization method for the boundary element method to solve the waveguide discontinuities has been given. The numerical results obtained agree well with the experimental results and numerical results in other literature. Especially, the scattering characteristics of Forded E-, H-plane T-junctions in 3mm band have been analyzed using boundary element method and the calculation results are presented.     

TEM Studies of High Temperature Corrosion Behaviour of TiAl Intermetallics with Surface Modifications

The oxidation/sulphidation behaviour of a Ti‐46.7Al‐1.9W‐0.5Si alloy with a TiAl₃ diffusion coating was studied in an environment of H₂/H₂S/H₂O at 850^oC. The kinetic results demonstrate that the TiAl₃ coating significantly increased the high temperature corrosion resistance of Ti‐46.7Al‐1.9W‐0.5Si. The SEM, EDX, XRD and TEM analysis reveals that the formation of an Al₂O₃ scale on the surface of the TiAl₃‐coated sample was responsible for the enhancement of the corroison resistance. The Ti‐46.7Al‐1.9W‐0.5Si alloy was also modified by Nb ion implantation. The Nb ion implanted and as received sampels were subjected to cyclic oxidation in an open air at 800^oC. The Nb ion implantation not only increased the oxidation resistance but also substantially improved the adhesion of scale to the substrate.     

Estimating crystallinity in high density polyethylene fibers using online Raman spectroscopy

Online Raman spectra, obtained at different points along the spin line during pilot‐scale nonisothermal melt spinning of high density polyethylene (HDPE) fibers, are presented for the first time. The fraction of the crystalline phase corresponding to each spectrum was determined from the normalized integrated intensity of the 1418 cm^?1 Raman band. It is well established that this band represents the orthorhombic crystalline phase in polyethylene. The estimates of percent crystallinity obtained from decomposition of the Raman spectrum were compared with the percent crystallinity from differential scanning calorimetry (DSC) measurements. It is concluded that online Raman spectroscopy can be successfully used to monitor the development of crystallinity in HDPE fibers as a function of distance from the spinneret. © 2003 Wiley Periodicals, Inc. J Appl Polym Sci 88: 545–549, 2003