Microwave dielectric properties of SrLa[Ga1−x(Mg0.5Ti0.5)x]O4 and SrLa[Ga1−x(Zn0.5Ti0.5)x]O4 (x = 0.2-0.8) ceramics

SrLa[Ga_1−x(R_0.5Ti_0.5)_x]O₄ (R = Mg, Zn) ceramics were prepared by a standard solid state sintering method. The single-phase ceramics with K₂NiF₄-type layered perovskite structure and I4/mmm space group were obtained, indicating that SrLa(R_0.5Ti_0.5) and SrLaGaO₄ can form the unlimited solid solutions. With increasing x for R = Mg and Zn, ε_r increases monotonously, the Qf value first increases and then decreases, while τ_f increases from a negative to a positive value. The optimized microwave dielectric properties were obtained as following: ε_r = 23.3, Qf = 89 400 GHz, τ_f = −0.8 ppm/°C for SrLa[Ga_0.6(Mg_0.5Ti_0.5)_0.4]O₄ and ε_r = 23.3, Qf = 76 200 GHz, τ_f = 0.2 ppm/°C for SrLa[Ga_0.7(Zn_0.5Ti_0.5)_0.3]O₄, indicating that the present solid solution ceramics are the promising candidates as microwave resonator materials for the telecommunication applications.     

Study on wax precipitation characteristics of wax deposit in pipes

Wax deposit properties are a significant concern in pipeline pigging during waxy crude oil transportation. In the present work, the impacts of flow conditions and oil properties on the wax precipitation characteristics of wax deposits are investigated. A flow loop apparatus was developed to conduct wax deposition experiments using four crude oils collected from different field pipes. The differential scanning calorimetry (DSC) technique was employed to observe the wax precipitation characteristics of crude oil and wax deposit. The results show that the wax content and the wax appearance temperature (WAT) of the deposits increase with shear stress and radial temperature gradient, and decrease with radial wax molecule concentration gradient near the pipe wall. The DSC tests on the wax deposits revealed that the deposit wax content is strongly correlated to the oil wax content. Furthermore, an empirical correlation was developed to predict the wax content and the WAT of the wax deposit. Verification of the empirical correlation using the different oils indicated that the average relative error of the wax content prediction and average absolute error of WAT prediction were 13.2% and 3.6°C, respectively.     

Moderate lameness leads to marked behavioral changes in dairy cows

Lameness is one of the most prevalent diseases affecting the welfare of cows in modern dairy production. Lameness leads to behavioral changes in severely lame cows, which have been investigated in much detail. For early detection of lameness, knowledge of the effects of moderate lameness on cow behavior is crucial. Therefore, the behavior of nonlame and moderately lame cows was compared on 17 Swiss dairy farms. On each farm, 5 to 11 nonlame (locomotion score 1 of 5) and 2 to 7 moderately lame (locomotion score 3 of 5) cows were selected for data collection in two 48-h periods (A, B) separated by an interval of 6 to 10 wk. Based on visual locomotion scoring, 142 nonlame and 66 moderately lame cows were examined in period A and 128 nonlame and 53 moderately lame cows in period B. Between these 2 periods, the cows underwent corrective hoof trimming. Lying behavior, locomotor activity, and neck activity were recorded by accelerometers (MSR145 data logger, MSR Electronics GmbH, Seuzach, Switzerland), and feeding and rumination behaviors by noseband sensors (RumiWatch halter, ITIN + HOCH GmbH, Liestal, Switzerland). Furthermore, visits to the brush and the concentrate feeder, and the milking order position were recorded. In comparison with nonlame cows, moderately lame cows had a longer lying duration, a longer average lying bout duration, and a greater lateral asymmetry in lying duration. Average locomotor activity, locomotor activity during 1 h after feed delivery or push-ups, and average neck activity were lower in moderately lame cows. Eating time and the number of eating chews (jaw movements) were reduced in moderately lame compared with nonlame cows, whereas no effect of moderate lameness was evident for ruminating time, number of ruminating chews and boluses, and average number of ruminating chews per bolus. Moderately lame cows visited the concentrate feeder and the brush less frequently, and they were further back in the milking order compared with nonlame cows. In conclusion, nonlame and moderately lame cows differed in a biologically relevant way in many of the behavioral variables investigated in this study. Therefore, the use of these behavioral changes seems to be promising to develop a tool for early lameness detection.     

Solar light-driven reduction of crystal violet by a composite of g-C3N4, β-Ag2Se, γ-Fe2O3 and graphite

Abstract

In this work, a new g-C₃N₄-based Z-scheme with γ-Fe₂O₃ and β-Ag₂Se both n-type semiconductors, and graphite to favor electron exchange is presented. The composite material was studied by XRD, FTIR, UV-Vis, TEM, XPS, TGA, DSC and TOF-SIMS, and the ability of this photocatalytic system to act as a photo-reductant was assessed using crystal violet (CV⁺) dye. Solar light driven photo-reduction of CV⁺ in the presence of tri-sodium citrate evidenced a synergistic enhancement of the activity of the composite toward reduction, with ～20 times higher conversion rates per unit of surface area than those of g-C₃N₄. Photo-oxidation experiments under Xe lamp irradiation in the presence of H₂O₂ also showed that the AgFeCN composite featured a higher activity (～8×) than g-C₃N₄. This Z-scheme may deserve further study as a photo-reductant to obtain hydrogen or hydrogenated compounds. Moreover, the use of CV⁺ may represent a facile procedure that can aid in the selection of new photocatalysts to be used in hydrogen production.     

Nb和时效时间对热轧中锰TRIP钢中P偏聚的影响

热轧态中锰TRIP钢首先经650 ℃退火2 h,随后在550 ℃进行等温时效热处理,采用场发射扫描电镜(FE-SEM)研究该钢中P的偏聚和时效析出行为的变化情况。结果表明,中锰TRIP钢中P在晶界的偏聚是一种非平衡偏聚现象,临界时间约为50 h,与理论计算结果48 h较为吻合。在局部偏聚区域内,C与P存在共偏聚的关系,即P偏聚量高的地方,C含量也高。而合金元素Nb具有抑制P偏聚的效果,在20~70 h时效时间内,可以相对降低6.57%~19.5%的最大P偏聚量。根据电子背散射衍射(EBSD)菊池线分析,P偏聚量低于2.28at%时,P为固溶状态,高于2.28at.%时,P为析出状态。     

Deformation of a surface layer and coating application using a flexible tool

The microstructure and properties of the functional coatings formed by impact friction processing of product surfaces with a flexible tool are studied. It is established that the processing produces a hard nanostructured surface layer with fragments up to 0.13 µm in size, as it is achieved by severe plastic deformation.