Electrochemical corrosion behavior of 300M ultra high strength steel in chloride containing environment

The electrochemical corrosion behavior of 300M ultra high strength steel in chloride containing environment was investigated by potentiodynamic polarization technique, electrochemical impedance spectroscopy (EIS) and scanning electron microscopy (SEM). The results show that uniform corrosion occurs on 300M steel during the electrochemical measurements because no anodic passivation phenomenon is observed on polarization curves within the measurement range. The tests also show that 300M steel is highly susceptible to chloride containing solution, which is characterized by corrosion current density increasing with the addition of chlorides, and corrosion potential shifting towards positive direction and corrosion resistance decreasing, positively suggesting that chloride ions speed up the corrosion rate of 300M steel. Meanwhile corrosion products on the 300M steel surface formed during the salt spray test are too loose and porous to effectively slow down the corrosion rate. Additionally, a schematic structure of uniform corrosion mechanism can explain that 300M steel has better property of stress corrosion cracking (SCC) resistance than stainless steels.     

X100管线钢在水饱和酸性土壤中的电化学阻抗谱特征

利用电化学阻抗谱(EIS)研究X100管线钢在水饱和酸性土壤中短期的电化学腐蚀行为。结果表明,X100管线钢在鹰潭水饱和土壤中浸泡104 h后已产生点蚀。腐蚀过程的EIS谱具有两个时间常数特征,高频区为代表反应的容抗弧,低频区为代表吸附或点蚀形核期产生的感抗弧。腐蚀初期(1 h～33 h),由于水饱和土壤介质电导率较低,电极反应过程受扩散控制;腐蚀产物在电极表面积累对反应离子扩散有阻碍作用,使阻抗增大;腐蚀产物膜疏松多孔,形成局部活化区域,使阻抗减小;Cl~-对腐蚀产物膜有破坏作用且在膜内局部地区浓缩,诱发点蚀,使阻抗减小,出现感抗特征。     

大气腐蚀研究方法进展

综述了近几十年来国内外大气腐蚀研究方法的发展，重点介绍了大气腐蚀的加速试验方法、电化学研究方法和实时监测技术．湿热试验、盐雾试验、周期喷雾复合腐蚀试验、干湿周浸循环试验和多因子复合加速腐蚀试验是目前使用较多的加速试验，而多因子复合加速试验是模拟大气腐蚀加速试验方法以后发展的方向；发展了研究薄液膜的电化学测试技术，大气腐蚀监测电池ACM和Kelvin探头参比电极技术，极化和阻抗测量方法通常用于干湿交替加速试验中，也用于测试带锈试样在浸渍液中的电化学行为；原位动态实时监测技术的发展促进了从微观水平对材料大气腐蚀机理的研究工作的开展．最后提出了今后大气腐蚀研究方法的发展趋势．     

神经网络分析在高温硫腐蚀中的应用

利用神经网络的分析方法和高温硫腐蚀的数据积累,对炼油过程中的高温硫腐蚀进行分析建模,从系统的观点出发,综合考虑温度、硫或硫化氢浓度、材质和腐蚀速度之间的关系,为更准确的数学建模、预测设备的使用寿命和相应专家系统的研制开拓了新的思路。     

金刚石薄膜膜基界面结合强度测量技术的研究进展

膜基界面结合强度的测量与评价是金刚石薄膜制备与应用关键问题，本文介绍了国内外金刚石薄膜膜基界面结合强度的几种典型的测量方法，着重探讨了膜基界面结合强度的精确定量测量技术的研究现状以及发展趋势，提出了用一种新的内涨鼓泡测量法，对复杂形状基体上金刚石薄膜膜基界面结合强度进行精确定量检测，为金刚薄膜的制备工艺优化及其质量的评估提供可靠的依据和标准。     

X70钢在酸性土壤模拟溶液中的应力腐蚀行为

在不同的阴极保护电位下,采用慢应变速率拉伸实验、动电位极化方法以及SEM研究了X70钢在酸性土壤模拟溶液中的应力腐蚀行为.结果表明: X70钢发生穿晶应力腐蚀裂纹;应力腐蚀开裂(SCC)萌生与外加保护电位有关,完全受阳极过程控制时X70钢的SCC敏感性较低,但会发生点蚀和严重的均匀腐蚀;受混合电极过程控制和全受阴极过程控制时均能发生SCC;受混合电极过程控制时,SCC二次裂纹与点蚀伴生,裂纹形核密度大;而完全受阴极过程控制时,SCC裂纹附近未见点蚀坑,裂纹形核密度低;混合电极过程控制时比完全阴极电极过程控制下更容易发生SCC裂纹.     

X80管线钢在NaHCO_3溶液中的阳极电化学行为

采用动电位极化曲线、动电位电化学阻抗谱(DEIS)和SEM研究了X80管线钢在NaHCO_3溶液中的阳极电化学行为,结果表明:随着HCO_3~-浓度增加,X80管线钢腐蚀速率呈现先增加、后减小的趋势,X80管线钢钝化的临界HCO_3~-浓度为0.009 mol/L.随着HCO_3~-浓度增加,极化曲线阳极电流峰发生变化,当HCO_3~-浓度低于0.009 mol/L时,无阳极电流峰;当浓度在0.009—0.05 mol/L时,有一个阳极电流峰;当浓度增加到0.1 mol/L时,出现两个明显的阳极电流峰,且第1峰与第2峰的峰值电流比随浓度的增大而逐渐增大,DEIS结果与动电位极化曲线完全对应,二者相结合可以很好地研究在不同电位下NaHCO_3溶液中X80管线钢的腐蚀行为,同时对其腐蚀产物和腐蚀机理进行了分析。     

大块涂层缺陷对碳钢腐蚀特性及阴极保护效果的影响

采用了环氧煤沥青作为涂层材料，研究了大块涂层缺陷对碳钢腐蚀特性及阴极保护效果的影响，测定了具有面积比例为4．91％大块涂层缺陷的Q235钢于3．5％NaCl水溶液中的交流阻抗谱．结果表明，随着浸泡时间的延长，在自然腐蚀电位下，存在剥离涂层缺陷时碳钢的腐蚀程度高于破损涂层缺陷时碳钢的腐蚀程度；在阴极极化条件下，具有剥离涂层缺陷的碳钢阴极保护效果随时间延长逐渐降低直至最后消失，而具有破损涂层缺陷时阴极保护效果随时间延长优于剥离涂层缺陷；电解质溶液向涂层内部的渗透以及涂层缺陷与钢基体间的缝隙腐蚀是导致具有大块涂层缺陷碳钢腐蚀的主要原因．     

Ageing behavior of acrylic polyurethane varnish coating in artificial weathering environments

Polyurethane-based coatings reinforced by ZnO nanoparticles (about 27 nm) were prepared via solution blending. The ZnO/PU films and coats were fabricated by a simple method of solution casting and evaporation. The mechanical properties of the films were investigated by a universal material test, and the abrasion resistance of the prepared coats was evaluated by a pencil-abrasion-resistance tester. It was found that significant improvement of the PU films in Young’s modulus and tensile strength was achieved by incorporating ZnO nanoparticles up to 2.0 wt%, and that the abrasion resistance of the PU coats was greatly enhanced due to the addition of ZnO nanoparticles. Moreover, the antibacterial property test was carried out via the agar dilution method and the result indicated that PU films doped with ZnO nanoparticles showed excellent antibacterial activity, especially for Escherichia coli.     

碳纤维布约束对锈蚀钢筋与混凝土间粘结性能的影响

通过外加电流加速锈蚀法获取锈蚀钢筋混凝土试件,采用横向粘贴碳纤维布的方法进行加固,设计并制作了未加固锈蚀试件、先锈蚀后加固和先加固后锈蚀三组22个试件。考虑保护层厚度、加固前或加固后的钢筋锈蚀率等因素,通过拉拔试验研究了碳纤维布约束对锈蚀钢筋与混凝土间粘结性能的影响。分析结果表明,碳纤维布的约束作用能显著提高锈蚀后钢筋与混凝土间的粘结性能,试件破坏模式由混凝土劈裂破坏向钢筋拔出破坏转变。未加固锈蚀试件极限粘结强度随着锈蚀的发展而降低;锈蚀试件采用碳纤维布加固后,由于保护层的劈裂受到约束,极限粘结强度显著提高;由于碳纤维布对锈胀力和保护层劈裂的双重约束作用,先加固后锈蚀试件的极限粘结强度随着锈蚀的发展而增大,且比同等锈蚀率的先锈蚀后加固试件更为显著。根据试验结果分别建立了不同约束条件下锈蚀钢筋与混凝土间极限粘结强度的计算模型。