Microstructure and damage evolution of SiCf/PyC/SiC and SiCf/BN/SiC mini-composites: A synchrotron X-ray computed microtomography study

SiC_f/PyC/SiC and SiC_f/BN/SiC mini-composites comprising single tow SiC fibre-reinforced SiC with chemical vapor deposited PyC or BN interface layers are fabricated. The microstructure evolutions of the mini-composite samples as the oxidation temperature increases (oxidation at 1000, 1200, 1400, and 1600?°C in air for 2?h) are observed by scanning electron microscopy, energy dispersive spectrometry, and X-ray diffraction characterization methods. The damage evolution for each component of the as-fabricated SiC_f/SiC composites (SiC fibre, PyC/BN interface, SiC matrix, and mesophase) is mapped as a three-dimensional (3D) image and quantified with X-ray computed tomography. The mechanical performance of the composites is investigated via tensile tests.The results reveal that tensile failure occurs after the delamination and fibre pull-out in the SiC_f/PyC/SiC composites due to the volatilization of the PyC interface at high temperatures in the air environment. Meanwhile, the gaps between the fibres and matrix lead to rapid oxidation and crack propagation from the SiC matrix to SiC fibre, resulting in the failure of the SiC_f/PyC/SiC composites as the oxidation temperature increases to 1600?°C. On the other hand, the oxidation products of B₂O₃ molten compounds (reacted from the BN interface) fill up the fracture, cracks, and voids in the SiC matrix, providing excellent strength retention at elevated oxidation temperatures. Moreover, under the protection of B₂O₃, the SiC_f/BN/SiC mini-composites show a nearly intact microstructure of the SiC fibre, a low void growth rate from the matrix to fibre, and inhibition of new void formation and the SiO₂ grain growth from room to high temperatures. This work provides guidance for predicting the service life of SiC_f/PyC/SiC and SiC_f/BN/SiC composite materials, and is fundamental for establishing multiscale damage models on a local scale.     

Preparation of biaxially textured Ce1-x(Y0.2Zr0.8)xOδ buffer layers on RABiTS NiW tapes by chemical solution deposition

Highly (100)-oriented Ce_1-x(Y_0.2Zr_0.8)_xO_δ (CYZO) films were prepared on biaxially textured NiW substrates by a chemical solution deposition approach using metal inorganic salts as starting materials. It has been found that both the preferential orientation and surface roughness of CYZO films decrease gradually with increasing of the doping percentage of Y³⁺ and Zr⁴⁺ ions. The epitaxial growth relationship of (220)_CYZO//(200)_NiW and [00?l]_CYZO//[001]_NiW was demonstrated by XRD texture measurement as well as atomic resolution STEM observation. XRD, Raman and XPS spectra results indicate that Y³⁺ and Zr⁴⁺ ions were indeed introduced into CeO₂ lattice to substitute Ce⁴⁺ ions and form cubic fluorite CYZO solid solution. Moreover, CeO₂ buffer layer can be endowed a strong enough capability to prevent element diffusion through co-doping of yttrium and zirconium, provided that an optimal doping ratio of them is adopted. This will provide a new approach to fabricating strong-barrier single buffer layer for coated conductor.     

Adaptive Finite-time Tracking Control for Class of Uncertain Nonlinearly Parameterized Systems with Input Delay

International Journal of Control, Automation and Systems - In this paper, the tracking problem for a class of uncertain nonlinearly parameterized systems with input delay based the adaptive...     

Bearing Failure Optimization of Composite Double-Lap Bolted Joints Based on a Three-Step Strategy Marked By Feasible Region Reduction and Model Decoupling

To minimize the mass and increase the bearing failure load of composite doublelap bolted joints, a three-step optimization strategy including feasible region reduction, optimization model decoupling and optimization was presented. In feasible region reduction, the dimensions of the feasible design region were reduced by selecting dominant design variables from numerous multilevel parameters by sensitivity analyses, and the feasible regions of variables were reduced by influence mechanism analyses. In model decoupling, the optimization model with a large number of variables was divided into various sub-models with fewer variables by variance analysis. In the third step, the optimization sub-models were solved one by one using a genetic algorithm, and the modified characteristic curve method was adopted as the failure prediction method. Based on the proposed optimization method, optimization of a double-lap single-bolt joint was performed using the ANSYS^® code. The results show that the bearing failure load increased by 13.5% and that the mass decreased by 8.7% compared with those of the initial design of the joint, which validated the effectiveness of the three-step optimization strategy.     

Synthesis of Cellulose-Based Macromolecular Coupling Agent and its Utilization in Poly (butylene succinate)/Wood Flour Composites

A long fatty side chain was introduced into the macromolecule of hydroxyethyl cellulose (HEC) via esterification reaction. The hydrophobicity of hydroxyethyl cellulose lauric acid ester (HECLAE) was enhanced in comparison with HEC. The obtained HECLAE was used as macromolecular coupling agent in poly (butylene succinate)/wood flour composites and exhibited a positive influence on improving the mechanical performance of composites. Besides, HECLAE plays a role as a hydrophobic agent in composites. A significant increase in storage modulus (E’) was observed upon the incorporation of treated wood flour. SEM images showed that the dispersion of treated wood flour in PBS matrix was improved.