Preparation and electrochromism of pyrochlore-type tungsten oxide film

Pyrochlore-type WO_3 powder was synthesized via hydrothermal method using aqueous sodium tungstate solution and oxalic acid as raw materials. The as-prepared powder was made into a soliquoid,from which films were made by dip coating process with indium-tin oxide(ITO).The obtained films were characterized by thermogravimetric and differential thermal analysis(TG-DTA), X-ray diffraction(XRD),scanning electron microscopy(SEM),transmission electron microscopy(TEM), cyclic voltammetry(CV), chronoamperometry(CA) and ultravioletvisible(UV-Vis) absorption. Results show that the crystal of the pyrochlore-type WO_3 powder is perfect. When the calcination temperature rises from room temperature to500 ℃,the pyrochlore-type structure first becomes deformed, then it is destroyed and turns into amorphous phase,finally it will completely convert to WO_3 with a monoclinic structure. Electrochemical and optical tests demonstrate that the film calcined at 300 ℃ exhibits the best electrochromic performance and has a coloration efficiency of up to 68.5 cm~2 C~(-1) at 884 nm.     

Design and optimization of ceramic membrane structure: From the perspective of flux matching between support and membrane

The support flux was first investigated as a separate influencing factor for its effect on performances of ceramic filtration membranes. Three pre-membranes were prepared by tape-casting and then transfer-coated to supports to form dual-layer ceramic membranes after sintering. Experiments demonstrated that membrane layers with almost the same properties were obtained despite the huge difference in support flux. When the support flux increases from 3.120 to 97.53 m³m^?2h^?1, the flux of these three membrane series have increased by 75%, 186% and 228%, respectively. Experimental rules can provide structural design and evaluation from the perspective of permeability. The limit membrane flux of a certain system was derived according to the resistance distribution law of internal membrane structure and the Darcy's theorem. On this basis, a method for designing support flux was proposed. Furthermore, we present a criterion to quickly and easily evaluate the match between the support and the top layer, which is the ratio of membrane resistance to total resistance. Finally, the filtration resistance of penetration caused by suction of membrane particles into the support was measured for the first time, taking the advantage of the transfer-coating method that inherently free of penetration. Our works are expected to deepen the understanding of the ceramic membrane structure and provided guidance for its rational design and optimization.     

埋地管道泄漏内封堵装置设计与研究

针对流体输送埋地管道泄漏问题,设计了一种利用管道机器人携带封堵气囊进行快速应急封堵修复的埋地管道泄漏内封堵装置。采用矩阵变换方法建立了牵引系统驱动轮过弯方程,利用MATLAB软件对过弯方程进行了验证,同时利用ADAMS软件仿真分析过弯路径与驱动轮转角对牵引系统行走速度的影响。研究结果表明:由两个串联封堵器组成的应急封堵系统可满足复杂工况下的管道泄漏封堵要求;牵引系统驱动轮在弯管内部行走时,单轮速度呈周期性变化,但三个驱动轮整体周期运动特性一致;驱动轮转角在25°~40°时,牵引系统行走速度与驱动轮转角成正比,且转角为30°时驱动效果最好。该内封堵装置的结构设计可为管道泄漏应急封堵领域装备的研发提供重要参考。     

Structural,morphological, dielectric and magnetic properties of Zn-Zr co-doping yttrium iron garnet

In this study, yttrium iron garnet co-doped with Zn and Zr atoms with a chemical formula Y₃Zn_xZr_xFe_(5−2x)O₁₂ (x = 0.0-0.3) has been successfully prepared by the solid-state reaction method. The effects of doping concentration on the microstructure, crystal structure, magnetic properties, and dielectric properties of Y₃Zn_xZr_xFe_(5−2x)O₁₂ were investigated. The microstructure analysis indicates that co-doping of YIG with Zn and Zr can effectively reduce the grain size of the ceramic. The crystal structure results reveal that the doping concentration of Zn–Zr has substantial influence on the lattice parameters of YIG, such as, increases the lattice constant, crystal cell size, and interplanar spacing. However, the second phase of ZrO₂ appears once x ≥ 0.15. Additionally, the dielectric properties of YIG ferrite can be regulated using this Zn–Zr co-doping method. Zn–Zr co-doping can improve the dielectric stability and reduce the dielectric loss at high temperature. The magnetization measurement shows that the saturation magnetization is stabilized at x < 0.15, and the magnetic loss is decreased with the increase in the doping concentration. Overall, the findings show that the ceramic with x = 0.1 exhibits better properties included high saturation magnetization (24.607 emu/g), low magnetic loss (0.0025 @ 1 MHz), and relatively low dielectric loss (496 @ 400°C).     

Operating Range Scheduled Robust Dahlin Algorithm to Typical Industrial Process with Input Constraint

International Journal of Control, Automation and Systems - There is a class of typical nonlinear industrial process, which can be characterized by a first-order inertia plus pure delay model in an...