Dominant stress region for crack initiation at interface edge of microdot on a substrate

In order to examine the mechanics of crack initiation at the free interface edge of a microcomponent on a substrate, delamination tests are carried out for two specimen shapes of Cr microdots on a SiO₂ substrate. The microdots of the first specimen are shaped like the frustum of a round cone. The Cr microdots are successfully delaminated from the SiO₂ substrate in a brittle manner and the critical load is measured by atomic force microscopy (AFM) with a lateral loading apparatus. Stress analysis reveals that a singular stress field exists near the interface edge and the strength for the crack initiation is governed by the intensified normal stress field. The critical stress intensity parameter is evaluated as K_σC ≈ 0.24 MPa m^0.39. Similar delamination tests are conducted for microdots shaped like the frustum of an oval cone. The stress distributions at the crack initiation of this specimen shape show a higher normal stress than the first specimen shape in the region near the interface edge of about x < 40 nm, while it is lower in the region of about x > 50 nm (x: distance from the edge). This suggests a limitation of conventional fracture mechanics: namely, the crack initiation in these specimens is not uniquely governed by the intensity of the singular field. It is found that the delamination crack is initiated when the averaged stress σ_ya in the region of 90-130 nm reaches 190-270 MPa, regardless of the specimen shape. This indicates that the dominant stress region of crack initiation is roughly estimated as 90-130 nm and the criterion is given in terms of the averaged stress in the region.     

一种用于推挽式电压型逆变器的低损耗无源吸收电路

提出并实现了一种推挽式PWM电压型逆变器用无源吸收电路;设有独立的放电回路让缓冲电容器上的能量部分地回馈到直流电源中,高频放电能量不会叠加在输出电压上;缓冲电容器的电压被钳位,使得推挽电路特有的倍压不会在吸收电路上造成额外的损耗。给出吸收电路参数的设计准则和计算实例,在200VDC和30kW级的中压中功率逆变装置中发挥了推挽拓扑的优点。理论分析和实验验证了所提方法的有效性。     

金属注射成形冷作工具钢的超声疲劳性能

用超声疲劳试验研究了金属注射成形(MIM)冷作工具钢和锻轧钢(JIS SKD11)的高周疲劳性能。锻轧钢试样于423K回火1h。另一方面，为了评估回火温度对疲劳性能的影响，将MIM钢试样于不同温度下进行了回火。在N=103～108疲劳寿命范围内进行了超声疲劳试验。MIM钢试样的疲劳强度和锻轧钢试样相同。MIM钢试样的疲劳强度随着回火温度升高而减低。显微组织的观察结果表明，MIM钢试样的碳化物的直径与形状比锻轧钢试样的均一。     

How international is Computers and Composition?

In this article, I examine to what extent Computers and Composition: An International Journal for Teachers of Writing is international. My analysis of several aspects of the journal indicates limited international scope. I also discuss two issues important when considering the potential international scope of computers and writing research and practices: the differing uses of computers for writing by different language users and the differing concepts of identity and self in different cultures in relation to writing. I conclude with concrete suggestions for broadening our perspectives on computers and writing and making this journal truly international.     

Shape memory properties of polypeptide hydrogels having hydrophobic alkyl side chains

Polypeptide hydrogels were prepared by cross-linking of hydrophobically-modified poly[N⁵-(2-hydroxyethyl) l-glutamine] having alkyl side chains –C_nH_2n+1. Chain length of the alkyl group was n = 8, 16, and 18, and their mole fractions in the polypeptide were varied in the range of 0.05–0.16. Shape memory ability of the prepared polypeptide hydrogels was investigated. After deformation at 60 °C, the hydrogel was cooled in order to fix the temporary deformed shape. It was found that crystallization of the alkyl side chains did not occur, and the fixation ability of the hydrogel at 0 °C was low. In the subsequent heating process, the deformed temporary shape spontaneously recovered to the original shape gradually with increasing temperature, in other words, the shape recovery ratio varied with depending on the recovery temperature. From these observations, it was proposed that the shape fixation of the polypeptide hydrogel was achieved by strong segregation of the hydrophobic alkyl chains at low temperature, and the shape recovery of the deformed hydrogel was accompanied by the gradual decrease of the segregation strength with the temperature increase.     

Critical assessment 29: TRIP-aided bainitic ferrite steels

Transformation-induced plasticity (TRIP)-aided bainitic ferrite steels developed for automotive applications have attractive mechanical properties such as ductility, formability, toughness, fatigue strength and delayed fracture strength. These mechanical properties are principally associated with a ductile lath-structure matrix and the strain-induced transformation of the metastable-retained austenite films of 3–20 vol.%. In this paper, data on the microstructural and mechanical properties of the low-carbon TRIP-aided bainitic ferrite steels are critically assessed, as well as their deformation mechanism.