Synthesis of antimony tris(mercaptoethyl carboxylates) as thermal stabilizer for polyvinyl chloride

A novel type of thermal stabilizers-antimony tris(mercaptoethyl carboxylates) (Sb(SCH2CH2OOCR) 3), was synthesized from carboxylic acid, antimony trioxide and 2-mercaptoethanol in two steps. The experimental results show that the molar ratio of carboxylic acid to antimony tris(2-hydroxyethyl mercaptide) is 1.2, when adding 0.6% tetra-n-butyl titanate as catalyst and xylene as isotropic solvent, heating and refluxing for about 2～4h. The thermal stability was measured by heat-aging oven test. The thermal stability time is about 8～40min(at 200℃) when adding 2% tetra-n-butyl titanate in polyvinyl chloride(PVC). Among these stabilizers, antimony tris(mercaptoethyl stearate) has best thermal stability. Its thermal stability is better than that of Ca-Zn complex and basic lead stabilizers, and equal to that of organotin. In addition, the stabilization mechanism of this kind of stabilizers for PVC was discussed briefly.     

InBO3:Eu3+荧光粉的制备及光谱特性

合成了InBO3:Eu3 红色荧光粉 ,测定了其发光光谱 ,讨论了其发光亮度与稀土离子Eu3 浓度的关系     

Synthesis of mono(1-chloride-2-hydroxy propyl)phosphate and antimony mono(1-chloride-2-hydroxy propyl)phosphate

1　ＩＮＴＲＯＤＵＣＴＩＯＮＭａｎｙａｌｔｅｒｎａｔｉｖｅｍａｔｅｒｉａｌｓｃａｎｂｅｕｓｅｄａｓｆｌａｍｅｒｅｔａｒｄａｎｔｓ.Ｔｈｅｍａｉｎｆｌａｍｅｒｅｔａｒｄａｎｔｓｃｕｒｒｅｎｔｌｙｕｓｅｄｉｎｐｌａｓｔｉｃｓｆａｌｌｉｎｔｏｓｅｖｅｒａｌｃｌａｓｓｅｓ:1 )ａｌｕｍｉｎａｔｒｉｈｙ ｄｒａｔｅ;2 )ｈａｌｏｇｅｎａｔｅｄｃｏｍｐｏｕｎｄｓ ,ｕｓｕａｌｌｙｕｓｅｄｉｎｃｏｍｂｕｓｔｉｏｎｗｉｔｈＳｂ2 Ｏ3;3)ｂｏｒａｘａｎｄｂｏｒｉｃａｃｉｄ ;4 )ｔｈｅ ｐｈｏｓｐｈｏｒｏｕｓ,ｐｈｏｓｐｈｏｒｏ…     

铝土矿的盐酸浸取研究

利用湘西铝土矿进行盐酸浸取，研究了焙烧及浸取的最佳条件，制出了合格的碱式氯化铝，此外用热重法考察了铝土矿的分解情况。     

微胶囊红磷阻燃剂在低密度聚乙烯材料中的应用研究

研究了微胶囊红磷不同包覆、用量、粒径及与其它阻燃剂的协效作用等因素对低密度聚乙烯(LDPE)材料的阻燃性、力学性能及抑烟性能的影响。蜜胺树脂囊材包覆与蜜胺树脂／硼酸锌双层囊材包覆微胶囊红磷在聚乙烯(PE)中的阻燃性最好；8phr的微胶囊红磷添加量即可使材料的阻燃性能达UL 94V-0级，极限氧指数(LOI)从17．4％上升到22．5％；在添加量范围内对材料的力学性能影响很小；二元体系中，微胶囊红磷／氢氧化铝，微胶囊红磷／氢氧化镁与微胶囊红磷／硼酸锌复配具有良好的阻燃协效作用，协效指数分别为1．6、1．4和2．3，微胶囊红磷／硼酸锌二元复合体系有良好的抑烟协效作用，三元体系中，微胶囊红磷／硼酸锌／十溴联苯醚、微胶囊红磷／氢氧化铝／氢氧化镁和微胶囊红磷／硼酸锌／三聚氰胺体系有很好的阻燃协效作用，协效指数分别为2．6、2．1与2．0。     

原位聚合法制备颜料耐晒黄-G微胶囊的研究

研究了三聚氰胺树脂微胶囊化耐晒黄-G的特点和工艺步骤，以提高其热稳定性。讨论了乳化分散剂、三聚氰胺与甲醛摩尔比、三聚氰胺囊材用量和反应pH值对产品性能的影响，确定了最佳工艺条件。采用差热分析(DTA)和扫描电镜表征了该颜料产品。     

微胶囊红磷阻燃剂在环氧树脂基电子电气封装材料中的应用研究

研究了微胶囊红磷对环氧树脂基电子电气封装材料的阻燃性能、力学性能及抑烟性能的影响。添加微胶囊红磷10份量即可使材料的阻燃性能达UL94V 0级,氧指数(LOI)从19 5上升到28 2;添加量在一定范围内对材料的力学性能影响很小,随添加量从0增加至14份,材料的拉伸强度略有下降,从48 84MPa下降至46 92MPa;冲击强度有所上升,从9 29kJ·m-2提高到10 28kJ·m-2;弯曲强度先略有上升然后有所降低,从130 2MPa变化至136 6MPa;微胶囊红磷与硼酸锌的复配体系具有很好抑烟性能。     

Using sensitive surface plasmon resonance to detect binding of peptide molecules and immobilized vancomycin

To perform the mechanism study of special association for vancomycin and D-Ala-D-Ala-containing peptides on the interface of solution and self-assemble monolayer,the binding between vancomycin and pentapeptide(Lys-Lys-Gly-D-Ala-D-Ala) was investigated by flow injection surface plasmon resonance(FI-SPR) and flow injection quartz crystal microbalance(FI-QCM).To facilitate the formation of a compact vancomycin adsorbates layer with a uniform surface orientation,vancomycin molecules were attached onto a preform...     

铕-噻吩甲酰三氟丙酮-活性配体三元配合物的合成及发光性能研究

以噻吩甲酰三氟丙酮为第一配体,顺丁烯二酸酐、十一烯酸、油酸、丙烯腈为活性第二配体,合成了四种新的反应型三元铕配合物。通过元素分析,EDTA配位滴定分析,红外、紫外、荧光光谱分析,对标题配合物的组成、结构进行了表征,并研究了它们的发光性能,结果表明,四种新的反应型三元配合物具有良好的发光性能,且配合物中引入了能与其它单体共聚的活性第二配体,为合成具有优异发光性能的键合型稀土高分子功能材料提供了一条新的途径。     

二氯二茂钛二甲硫氨酸与DNA相互作用的电化学及紫外-可见光谱研究

用循环伏安法考察了二茂钛二甲硫氨酸配合物(TMC)与DNA在pH=3.0的KCl水溶液中相互作用的电化学行为。TMC在玻碳电极上分别于-412 mV和-528 mV(υs.SCE)有一个氧化峰和相应的还原峰。加入DNA后,TMC的式量电位负移5 mV,峰电流增加,电化学参数(α和ks)改变。结果表明:在该条件下,TMC与DNA之间通过静电作用,形成了一种具有电活性的复合物,且TMC与DNA之间的结合位点数n和结合常数K分别为4.36和2.74×1016。结合紫外-可见光谱法测定结果,加入DNA后TMC的紫外-可见光谱在393 nm处呈现增色效应,进一步确证了TMC与DNA之间主要以静电作用为主。