Al-3Ti-1B-0.2C中间合金对A356合金的晶粒细化行为

对比了Al-5Ti-0.4C、Al-5Ti-1B及Al-3Ti-1B-0.2C中间合金对A356合金的晶粒细化行为.发现在730℃时,加入0.2%的Al-3Ti-1B-0.2C中间合金,可以使A356合金的晶粒尺寸由1000 μm以上细化至175 μm左右,保温60 min内,细化效果稳定,其细化能力明显优于Al-5Ti-1B和Al-5Ti-0.4C中间合金,且该中间合金的加入不影响Sr对共晶Si的变质效果.与Al-5Ti-1B中间合金细化后的A356合金相比,经Al-3Ti-1B-0.2C中间合金细化后的A356合金室温抗拉强度和伸长率分别提高了5.18%和15.98%.     

高强韧Al-Si-Mg合金材料设计与制备

为获得高强韧Al-Si-Mg合金,以亚共晶Al-Si-Mg合金为研究对象,探究了ASN晶种合金对其组织及室温力学性能的影响.试验结果表明:未添加ASN晶种合金时,Al-Si-Mg合金中α-Al晶粒粗大,枝晶发达,共晶组织分布不均匀;而向Al-Si-Mg合金中添加1％的ASN晶种合金后,α-Al晶粒得到一定细化,枝晶生长...     

快速凝固铝—硅合金微粒中共晶硅生长形态的研究

用氮气雾化法制取了Ａｌ－１２．５４％Ｓｉ合金微粒，再加热至７００℃进行重熔处理。用扫描和透射电镜研究了快速凝固对Ａｌ－Ｓｉ合金中共晶硅生长形态的影响。结果表明，用氮气雾化法和重熔处理的试样中，共晶硅呈球状和弯扭的纤维状。     

富磷中间合金对过共晶Al-24%Si合金的高效变质处理

研究了富磷中间合金(含22wt%P)对过共晶Al-24%Si合金的变质效果。结果表明:采用Si-P-Cu富磷中间合金对Al-24%Si合金进行变质时,其加入量为0.1%时即能达到理想的变质效果,使其初晶硅颗粒明显增多,平均颗粒尺寸下降到35!m左右;最佳变质温度为825℃左右;变质效果长效稳定,有着广阔的应用前景。     

铝硅合金原锭中气孔的遗传现象及控制

通过测定铝硅合金原锭及其重熔以后试样的气孔度和气孔率，发现气孔具有遗传性。对气孔遗传的机理进行了探索，并提出了控制措施。     

United modification of Al-24Si alloy by Al-P and Al-Ti-C master alloys

The modification effect of a new type of Al-P master alloy on Al-24Si alloys was investigated.It is found that excellent modification effect can be obtained by the addition of this new type of Al-P master alloy into Al-24Si melt and the average primary Si grain size is decreased below 47μm from original 225μm.It is also found that the TiC particles in the melt coming from A18Ti2C can improve the modification ffect of the Al-P master alloy.When the content of TiC particles in the Al-24Si melt is 0.03%.the improvement reaches the maximum and keeps steady with increasing content of TiC particles.Modification effect occurs at 50 min after addition of the Al-P master alloy and TiC particles,and keeps stable with prolonging holding time.     

Al-Ba中间合金及其对共晶Al-Si合金的变质处理

制备出一种新型的Al-Ba中间合金变质剂，并探讨了它对Al-Si合金的变质处理效果。试验结果表明，Al-Ba中间合金对共晶Si的变质效果与Al-Si合金相当，可以使共晶Si由片状变为珊瑚状，显著改善Al-Si合金的显微组织。另外，用Al-Ba中间合金与A1-P中间合金同时对Al-Si合金进行变质处理时，还可达到双重变质效果。同时，用Al-Ba中间合金时，变质持效时间比钠盐变质剂更长久，显示出较好的应用前景。     

铝熔体中的钠在电场下的运动行为

本文研究了铝熔体中钠在电场作用下的运动状态,考察了电流密度、处理时间对铝含钠量的影响,找出了影响除钠的因素,同时对除钠机理作了探讨。     

微量Mg、Si对A1TiC中间合金细化效果的促进作用

研究了微量的合金元素Mg和Si对A1TiC中间合金细化效果的影响。实验结果表明：微量的Mg和Si均能促进A1TiC中间合金对工业纯铝和6063合金等铝合金的晶粒细化作用；在细化温度相同的条件下，与Si相比，Mg 对A1TiC中间合金细化效果具有更大的促进作用；微量的Mg可以抑制A1TiC中间合金晶粒细化的“温度效应”；铝熔体中同时存在微量的Mg和Si时A1TiC中间合金的细化效果更好。初步探讨了这两种微量元素促进A1TiC中间合金细化效果的机理。