Fabrication and photo-catalytic properties of pure and cation doped TiO2 nanotube arrays

The highly ordered and vertically oriented pure TiO2 nanotube arrays （TONTAs） are synthesized by anodic oxidation of titanium foils in fluoride-based electrolytes under different temperatures and voltages. Then TONTAs are treated at different temperatures. X-ray diffraction （XRD） patterns show that its structure is anatase at 500℃ with the temperature increasing to 700℃, the most of anatase will transform to rutile, the nanotube arrays form granular titanium oxide, while at 900℃, anatase will transform to rutile completely. The experimental results of photocatalytic degradation of methylene blue solution show that the cobalt-manganese co-doped TONTAs have good photocatalytic degradation efficiency.     

原油总碳含量的粒子群优化集成神经网络预测模型

原油评价新技术的研究和应用成为目前世界石油炼制企业致力发展的方向,也是今后发展的必然趋势.本文采用核磁共振(nuclear magnetic resonance, NMR)光谱技术和粒子群优化集成神经网络(particle swarm optimiza tion-ensemble neural network, PSO-ERNN)建立了一种快速评价原油总碳物性指标预测模型.该模型以随机向量函数连接网络(random vector functional link network, RVFL)作为基本模型,采用正则化负相关学习策略集成基本模型,并采用粒子群优化算法优化各基本模型的最优隐含层节点数(L)以及集成规模的最佳集成个数(M),最后利用在线学习方法对模型进行更新.实例验证表明,所提出的模型显著提高了预报精度,避免了随机选择L和M对模型精度的影响,对提高原油评价精度与效率和及时满足加工炼制要求具有应用价值.     

激光熔覆无碳化物贝氏体涂层制备及其摩擦学性能

通过控温激光熔覆及后续等温转变处理,制备出显微组织细小、硬度分布均匀且耐磨性良好的无碳化物贝氏体涂层。采用光学显微镜、XRD、TEM、SEM、显微硬度计、纳米压痕仪和摩擦磨损试验机等分别对不同参数的熔覆试样、对比试样的显微结构及性能进行测试。结果表明:与盐浴淬火试样相比,采用控温激光熔覆技术制备的无碳化物贝氏体涂层显微组织均匀细小,贝氏体晶格常数由2.8692?增加到2.8697?,铁素体微晶尺寸由86.3 nm减小至67.0 nm,无碳化物贝氏体涂层的显微硬度由(384±18)HV0.1提高到(430±13)HV0.1。摩擦因数由1.21降低至1.05,磨痕深度由0.1 mm降低至0.04 mm。较高的表面硬度提高了无碳化物贝氏体涂层表面抵抗塑性变形的能力,减缓了磨痕表层的剥落。