通过在U71Mn、90 0A钢生产中的应用 ,并与硅钙合金脱氧相比 ,得出在同等加入量的情况下 ,采用硅钙钡合金脱氧后 ,转炉终点钢水氧活度降低 ,钢中全氧含量小于 2 0× 10 -4 %,非金属夹杂物形态得到了改善。     

Effect of Rare Earths on Properties of BNbRE Rail Steel

The development and properties of BNbRE rail steel and the effect of RE on rail steel were studied. The results show that the properties of rail steel (δb ≥980 MPa, δ5≥ 8 % ) can be improved by adding RE and niobium and adjusting the content of C, Si and Mn in steel. At the same time, the abrasion resistance, contact fatigue and fatigue property of BNbRE rail steel are excellent. It also shows that RE in rail steel has the functions of purifying steel, modifying inclusion and micro-alloy action effect. The improved steel-making process enhances the quality of molten steel. Although the content of RE is low, excellent properties of BNbRE rail steel are achieved.     

重轨钢连铸技术在包钢的开发应用

介绍了包钢在重轨钢生产工艺方面的变化和目前所能达到的质量水平;重点说明了采用连铸工艺后,钢中气体的控制,钢中全氧的控制,钢中夹杂物的控制和大方坯内部质量的控制所采取的技术措施;分析了电磁搅拌技术对大方坯内部质量的影响.     

稀土氧化物对连铸保护渣理化性能的影响

稀土钢浇铸过程中,稀土氧化物进入到保护渣熔融层中,影响和限制了保护渣冶金性能的正常发挥,针对这一问题,文章系统分析了稀土氧化物对结晶器保护渣不同碱度熔化温度、粘度和结晶温度的影响。结果表明,少量的稀土氧化物对保护渣有助熔作用,随稀土氧化物含量的增加,不同碱度保护渣的熔化温度、粘度和结晶温度变化显著。     

包钢一炼钢洁净钢生产技术开发

通过包钢-炼钢复吹转炉冶炼-LF精炼-VD真空处理-连铸工艺路线下生产重轨钢钢的氢、氧、氮控制水平研究,得出在稳定钢中w[H]、w[O]的基础上,主要是对钢中w[N]的控制,并提出了技术措施,结果重轨钢中w[N]同比降低10×10-6、w[H] w[O] w[N]≤60×10-6达90%以上.     

连铸坯热装轧制钢轨组织与性能试验研究

文章主要介绍了采用钢轨钢连铸坯热送热装工艺生产钢轨组织的变化和所能达到的各项性能指标.试验结果表明,连铸坯在640℃以下装炉时,所生产钢轨的各项性能指标均能够满足相关标准要求,且和常规冷态装炉基本一致.     

连铸中间包覆盖剂研究

对包钢连铸中间包覆盖剂配方的设计思路及设计原则 ,以及配方的物化性能和连铸机的试验情况作了介绍 ,试验结果表明覆盖剂保温性能好 ,渣耗适中 ,并有较强的防止钢液二次氧化及吸收Al2 O3 等非金属夹杂的能力 ,且对内衬及长水口侵蚀也较少     

310乙字钢组织对低温冲击功的影响

通过检验310乙字钢不同部位钢的-40℃V型缺口冲击功,以及对应的金相组织,分析了310乙字钢组织对低温冲击功的影响,结果说明：同一支310乙字钢在不同部位的低温冲击功存在差异,主要因素在于铁素体的晶粒大小、形态及分布的差别。     

高温防氧化钢坯涂料的研制

本文分实验室模拟研究的现场涂料试用研究两大部份。研究了高温下钢坯氧化机理;硅酸盐珐琅涂层在1200℃下防氧化机理;涂层的实验室模拟研究。 现场试用表明:涂层在1200℃下,2～2.5小时可减少钢坯在加热炉内氧化40～60%,全程氧化30%左右。涂层对轧制工艺、表面质量没有不利影响。