Influence of the shape of fiber cross section on fabric surface characteristics

Fiber cross sections for use in textiles and composites are becoming more and more complex. Shape impacts fiber or filaments properties and therefore the yarn and fabric characteristics. This paper presents the influence of the fiber cross section on the fabric surface characteristics. The material used was polyester staple fibers, of four different shapes: round, scalloped oval, cruciform and hexachannel. All fibers had the same cut length with different fineness. Yarns obtained from these fibers had nominally the same yarn count, torsion value and structure. Plain jersey fabrics were knitted from each of the yarns under identical conditions and then relaxed prior to testing. Friction behavior was evaluated and a roughness-friction criterion developed. An indirect measurement of the real area of contact was obtained in order to provide roughness and friction properties. The influence of fiber cross section on yarn bending rigidity and on the state of the knitted fabric surface was characterized.     

On the stabilizing behavior of zirconia: A Combined experimental and theoretical study

Reactive zirconia powder was synthesized by the complexation of zirconium metal from zirconium hydroxide using a solution of 8-hydroxiquinoline. The kinetics of zirconia crystallization was followed by X-ray diffraction, scanning electron microscopy and surface area measured by the nitrogen adsorption/desorption technique. The results indicated that zirconia with a surface area as high as 100 m²/g can be obtained by this method after calcination at 500°C. Zirconia presents three polymorphic phases (monoclinic, tetragonal and cubic), which are reversibly interconversible. The cluster model Zr₄O₈ and Zr₄O₇ ⁺² was used for a theoretical study of the stabilization process. The ab initio RHF method was employed with the Gaussian94 program and the total energies and the energy gap of the different phases were calculated and compared with the experimental energy gap. The theoretical results show good reproducibility of the energy gap for zirconia.     

HRTEM observation of the monoclinic-to-tetragonal m-t) phase transition in nanocrystalline ZrO2

The orientation relations m(100) || t(001), m[001] || t[110]; m(011) || t(100), m[100] || t[001]; m(100) || t(110), m[001] || t[001]; m(013) || t(116), m[001] || t[001] (indices for the primitive tetragonal cell) have been found between the tetragonal (t) and monoclinic (m) domains during the electron irradiation-induced m-t phase transition observed in-situ with HREM within isolated zirconia nanoparticles. Geometric models of the m-t interfaces are proposed.     

Potential for integration of electrophoretic deposition into electronic device manufacture; demonstrations using silver/palladium

A silver palladium (Ag/Pd) alloy powder is used as an example material to illustrate potential applications of electrophoretic deposition (EPD) in electronics manufacturing, in particular the forming of multilayer devices. The dispersion and deposition of the Ag/Pd powder in acetic acid is characterized. It is found that deposition can be explained by the direct action of electrostatic force on individual particles. Depositions of this Ag/Pd powder are then used to demonstrate: forming of a continuous layer on a rigid substrate; forming of continuous layers in laminated and sintered BaTiO₃ multilayers; and incorporation of patterned depositions into a multilayer by either overcasting the patterned deposition with a particulate slip to form a multicomponent tape, or direct lamination of the patterned deposition to a low temperature co-fired ceramic (LTCC) tape. It is shown that electrically conducting layers can be formed at an average thickness of only two times the diameter of the starting powder. Continuous conductor lines thirty times the average diameter of the starting powder were formed.     

Magnetic properties and thermal stability of CoFeNi-based amorphous films

CoNiFe-based amorphous films were magnetron-sputtered to investigate their structural and magnetic properties, including annealing-induced effects and interfacial influence from additional layers of Ta and Cu. The amorphous structure was confirmed by diffraction experiments. The magnetic measurements showed a well-defined uniaxial anisotropy in plane, arising possibly from atom oblique incidence effects competing with the stray field of the magnetron. The anisotropy could be influenced by using a Ta buffer layer, though the interfacial reaction gives rise to a dead layer. A coercive force H _c of 1–2 Oe and a magnetization of 680 emu/cm³ were measured at room temperature; properties which show promise for application in magnetotunneling junction devices. Thermal analyses showed a two-stage crystallization behavior, which started at 400°C and ended at about 600°C. The Curie temperature of the amorphous phase was estimated to be about 440°C.     

Sensors for chemicals based on electrically conductive immiscible HIPS/TPU blends containing carbon black

Carbon Black (CB)-containing immiscible polymer blends based on high-impact polystyrene/thermoplastic polyurethane (HIPS/TPU) were studied as sensing materials for an homologous series of alcohols, including, methanol, ethanol and 1-propanol. The studied immiscible blend was designed to exhibit a double-continuity structure i.e., the CB particles form chain-like network structures within the TPU phase, which forms a continuous phase within the HIPS matrix. Extruded HIPS/TPU/CB filaments produced by a capillary rheometer process at various shear rate levels were used for the sensing experiments. All filaments displayed a selective resistance changes upon exposure to the various alcohols combined with reproducibility and recovery behaviour. An attempt is made to identify the dominant mechanisms controlling the sensing process in a CB-containing immiscible polymer blend characterized by a double-continuity structure. The distinct structure and composition of the HIPS/TPU interphase region were found to have a crucial role in the sensing mechanism, determining the selectivity of the filaments toward the studied alcohols. Additionally, the sensing performance of HIPS/TPU/CB system is compared to recent results for TPU/CB compounds, polypropylene/TPU/CB and HIPS/ethylene vinyl acetate/CB immiscible polymer blends.