Fugitive Diffusion Barrier for Integration of Sol-Gel-Derived Lead Titanate with Oxidized Silicon Substrates

The crystalline phase development and microstructural changes with heating of sol-gel-derived lead titanate (PT) particles and films on silica with and without a fugitive (or removable) diffusion barrier layer were investigated. Amorphous gel-derived PT particles were deposited on SiO₂-coated TEM grids with and without polyimide (PI) or carbon barrier layers between SiO₂ and PT. TEM analysis showed that PI or carbon barriers prevented reaction between the gel-derived PT particles and SiO₂. PT particles crystallize and then the PI or carbon film decomposes. Sol-gel-derived PT films were deposited on oxidized Si substrates (Si/SiO₂) with and without a PI barrier layer. Perovskite PT films were prepared on Si/SiO₂ substrates with a PI barrier; however, some porosity remained in the films. Identically prepared films without the PI barrier formed a mixture of pyrochlore and perovskite. X-ray photoelectron spectroscopy results indicate that the PI film pre- vents the diffusion of Si into the PT film.     

Aorto-left atrial fistula in prosthetic aortic endocarditis

Aortic valve endocarditis commonly leads to the formation of a root abscess, but fistulae are uncommon. The echocardiographic findings in a patient with Streptococcus viridans endocarditis of a prosthetic aortic valve associated with a fistula between the aorta and the left atrium are presented. The diagnosis was made by transthoracic echocardiography, although the transesophageal study gave higher resolution views and allowed a more confident exclusion of mitral valve involvement.     

Bending and torsional fatigue of nylon 66 monofilaments

Using newly developed test equipment, the fatigue behavior of nylon 66 monofilaments was studied under two loading conditions, pure bending or simple torsion. For each mode, results are expressed in terms of the measured decay in stiffness with numbers of cycles over a range of maximum applied strain levels. Fatigue lifetimes are presented in S–N format where the log number of cycles of fatigue for a 40% decay in stiffness (N) is plotted as a function of applied strain (S). The failure mechanism for these fibers in each fatigue mode reflects the morphology of semicrystalline-oriented synthetic fibers. In torsion, many longitudinal cracks form around the perimeter of a fiber as the result of cleavage of the relatively weak interfibrillar bonds in nylon 66. In bending, cracks form within kink band boundaries and grow at an oblique angle to the fiber axis. © 1992 John Wiley & Sons, Inc.     

Studies on the efficacy of hyperbaric rendering procedures in inactivating bovine spongiform encephalopathy (BSE) and scrapie agents

The efficacy of the procedures in use at the two rendering plants in the Netherlands was assessed on a laboratory-scale using procedures that simulated the pressure cooking part of the rendering process. A pool of bovine spongiform encephalopathy (BSE)-infected brainstem from the United Kingdom and a pool of scrapie-infected brainstem from Dutch sheep were used to spike the rendering materials. The mixtures were subjected to various time-temperature combinations of hyperbaric heat treatment related to the conditions used in Dutch rendering plants in the early 1990s, and to the combination of 20 minutes at 133 degrees C required by the EU Directive on rendering of 1996. The efficacy of the procedures in inactivating BSE or scrapie infectivity was measured by titrating the materials before and after heat treatment in inbred mice, by combined intracerebral and intraperitoneal inoculations at limiting dilutions. Two independent series of experiments were carried out. The design of the study allowed for minimum inactivations of up to 2.2 log (2.0 in the second series) to be measured in the diluted infective material and 3.1 log in the undiluted material. After 20 minutes at 133 degrees C there was a reduction of BSE infectivity of about 2.2 log in the first series (with some residual infectivity detected), and in the second series more than 2.0 log (with no residual infectivity detected). With undiluted brain material there was an inactivation of about 3.0 log (with some residual infectivity detected). With the same procedure, scrapie infectivity was reduced by more than 1.7 log in the first series and by more than 2.2 log in the second series. With undiluted brain material there was an inactivation of more than 3.1 log. In each case no residual scrapie infectivity was detected. The BSE agent consistently appeared to be more resistant to heat inactivation procedures than the scrapie agent, particularly at lower temperatures and shorter times.