Processing of Yttria-Alumina Coated Silicon Nitride Slips by Slip Casting

Si₃N₄powders coated with 6 wt% Y₂O₃and 4 wt% Al₂O₃were prepared by coprecipitation. The resulting powders were dispersed in water at different pH values and with addition of various amounts of ammonium polyacrylate (NH₄PA) to produce 32 vol% slips. The influence of the amount of NH₄PA solution added and pH on the rheological properties of 32 vol% coated Si₃N₄slips were studied. In addition, the sintered density of cast samples was determined and related to the degree of slip dispersion. The adsorption of the NH₄PA on the coated particle surface was rather high and the surface became saturated near 0.86 mg/m²at pH 9.2. High NH₄PA concentrations (1.7–3 wt%) were necessary to obtain well dispersed 32 vol% coated Si₃N₄slips at pH 9.2. The best stabilization was obtained with the addition of 2.3 wt% NH₄PA; in this condition, the viscosity reached a minimum value of 35 mPa.s at 100 s^–1. The slip viscosity increased with increasing pH from 9.2 to 10.2. Slips with low viscosities gave a more dense packing of cast samples and consequently higher sintered density values.     

Parametric inference for step-stress models

Applications of the additive accumulation of damages (AAD) or the accelerated failure time (AFT) and the proportional hazards (PH) models in accelerated life testing with step-stresses are discussed. A new model including AAD and PH models is proposed. It is more reasonable than the PH model and wider then the AAD model. Constructing the maximum likelihood function is discussed     

Experience in High-Temperature Thermomechanical Treatment with Helical Reduction in the Production of Axisymmetric Parts

Metal Science and Heat Treatment -     

Use of166mHo for calibration of gamma-ray spectrometers with semiconductor detectors

Translated from Atomnaya Énergiya, Vol. 67, No. 3, pp. 215–216, September, 1989.     

Improving a technology for treating pig iron outside the furnace with magnesium

Institute of Ferrous Metallurgy. Translated from Metallurg, No. 4, p. 24, April, 1989.     

The effects of pressure on the isothermal fluid behavior of bituminous coals

An investigation into the effects of pressure (helium gas) on the isothermal fluid behavior includes: (1) the effect of pressure on the rate of melting and coking as evidenced by the rate constants k(melt) and k(coke); (2) the effect of pressure on the energies of activation of melting and coking; (3) the effects of pressure on the characteristic times; (4) the effects of pressure on the maximum isothermal fluidity. Results from the effects of pressure on k(melt) revealed that it was generally the high total sulfur, low nitrogen, low reactives/mineral matter ratio, medium rank coals which show the greatest increase in k(melt), whereas the highest rank coals show the least decrease in k(coke). The energies of activation of melting and coking were not significantly affected by pressure. The investigation also reveals increases or decreases in the respective times of softening, maximum fluidity, resolidification and total time of fluid behavior under isothermal pressurized conditions. There appears the possibility that these shifts may be rank dependent. Additionally, the lower rank coals show the largest relative increase in their fluidities when subjected to pressure. Empirical relationships were derived in order to quantitatively predict the maximum isothermal fluidity for most (fluid) coals at a given pressure.