Segregation in Single-Crystal Fully Stabilized Yttria-Zirconia

X-ray photoelectron spectroscopy (XPS) has been used to study surface segregation in 9.5 mol% single-crystal Y₂O₃-ZrO₂ which has been subjected to air anneals at temperatures ranging from 900° to 1500°C. The kinetics of segregation reveal an enrichment of Y, Si, Na, and Fe at short times; however, at longer times surface equilibrium is reached. The heats of segregation for Y, Si, Na and Fe, determined from Arrhenius plots, were 9.3 ± 3.0, 59.0 ± 7.0, –23.5 ± 11.5, –18.0 ± 6.0 kJ/mol, respectively. XPS analysis of the equilibrium states at all temperatures revealed a distinct surface layer which, given the positive heats of segregation for Si and Y, is quite stable.     

海洋潮差区混凝土表面微生物16S rDNA分子鉴定

针对目前海洋混凝土工程的腐蚀现状,进行了海洋微生物对潮差区混凝土的作用机理及完善海工混凝土的腐蚀机理探索.通过海工混凝土潮差区部位取样,对暴露于潮差区中部22 y的混凝土试样表面进行FE-SEM、EDAX分析,结果表明:潮差区混凝土表面腐蚀严重,结构疏松,表面覆盖有有机物质和微生物.并将暴露于潮差区中部22 y的混凝土试样和该取样位置挂置7 d的混凝土试样表面的微生物群落分别分离,克隆了其中30株和12株细菌的16S rDNA基因,测定其序列且进行比对,其分别属于15个和7个种属中.优势种属均为假交替单胞菌,但随着暴露时间的增加,总细菌株数和总菌属数分别增大到2.5和2.14倍,且种属的变化也很大.同时,建立了海洋混凝土工程表面细菌鉴定方法,以及分离、鉴定的菌种为后续细菌对混凝土作用的试验提供菌种.     

钢纤维混凝土高温后SHPB试验研究

为了研究钢纤维混凝土(SFRC)常温以及经历400和800℃高温后的动态压缩性能,采用改进的分离式Hopkinson压杆装置,结合应变直测技术对其进行了单轴冲击压缩试验.结果表明:经历400和800℃高温后,未掺钢纤维混凝土的峰值应力分别只有常温时的79.2%和38.9%,弹性模量分别降为常温时的82.8%和56.2%,同时,试件的能量吸收能力大幅度下降;钢纤维混凝土400,800℃对应的峰值应力分别降为常温时的76.8%和39.0%,弹性模量稍有降低,分别为常温的91.8%和82.7%,较基准混凝土有了较大的提高.钢纤维的加入可以增加混凝土的极限应力对应应变,曲线的下降段较为平缓,同时增强了混凝土的能量吸收能力,在20,400和800℃时,分别提高了38.5%,27.5%和25%.     

电化学除氯处理后的混凝土微观结构研究

为了研究电化学除氯对混凝土中离子分布和微观结构的影响规律,采用压汞法、SEM电子显微镜分析等方法对电化学除氯后不同水灰比混凝土试件中钢筋附近和表面层的氯离子和钾钠离子含量、孔隙结构、显微结构进行对比分析.结果显示,电化学除氯后,钢筋附近混凝土与外层混凝土相比,氯离子含量约为1/2,钾离子含量约为5～10倍,钠离子含量约为8～18倍,水化物颗粒间结合不连续、部分水化产物分解.钢筋附近区域混凝土中的氯离子含量明显低于外表层混凝土,钾、钠离子在钢筋阴极附近大量聚集.经过电化学处理后的混凝土试件钢筋附近区域的孔隙率和大孔含量增多,结构疏松;而外表层混凝土结构致密,孔隙细化,水化产物成网络状结合良好.     

新型多单体接枝物增容PP/PVC共混体系的研究

自制了多单体接枝物PP g (St co MMA) ,并利用其增容PP/PVC共混体系。讨论了共混物组成、相容剂用量在不同温度、不同压力下对其流变行为的影响。实验结果表明 ,在所研究的温度和压力范围内 ,加入PP g (St co MMA)增容PP/PVC共混体系后 ,共混物熔体呈典型的假塑性流体特性 ,粘流活化能增加 ,非牛顿性有增大的趋势。共混体系的力学性能提高 ,SEM照片证明了多单体接枝物对PP/PVC的增容作用     

Visible light localization algorithm based on multi-measurements constraints

In the indoor visible light transmission environment with complex noise, traditional received signal strength indication(RSSI)localization algorithm and imaging localization algorithm are unable to accurately determine the reason of the inaccurate localization model and inadequate constraints of position coordinates. In order to solve the problems, a visible light localization algorithm based on multi-measurements constraints is presented in the paper. The algorithm first constructs a joint localization state space model based on RSSI localization and the imaging localization algorithm. Then, states, measurements and their equations are constructed based on the space model. Finally, the equations are resolved using the unscented Kalman filter(UKF). Compared with RSSI localization and imaging localization, simulation results show that the RMSE of the proposed algorithm could be closer to the Cramer Rao bound. Besides, the localization probability of the proposed algorithm is higher than that of RSSI localization and imaging localization algorithm.     

Runout effects in milling: Surface finish, surface location error, and stability

This paper investigates the effect of milling cutter teeth runout on surface topography, surface location error, and stability in end milling. Runout remains an important issue in machining because commercially-available cutter bodies often exhibit significant variation in the teeth/insert radial locations; therefore, the chip load on the individual cutting teeth varies periodically. This varying chip load influences the machining process and can lead to premature failure of the cutting edges. The effect of runout on cutting force and surface finish for proportional and non-proportional tooth spacing is isolated here by completing experiments on a precision milling machine with 0.1 μm positioning repeatability and 0.02 μm spindle error motion. Experimental tests are completed with different amounts of radial runout and the results are compared with a comprehensive time-domain simulation. After verification, the simulation is used to explore the relationships between runout, surface finish, stability, and surface location error. A new instability that occurs when harmonics of the runout frequency coincide with the dominant system natural frequency is identified.     

硼离子注入对多晶Ni力学性能及微观结构的影响

用能量为50keV,剂量为3×10~(17)ions/cm_2的B~+注入多晶Ni,通过力学性能实验研究了多晶Ni注入前后表面硬度和疲劳性能的变化,以及多晶Ni表面层注入和疲劳前后化学成分、滑移特征、裂纹萌生、断裂方式和微观结构的变化。结果表明,B~+注入多晶Ni后,表面区域形成一个不同组织结构的由Ni-B非晶、Ni_3B和Ni_4B_3第二相以及辐照损伤组成的多层次的注入层,提高了多晶Ni的表面硬度,并使其疲劳极限提高16％。探讨了B~+注入影响多晶Ni疲劳极限的几种可能机制。     

Effect of solid fraction on steel-mushy Cu-graphite pressing bonding

The pressing bonding of steel plate to QTi3.5-3.5graphite slurry was studied. The bonding conditions were 620℃ for preheating temperature of steel plate, 530℃ for preheating temperature of dies, 50 MPa for pressure and 2 min for pressing time. The relationship between the solid fraction of QTi3.5-3.5graphite slurry and the interracial mechanical property of bonding plate was obtained. The results show that when the solid fraction of QTi3.5-3.5graphite slurry is smaller than 45.8%, the interracial shear strength of bonding plate increases with the increasing of solid fraction. When the solid fraction is larger than 45.8%, the interracial shear strength decreases with the increasing of solid fraction. When the solid fraction is 45.8%, the largest interracial shear strength of bonding plate 127 MPa can be got, and the interface is made up of Fe-Cu solid solution.     

38CrSi钢表面纳米结构层力学性能的研究

采用超音速微粒轰击技术在38CrSi合金钢表面制备了厚度约为25μm纳米晶层.利用X射线衍射、扫描电镜和透射电镜对表面结构进行分析.纳米结构层的最表面层的晶粒尺寸约为16nm,晶粒尺寸随着距表面距离的增加而增大.利用纳米压痕仪对表面纳米结构层的力学性能进行研究,结果表明,当表面晶粒尺寸降低到纳米量级时力学性能明显改善,最表面纳米结构层的硬度是基体的2倍左右,并服从Hall-Petch关系;表面纳米结构层的弹性恢复系数明显提高;利用该方法制备的纳米晶对弹性模量的影响较小;对表面纳米化样品进行低温退火处理可使纳米结构层的性能更加稳定.分析表明表面纳米结构层力学性能的改善主要是表面晶粒细化的结果.