TEM Studies of High Temperature Corrosion Behaviour of TiAl Intermetallics with Surface Modifications

The oxidation/sulphidation behaviour of a Ti‐46.7Al‐1.9W‐0.5Si alloy with a TiAl₃ diffusion coating was studied in an environment of H₂/H₂S/H₂O at 850^oC. The kinetic results demonstrate that the TiAl₃ coating significantly increased the high temperature corrosion resistance of Ti‐46.7Al‐1.9W‐0.5Si. The SEM, EDX, XRD and TEM analysis reveals that the formation of an Al₂O₃ scale on the surface of the TiAl₃‐coated sample was responsible for the enhancement of the corroison resistance. The Ti‐46.7Al‐1.9W‐0.5Si alloy was also modified by Nb ion implantation. The Nb ion implanted and as received sampels were subjected to cyclic oxidation in an open air at 800^oC. The Nb ion implantation not only increased the oxidation resistance but also substantially improved the adhesion of scale to the substrate.     

Training and optimization of an artificial neural network controlling a hybrid power filter

A hybrid power compensator (HPC) consisting of a static VAr compensator and a dynamic compensator needs to be optimally controlled during the compensation of nonlinear loads. The HPC must be controlled to meet minimum requirements in terms of power factor and harmonic distortion, while at the same time minimizing its total cost. An artificial neural network (ANN) is used to control the HPC amidst a very dynamic power system environment. The performance of a reference ANN is evaluated while controlling an HPC connected to a typical nonlinear industrial load. The training and performance of the ANN is then optimized in terms of training set size, training set packing and ANN topology and the performance compared to the reference ANN. This paper highlights the importance of optimising the mentioned ANN parameters to achieve optimum ANN training and modeling accuracy. The results obtained reveals that the application of an ANN in controlling an HPC is feasible given that the ANN parameters are chosen appropriately.     

High-performance MIM capacitor using ALD high-k HfO/sub 2/-Al/sub 2/O/sub 3/ laminate dielectrics

For the first time, we successfully fabricated and demonstrated high performance metal-insulator-metal (MIM) capacitors with HfO/sub 2/-Al/sub 2/O/sub 3/ laminate dielectric using atomic layer deposition (ALD) technique. Our data indicates that the laminate MIM capacitor can provide high capacitance density of 12.8 fF//spl mu/m/sup 2/ from 10 kHz up to 20 GHz, very low leakage current of 3.2 /spl times/ 10/sup -8/ A/cm/sup 2/ at 3.3 V, small linear voltage coefficient of capacitance of 240 ppm/V together with quadratic one of 1830 ppm/V/sup 2/, temperature coefficient of capacitance of 182 ppm//spl deg/C, and high breakdown field of /spl sim/6 MV/cm as well as promising reliability. As a result, the HfO/sub 2/-Al/sub 2/O/sub 3/ laminate is a very promising candidate for next generation MIM capacitor for radio frequency and mixed signal integrated circuit applications.     

溶胶--凝胶镀膜技术综述(连载5)

第三节　常见氧化物膜目前研究最多的氧化物膜可谓二氧化硅和二氧化钛膜 ,这两种薄膜也是接受呈色离子、制备彩色镀膜常用的基体膜 ,所以 ,有必要将它们单独列出 ,加以讨论。1　二氧化钛膜在所有高折射率材料中 ,由钛的化合物制备的氧化物膜具有特殊的实际意义。因此 ,对二氧化     

Bio-layer management in anaerobic membrane bioreactors for wastewater treatment.

Membrane separation technology represents an alternative way to achieve biomass retention in anaerobic bioreactors for wastewater treatment. Due to high biomass concentrations of anaerobic reactors, cake formation is likely to represent a major cause of flux decline. In the presented research, experiments are performed on the effect of biomass concentration and level of gas sparging on the hydraulic capacity of a submerged anaerobic membrane bioreactor. Both parameters significantly affected the hydraulic capacity, with biomass exerting the most pronounced effect. After 50 days of continuous operation the critical flux remained virtually unchanged, despite an increase in membrane resistance, suggesting that biomass characteristics and hydraulic conditions determine the bio-layer formation rather than the membrane's fouling level. The concept of bio-layer management is introduced to describe the programmed combination of actions performed in order to control the formation of biomass layer over membranes.     

ASON实际组网中架构及演进方式分析

对在实际组网中选择合理的ASON架构和保护方式作了相应分析，并为搭建可向ASON平滑演进的传统网络时需注意的问题提供了参考意见，     

Use of citric acid for heavy metals extraction from contaminated sewage sludge for land application.

Recent studies revealed that organic acids such as citric and oxalic acids seemed to be more promising as chemical extracting agents for removal of heavy metals from contaminated sludge, since they are biodegradable and can attain a higher metal extraction efficiency at mildly acidic pH compared to other extracting agents. Results of a lab-scale study on the efficiency of citric acid in the extraction of chromium (Cr), copper (Cu), lead (Pb), nickel (Ni) and zinc (Zn) from anaerobically digested sludge, revealed that citric acid seemed to be highly effective in extracting Cr (at 100%), Cu (at 88%), Ni (at 98%) and Zn (at 100%) at pH 2.33, mostly at 5 days leaching time except for Cu and Zn, which are at 1 day and 2 h contact times respectively. Lead removal at the same pH was also high at 95% but at a longer leaching time of 11 days. At pH 3, citric acid seemed to be highly effective in extracting Pb (at 100%) at 1 day leaching time, although higher removals were also attained for Ni (70%) and Zn (80%) at only 2 h leaching time. Chemical speciation studies showed that Cr, Cu and Ni in the sludge sample seem to predominate in residual fractions, while Pb and Zn were found mostly bound to organic and inorganic matter forms, hence the potential of the sludge for land application.