Fabrication and properties of low oxygen grade Al2O3 dispersion strengthened copper alloy

The low oxygen grade Al2O3 dispersion strengthened copper alloy without hydrogen-fired expansion was fabricated by the technique of vacuum hot press and hot extrusion. The mechanical and electrical properties measurements and microstructures observation on as-hot extruded, as-cold drawn and as-annealed Cu-Al2O3 alloy were conducted. The results show that the addition of a suitable amount of boron in the alloy can lower the residual free oxygen content and then inhibit the hydrogen-fired expansion. The density, σb, σ0.2, hardness, δ and electrical conductivity of the alloy reach 8.86 g/cm^3 (relative density of 99.6%), 340MPa, 250MPa, HB95,24% and 93%(IACS) respectively after hot extruded with the extrusion ratio of 30:1. Its properties have no change after annealed at 900℃ for 1h. Its strength increases after cold drawing, while its ductility and electrical conductivity drop gradually. Various properties of the cold drawn alloy can recover to those of as-extruded after annealed at 900℃ for 1h without the occurrence of recrystallization.     

TiB2含量对TiB2/Cu复合材料性能的影响

研究了TiB2含量对原位生成TiB2／Cu复合材料性能的影响。结果表明：TiB2／Cu复合材料的硬度、强度随TiB2含量的增加有所提高，但强度在TiB2的含量超过2．0％后有所下降，导电率随TiB2含量的增加有所下降，软化温度基本保持在900℃左右。     

Electrode Process of Y（Ⅲ）on Nickel Electrode and Surface Metallizing

ＥｌｅｃｔｒｏｄｅＰｒｏｃｅｓｓｏｆＹ（Ⅲ）ｏｎＮｉｃｋｅｌＥｌｅｃｔｒｏｄｅａｎｄＳｕｒｆａｃｅＭｅｔａｌｌｉｚｉｎｇＺｈｏｕＣｈｕｎｇｅｎ（周春根）（ＵｎｉｖｅｒｓｉｔｙｏｆＡｅｒｏｎａｕｔｉｃｓａｎｄＡｓｔｒｏｎａｕｔｉｃｓＢｅｉｊｉｎｇ，Ｂｅ...     

A FUZZY NEURAL NETWORK DECISION MODEL ON THE OPERATION PROCESS OF ELECTRIC FURNACE FOR CLEANING SLAG AND ITS APPLICATION

ＡＦＵＺＺＹＮＥＵＲＡＬＮＥＴＷＯＲＫＤＥＣＩＳＩＯＮＭＯＤＥＬＯＮＴＨＥＯＰＥＲＡＴＩＯＮＰＲＯＣＥＳＳＯＦＥＬＥＣＴＲＩＣＦＵＲＮＡＣＥＦＯＲＣＬＥＡＮＩＮＧＳＬＡＧＡＮＤＩＴＳＡＰＰＬＩＣＡＴＩＯＮ￥Ｐｅｎｇ，Ｘｉａｏｑｉ；Ｍｅｉ，Ｃｈｉ；Ｚｈ...     

低压铸造ZL114A合金微观组织的研究与数值模拟

通过浇注阶梯试样对低压铸造ZLll4A合金进行了试验研究，分析了不同冷却速率对合金凝固过程的影响。基于试验数据统计分析，建立了形核模型，并给出了模型相关热力学、动力学参数。结果表明，随着冷速的增加，液相线温度、形核温度和共晶转变温度均降低，初生相以及共晶相的形核、凝固时间缩短。采用了一种改进的Celluar Automaton方法，耦合有限差分法对合金的宏观凝固及微观组织演化过程进行了数值模拟。对航空启动机叶轮不同部位的微观组织进行了预测并将模拟值与试验值进行了对比验证，试验和模拟值吻合较好。     

（V30Ti35Cr25Fe10）97．5Si2．5合金的结构与吸放氢性能

采用XRD，SEM和PCT测试研究了（V30Ti35Cr25Fe10）97.5Si2.5（at％）合金的组织结构与吸放氢性能。结果表明：合金由BCC相和C14 Laves相组成，BCC相含量为75％，晶胞参数为α=0．3021nm，Laves相含量为25％，晶胞参数为α=0．4920nm和c=0．7996nm。由于含有大量的Laves相，合金具有良好的活化性能，室温下不需孕育期就可以快速吸氢，5min内达到吸氢饱和状态，饱和吸氢量达到2．98％（质量分数，下同）。在一定氢压下，合金的容量可由合金中BCC相和Laves相的容量按组分的含量进行线性组合而成。     

溴离子—罗丹明6G浮选光度法测定痕量铂

研究了Pt(Ⅳ)-Br~--罗丹明6G(R6G)-萃取-浮选光度法测定痕量铂.浮选物溶于丙酮,λ_(ma??)=530nm,ε=4.5×10~5L·mol~(-1)·cm~(-1).在最佳条件下,浮选物组成为〔(PtBr_6~(2-))·(2R6G~ )·3(R6G~ ·Br~-)〕.0.5～5μgPt/10ml符合比尔定律.在研究了30余种共存物质的影响中发现常见阴、阳离子允许量较大,1～16倍贵金属离子不产生干扰,有较好的选择性.     

AgNO3浓度对SPE电极镀覆纳米Ag的影响

采用浸渍还原法(I-R法)在Nafion离子膜上镀覆纳米Ag,并就AgNO3浓度对SPE电极镀覆纳米银的影响作了研究.研究表明采用I-R法可制得细致Ag镀层,有效增加Ag的分散度及电极的真实面积.在还原剂浓度为0.1mol·L-1,浸渍还原温度均为50℃及浸渍还原时间分别为40 min,60 min的条件下,调节浸渍液AgNO3浓度至3.5 mmol·L-1时,可获得致密、均匀的纳米级Ag/SPE电极.同时验证砂纸糙化的预处理有利于增加Ag的负载和附着力,有利于提高Ag催化层的有效面积.     

Ti14钛合金半固态下的变形行为研究

研究了Ti14钛合金半固态条件下的变形行为。半固态变形后．由于液相的出现，加快了原子扩散的能力．其变形激活能明显高于钛合金固态变形时的激活能。结果表明，变形后，晶界、晶内液相长大，形成了宽化的晶界和网格状结构。     

中国的稀有金属

本文简要介绍了中国稀有金属在研究、生产方面的发展概况。