Studying the formation process of chromate conversion coatings on aluminium using continuous electrochemical noise resistance measurements

A unique electrochemical technique, namely continuous noise resistance calculation (CNRC), was used to obtain electrochemical kinetic information from the formation process of chromate conversion coatings (CCC) on aluminium electrodes. It was found that the noise resistance (R_n) of aluminium electrodes remained almost unchanged during electrodes' immersion in a chromate containing acidic solution where the CCC films were supposed to form rapidly. This result indicates that the formation of CCC was associated with continuous corrosion of the aluminium electrodes and that the CCC films formed on aluminium surface were not intact barrier films, but most likely porous layers. The CCCs became protective only after they were aged in the environment. Based on these findings, the formation and inhibition mechanisms of CCC have been discussed.     

Anticorrosion Behavior of Nickel-Rich Conductive Coating in Red Soil and the Effects of Fe2(SO4)3 on its Corrosion Resistance

Protection of Metals and Physical Chemistry of Surfaces - Anticorrosive conductive coatings were prepared by adding solvents, dispersants, nickel powders, etc. to acrylic resin coatings with high...     

SIEMENS FM357多轴驱动模块在铸咀布流控制系统中的应用研究

本文介绍了SIEMENS FM357多轴驱动模块的特点及在超薄快速铸钇铸咀布流控制系统中的应用，并对FM357的参数调协、各功能模块及数据模块的应用做了阐述。     

T形接头细丝埋弧自动焊工艺的研究及应用

针对整体节点钢桥桁梁对T形对接接头的焊接质量的高要求，研究推荐了一种细丝埋弧自动焊的工艺方法。与常用的手工电弧焊工艺相比，其焊缝成形美观、质量优良，焊接生产效率高，已成功地应用于钢梁焊接制造中。     

船舶柴油机主控装置

本文详细介绍了一种船舶柴油机主控装置的功能，结构、工作原理以及软件设计等，经现场调试和海上实验，主控装置完全满足设计和应用的要求。     

压铸态AZ91D镁合金热压缩变形流变应力研究

在应变速率为0.01～10 s1、变形温度250～50℃的条件下,采用Geeble-1500D热模拟机对压铸态AZ91D镁合金进行热压缩变形试验,得到并分析了该材料在不同变形条件下的流变曲线.采用数理统计的方法对实验数据进行处理,建立了用Zener-Hollomom参数描述的该材料的高温塑性变形本构方程为ε=1.41× 1012 [sinh(0.014σ)]5.295 exp (-159 449.509/RT),采用双曲正弦函数确定了该材料的变形激活能Q=159.45 kJ·mol1;与重力铸造态AZ91D镁合金比较显示,其流变应力和变形激活能更低.     

含氧空位单斜相HfO2电子结构和光学性质的第一性原理研究

采用基于密度泛函理论的平面波超软赝势方法对含氧空位单斜相HfO2的电子结构和光学性质进行了计算。计算结果表明,氧空位缺陷的存在使得HfO2带隙中出现了缺陷态,主要由最近邻Hf原子的5d态组成。随后,结合计算的电子态密度分析了氧空位对HfO2材料介电常数和吸收系数的影响。氧空位存在时,在380～220 nm的紫外波段内出现了较弱的吸收峰。     

β退火参数对Ti6Al4V合金组织和性能的影响

钛合金β退火产生的片层组织可以显著提高材料的损伤容限性能.通过不同的β退火温度和冷却速率试验研究了β退火参数对Ti-6Al-4V合金组织和性能的影响.结果表明:β退火温度在Tβ+10℃～Tβ+50℃范围内,随着退火温度的提高,β晶粒尺寸不断长大,温度提高到Tβ+50℃,合金强度、塑性降低明显;β退火保温时间基本与退火温...     

预处理温度对Cr-Ni-Co-Mo马氏体时效不锈钢强度的影响

研究了预处理温度对Cr-Ni-Co-Mo马氏体时效不锈钢强度的影响,其内容包括预处理温度对原始锻态粗晶遗传及自发再结晶的影响,以及对最终热处理后残留+逆转变奥氏体量和力学性能的影响。结果表明:900 ℃以下预处理遗传锻态粗晶,即通过α′→γ切变机制形成高缺陷密度的奥氏体。预处理温度升高,最终750 ℃固溶、－73 ℃冷处理后的残留奥氏体量,以及500 ℃时效的残留+逆转变奥氏体量减少,因此最终的抗拉和屈服强度升高。预处理温度提高到800 ℃以上,则不再影响最终热处理后的残留+逆转变奥氏体量,因此抗拉和屈服强度趋于稳定。900 ℃以上预处理遗传的锻态粗晶自发再结晶使晶粒细化,降低形成的奥氏体内的缺陷密度,降低750 ℃固溶处理后奥氏体内累积的缺陷密度,最终的时效强化效应下降,导致晶粒细化并不能提高最终的强度。     

Li4SiO4 氚增殖陶瓷的制备及其与14Cr-ODS钢的腐蚀界面行为

Li₄SiO₄小球与ODS钢的化学相容性对聚变反应器的安全运行具有重要意义。研究了在500、600、700 ℃的氩气环境中保温300 h后ODS钢与小球接触界面组织和成分的变化。结果表明,在600~700 ℃时,Li₄SiO₄小球与ODS钢的界面发生了严重的元素互扩散和反应。在Li₄SiO₄小球表面,由于ODS钢中Fe和Cr的扩散,出现了一层薄薄的反应层,这也导致了密度的增加,破碎负荷从51 N （500 ℃）下降到32 N（700 ℃）。XRD图谱显示,ODS钢表面出现了LiCrO₂和LiFeO₂新相,说明Li₄SiO₄小球中的Li和O原子可以扩散到ODS中,与Fe、Cr元素在高温下发生反应形成腐蚀层。在700 ℃时,腐蚀层可分为2个氧化层。最外层是LiFeO₂和LiCrO₂的混合物,下一层主要是LiFeO₂。在ODS钢的表面,700 ℃/300 h条件下氧扩散系数为2.2×10^-14 cm²/s,这说明ODS钢作为一种包层结构材料,在未来的包层设计中需要一层耐腐蚀涂层。