Blocked crystallization in capped ultrathin polymer films studied by molecular simulations

The crystallization of capped ultrathin polymer films is closely dependent on film thickness and interfacial interaction. Using dynamic Monte Carlo simulations, the crystallization behaviors of polymer films confined between two substrates were investigated. The crystallization rate of confined polymers is reduced with high interfacial interactions. Above a critical strength of interfacial interaction, polymer crystallization in the thin film is inhibited within the simulation time scales. An increase in film thickness leads to a rise in critical interfacial interaction. In thicker films, the chains have more space to change conformation to form crystal stems. In addition, there are fewer absorbed segments in confined chains for the thicker films, and thus the chains have stronger ability to adjust their conformation. Therefore an increase in film thickness can cause a reduction in the entropic barrier required for the formation of crystals and thus an increase in the critical interfacial interaction. © 2018 Society of Chemical Industry     

Fabrication of Cu/graphite film/Cu sandwich composites with ultrahigh thermal conductivity for thermal management applications

Effective thermal management of electronic integrated devices with high powder density has become a serious issue, which requires materials with high thermal conductivity (TC). In order to solve the problem of weak bonding between graphite and Cu, a novel Cu/graphite film/Cu sandwich composite (Cu/GF/Cu composite) with ultrahigh TC was fabricated by electro-deposition. The micro-riveting structure was introduced to enhance the bonding strength between graphite film and deposited Cu layers by preparing a rectangular array of micro-holes on the graphite film before electro-deposition. TC and mechanical properties of the composites with different graphite volume fractions and current densities were investigated. The results showed that the TC enhancement generated by the micro-riveting structure for Cu/GF/Cu composites at low graphite content was more effective than that at high graphite content, and the strong texture orientation of deposited Cu resulted in high TC. Under the optimizing preparing condition, the highest in-plane TC reached 824.3 W·m⁻¹·K⁻¹, while the ultimate tensile strength of this composite was about four times higher than that of the graphite film.