Preparation and properties of CuInS2 thin film prepared from electroplated precursor

Thin CuInS₂ films were prepared by sulfurization of Cu/In bi-layers. First, the precursor layer was electroplated onto the treated surface of Mo-coated glass. Observation of the cross-section prepared by focused ion beam (FIB) etching revealed that the void-free film was initially formed on the top surface of the precursor layer and continued to grow until the advancing front of the film reached the Mo layer. The nucleation of voids near the bottom of the CuInS₂ film followed. To determine whether the condition of the Cu/In alloy influences the CuInS₂ quality we investigated the Cu/In alloy state using FIB. We found that the annealed precursor of low Cu/In ratio (1.2) has several voids in the mid position in the layer compared with Cu-rich precursor (1.6). The cross-sectional view of the Cu-rich absorber layer is uniform compared with the low copper absorber layer. Thin film solar cells were fabricated using the CuInS₂ film (Cu/In ratio: 1.2) as an optical absorber layer. It was found that the optimization of a sulfurization period is important in order to improve the cell efficiency. We have not yet obtained good results with high Cu-rich absorber because of a blister problem. This blister was found before sulfurization. So, we are going to solve this blister problem before sulfurization.     

A formation of compatible poly(vinyl alcohol)/alumina gel composite and its properties

A formation of poly(vinyl alcohol) (PVA)/alumina gel composite was investigated with a viewpoint of compatibility of the composite. An alumina sol was prepared from aluminium iso-propoxide (Al(iPro)₃). The alkoxide was hydrolyzed and the resultant hydrate was peptized to a clear sol with acetic acid. The composite were transparent in whole content of alumina. The effects of dispersed alumina on the sorption of water and mechanical properties of composite were examined. The composites containing PVA 40–50% are flexible. They are folded in various forms and can be drawn five times the initial length in humid state. The residues obtained by calcination to remove PVA at 600°C keep its original form and transparency.     

Polymerization of [2,5-bis(trifluoromethyl)phenyl]acetylene and polymer properties

Summary [2,5-Bis(trifluoromethyl)phenyl]acetylene [BTFPA; HCCC₆H₃-2, 5-(CF₃)₂]polymerized with W, Mo, and Nb catalysts to produce methanol-insoluble polymers in high yields. The poly(BTFPA) produced by the W(CO)₆-based catalyst at 30 °C was soluble in p-(CF₃)₂C₆H₄, and had relatively high molecular weight ([]=0.352 dL/g in p-(CF₃)₂C₆H₄). The main chain of the polymer was composed of alternating double bonds, and the polymer was a dark brown solid. The temperature at which the weight loss of the polymer started was higher than 300 °C. The polymerization behavior and polymer properties for BTFPA are compared with those for phenylacetylene and [o-(trifluoromethyl)phenyl]acetylene.     

Male pheromone of swift moth,Hepialus hecta L. (Lepidoptera: Hepialidae)

(R)-6-Ethyl-2-methyl-2,3-dihydro-4H-pyran-4-one, (1R,3S,5R)-3-ethyl-1,8-dimethyl-2,9-dioxabicyclo[3.3. 1]non-7-ene, and (1R,3S,5R)-3-ethyl-1,8-dimethyl-2,9-dioxabicyclo[3.3.1]non-7-en-6-one represent the main components in the male pheromone of the swift moth,Hepialus hecta. The amounts of the three components were 40, 5, and 5 g per male, respectively. Structure elucidation of the compounds was based on spectroscopic data as compared to synthetic reference samples. The absolute configurations were determined by gas chromatography on chiral stationary phases; optically active samples served as reference compounds. Electrophysiological and behavioral experiments with natural material and synthetic samples clearly showed the three heterocyclic compounds to act as pheromones. (E, E)--Farnesene represents the main component of the scent secretion of maleHepialus humuli.     

Contrasting effects of water-soluble and water-insoluble dietary fibers on bile acid conjugation and taurine metabolism in the rat

The effect of the type of dietary fiber on the bile acid and taurine metabolism was examined in rats. Diets containing 10% of various water-soluble fibers (citrus pectin, konjak mannan, guar gum) as compared to a fiber-free diet increased biliary excretion of total bile acids. In contrast, water-insoluble dietary fibers (cellulose, corn bran, chitin; 10% in the diets) as well as cholestyramine (5% in the diet) considerably, decreased bile acid excretion. Water-soluble dietary fibermediated increases in bile acid excretion were totally attributable to increases in glycine-conjugates. Thus, these fibers greatly increased by the bile acid glycine-to-taurine ratio (G/T). Excretio of glycine conjugates decreased more than that of taurine conjugates in rats fed various water-insoluble dietary fibers. As a results, G/T in rats fed water-insoluble fibers was significantly lowered as compared to G/T in animals fed a fiber-free diet. Cholestyramine did not affect the G/T ratio of bile acids. Fecal bile acid excretion and the activities of hepatic cholesterol 7α-hydroxylase (EC 1.14.13.17) in rats fed various water-soluble dietary fibers approximately doubled as compared to the respective values for rats fed a fiber-free diet. Whereas cholestyramine greatly increased these parameters, water-insoluble fibers did not significantly affect them. Various water-soluble fibers decreased hepatic concentration and urinary excretion of taurine as well as the activity of hepatic cysteine dioxygenase (EC 1.13.11.20). In contrast, water-insoluble fibers considerably increased hepatic taurine concentrations and enzyme activities. The parameters for taurine metabolism were unaffected by cholestyramine. It was suggested that the types of dietary fiber affected hepatic taurine synthesis and thus modified bile acid glycine/taurine ratios.     

Far infrared reflection spectra in narrow-gap semiconductors

Far infrared reflection spectra of Cd_XHg_1?X Se are measured in the region 20 to 600 cm^?1 at temperatures between 5 and 77 K. Reflection spectra are explained well by the dynamic dielectric function which is constructed as a sum of Γ₈?Γ₈ interband, intraband and phonon contributions. The plasmon-LO phonon coupling effect is also discussed.     

Experimental Evaluation of Characteristics of SR Motor Made of Permendur

A switched reluctance (SR) motor has a doubly salient pole structure. The performance of the SR motor strongly depends on the magnetic properties of the core material, since it consists only of an iron core and copper windings. This study experimentally evaluates the performance of an SR motor made of permendur (Fe–49% Co alloy), which has very high saturation flux density and low core loss. Two types of SR motors that have the same dimensions but different core materials are used: one motor is made of the conventional nonoriented Si steel, and the other is made of permendur. Comparison of the characteristics of the two motors shows that the performance of the permendur SR motor surpasses that of the conventional one in terms of output power and efficiency. © 2014 Wiley Periodicals, Inc. Electr Eng Jpn, 187(1): 51–57, 2014; Published online in Wiley Online Library ( wileyonlinelibrary.com ). DOI 10.1002/eej.22431     

Reduction of Vibration in Concentrated Winding Permanent Magnet Synchronous Motor by Means of Skew Effects of Rotor

Global warming and the problem of successfully incorporating environmental safeguards are promoting the need for a more power‐efficient motor. Therefore, as a driving source, permanent magnet synchronous motors (PMSMs) with concentrated winding are widely used in a variety of fields. However, a PMSM with a concentrated winding generates more vibration than one with a distributed winding because of the radial electromagnetic force. This paper describes the effect of a new skewed rotor on the characteristics of a concentrated winding PMSM. We investigated this effect by three‐dimensional finite element method (3D FEM) analysis and measurement. We also demonstrate that the proposed rotor is effective in reducing the radial electromagnetic force without decreasing motor efficiency. © 2014 Wiley Periodicals, Inc. Electr Eng Jpn, 187(2): 33–43, 2014; Published online in Wiley Online Library ( wileyonlinelibrary.com ). DOI 10.1002/eej.22400     

Structure and viscoelastic properties of segmented polyurethane blends

Structure and viscoelastic properties of segmented polyurethanurea (SPU) blends were investigated. The glass transition temperature (T_g) of poly(tetramethylene glycohol) (PTMG) in a soft-segment block of the component SPU increased with decreasing molecular weight of PTMG. The blend samples showed two T_gs of PTMG in the temperature dispersions of the loss modulus (E″) and loss tangent (tan δ). The value of E′ in the leathery region for the blend specimens was trongly affected by the morphology. The blends were considered to have a morphology where PTMG differing in molecular weight was localized. © 1996 John Wiley & Sons, Inc.     

Fracture and acoustic emission characteristics of glass fiber reinforced plastics panels for hot water

This study deals with the fracture process and acoustic emission (AE) characteristics of a randomly oriented E-glass fiber mat reinforcement with a crosslinked polyester. These panels were evaluated after they were immersed in hot water. The fiber volume content of the panel was 19%. Glass fiber reinforced plastics (GFRP) panels wer immersed in water at 81°C. Bending and AE monitoring tests were Performed and after bending, the cross-section of the specimen was observed by an optical microscope and SEM. The influence of degradation, due to water immersion, on the changes of fracture process of GFRP is discussed. The dominant fracture mode of the virgin specimen was matrix cracks, whereas that of the immersed specimen was debondings at the fiber bundle/matrix and fiber/matrix interfaces. This change was caused by reduction of the bonding strength at the interface. The scale of fracture can be estimated by both AE amplitude and AE energy and this estimation method was used to estimate the fracture mode changes of GFRP panels immersed in hot water.