Preparation and antifouling performance of thin inorganic ultrafiltration membrane via assisted sol-gel method with different composition of dual additives

A novel TiO₂ thin film was prepared on the ceramic hollow fiber by the sol-gel method using poly(vinylpyrrolidone) (PVP) and polyvinyl alcohol (PVA) as additives. SEM images verified the formation of TiO₂ layer with various thickness using different composition of titania sols. The effect of the PVP and PVA contents on the TiO₂ sol properties, the separation and the antifouling performance of the ultrafiltration membranes were investigated thoroughly. When the contents of PVP and PVA were 1.0 wt% and 0.8 wt%, respectively, the resultant membrane showed a thickness of 0.55 μm with a pure water flux of 255 L m^?2 h^?1. In addition, the adherent foulant bovine serum albumin was applied to evaluate the antifouling performance. During the three fouling-recovery cycles, the flux recovery ratio and the flux decay ratio maintained about 99% and 30%. The BSA flux and rejection were still 169 L m^?2 h^?1 and 96.9% after the cycles, indicating a superior antifouling property.     

Analyzing the Conditions for the Electrolytic Formation of Ensembles from Metal Nanowires in the Pores of Track Membranes

Theoretical Foundations of Chemical Engineering - The effect of the electrolyte composition, mass-transfer conditions, pore diameter, interpore distance, and electric parameters on the formation of...     

Influence of pH on the DSSC Performance of Template Assisted SnO2 Nanostructures

Journal of Inorganic and Organometallic Polymers and Materials - This paper reports the performance of alizarin based SnO2 dye-sensitized solar cells. A novel template assisted method has been...     

Experimental Investigation of Oblique Impact Behavior of Adhesively Bonded Composite Single-Lap Joints

Applied Composite Materials - Determining the impact behavior of adhesive joints allows the designing of high-strength joints. Therefore, the dynamic behavior of adhesive joints has recently become...     

Simultaneous fractionation of multiple classes of polyphenols from honeybush tea using solid-phase extraction

The structural diversity of polyphenols and the inherent limitations of current extraction techniques pose a challenge to extract polyphenols using a simple and green method. Hence, in this study, a method was developed to simultaneously fractionate multiple classes of polyphenols by only varying ethanol-water solutions. Honeybush tea, which is rich in polyphenols, was selected as a model for this study. Solvent extraction followed by solid-phase extraction (SPE) was developed to obtain a polyphenol-rich fraction from six honeybush samples. Based on a gradient elution programme (10%, 30%, 50%, 70% and 90% (v/v) ethanol-water solution) of SPE, the Strata X cartridge showed a better recovery of most targeted polyphenols under 0.9 mL of the drying volume and 1 mL min⁻¹ of the dispensing speed. The elution programme for fractionating most polyphenols was as follows: single elution with 50% ethanol, followed by twice elution with 70% ethanol. The antioxidant capacity was used to analyse the differences among the polyphenol-rich fractions from six honeybush samples. Principal component analysis (PCA) revealed that unfermented C. genistoides (GG) has the greatest antioxidant capacity among the honeybush species studied. Additionally, mangiferin, isomangiferin and vicenin-2 were the main contributors to the antioxidant capacity in six honeybush fractions according to the correlation study.     

Dual effect synergistically triggered Ce:(Y,Tb)3(Al,Mn)5O12 transparent ceramics enabling a high color-rendering index and excellent thermal stability for white LEDs

Ce:Y₃Al₅O₁₂ transparent ceramics (TCs) with appropriate emission light proportion and high thermal stability are significant to construct white light emitting diode devices with excellent chromaticity parameters. In this work, strategies of controlling crystal-field splitting around Ce³⁺ ion and doping orange-red emitting ion, were adopted to fabricate Ce:(Y,Tb)₃(Al,Mn)₅O₁₂ TCs via vacuum sintering technique. Notably, 85.4 % of the room-temperature luminescence intensity of the TC was retained at 150 °C, and the color rendering index was as high as 79.8. Furthermore, a 12 nm red shift and a 16.2 % increase of full width at half maximum were achieved owing to the synergistic effects of Tb³⁺ and Mn²⁺ ions. By combining TCs with a 460 nm blue chip, a warm white light with a low correlated color temperature of 4155 K was acquired. Meanwhile, the action mechanism of Tb³⁺ ion and the energy transfer between Ce³⁺ and Mn²⁺ ions were verified in prepared TCs.     

Enhancement of glass-ceramic performance by TiO2 doping: In vitro cell viability,proliferation, and differentiation

A new TiO₂-containing bioactive glass and glass-ceramics based on 50SiO₂-(45-X)CaO-(XTiO₂)-5P₂O₅ system was designed using a sol–gel technique (where X = 5, 7.5 and 10 wt %). The roles of the crystallization behavior and physicochemical characteristics of the designed glass and glass-ceramics which were played in the introduction of TiO₂ substitutions were investigated. Moreover, cell proliferation and differentiation were evaluated against human osteosarcoma cells (Saos-2). The TiO₂/CaO replacements led to the formation of a stronger glass structure and thus increased thermal parameters and the chemical stabilization of the designed materials. The FTIR data confirmed the existence of Ti within the glass and glass-ceramics samples, and no remarkable effect on their chemical integrity was observed. The XRD patterns indicated that calcium-containing minerals, including Ca₂SiO₄,Ca₃(PO₄)₂, Ca(Ti,Si)O₅, CaTiSiO₅, and Ca₁₅(PO₄)₂·(SiO₄)₆ phases were developed as a role of structure/texture under the applied heat-treatment. The results of the cytotoxicity test proved that a safe sample dose is 12–50 μg/ml, at which cell viability is ≥ 85%. The cell differentiation determined by ALP test proved the superiority of glass-ceramics compared with their native glasses. Therefore, the obtained materials could be safely used as novel biocompatible materials for the regeneration of bone tissue.     

Phase formation,structure and properties of light-weight aluminosilicate proppants based on clay-diabase and clay-granite binary mixes

One of the drawbacks of fusible clays is the narrow sintering interval due to a sharp increase in the amount of iron-silicate melt at a temperature of 1000–1100 °C, which hardens in the form of a glass phase upon cooling. This leads to a relatively low mechanical strength of the calcined samples and causes the danger of melting the granular material surface from such clays during the firing process. To increase the strength of samples of fusible clays, the influence of diabase and granitoid rocks was considered. It was found that the strengthening effect of diabase and granitoid rock additives in an amount of 20–50% in a mixture with fusible clay is due to an increase of total content of the crystalline phase (mullite, cristobalite and residual quartz) from 18–20% in clays without additives to 22–28 % - in mixtures with diabase and to 28–34% - with granitoid additives) at a temperature of 1050–1100 °C. This increase is due to the activation of synthesis processes of secondary mullite and crystallization from alkali-rich feldspar melt of amorphous silica, released from the structure of clay minerals. The established influence of the igneous rocks used made it possible to develop compositions and propose process flow sheet for producing aluminosilicate proppants based on fusible clays. The use of granitoid and diabase rocks in an amount of 20–70% with fusible clays produces lightweight aluminosilicate proppants with bulk density of 1.40–1.46 g/cm³ at temperature range of 1050–1100 °C, which can endure destructive pressures up to 34.5–52 MPa.     

Novel pearl millet couscous process for West African markets using a low-cost single-screw extruder

Traditional West African pearl millet couscous products are popular; however, their preparation is laborious, time-consuming and energy-demanding, involving agglomeration, steaming, drying and sieving steps. In this study, a process was developed to produce millet couscous using a high pressure, high temperature and low-cost single-screw extruder. The innovation was to directly process the cooked low-moisture extrudate to a couscous product by drying and milling to the appropriate particle size (ranging between 1 and 2 mm). Throughput for the traditional process as prepared for commercial sale is 50 kg per day, but with the same amount of labour, the extrusion process yields ~350 kg per day. A consumer sensory study held in Niamey (Niger) showed that the extruded millet couscous was comparable to traditional couscous, though this was dependent on selection of the proper millet variety. This novel extrusion process could stimulate small- to medium-scale manufacturing of couscous and couscous-type products in West Africa.     

Spray pressure variation effect on the properties of CdS thin films for photodetector applications

Herein, we report the photosensing property of CdS thin films. CdS thin films were coated onto glass substrates via a spray pyrolysis method using different spray pressures. Prepared films were characterized using X-ray diffraction (XRD), scanning electron microscopy (SEM), and optical and photoluminescence spectroscopy. XRD analysis demonstrated the growth of crystalline CdS films with crystallite sizes varying from 26 to 29 nm depending on the pressure. The SEM and EDAX analyses revealed nearly-stoichiometric CdS films with smooth surfaces and slight variation in grain morphology due to pressure changes. Optical measurements showed a direct bandgap varying from 2.37 eV to 2.42 eV due to pressure changes. A photodetector was also fabricated using the grown CdS films; the fabricated photodetector exhibited good performance depending on the spray pressure. A spray pressure of 1.5 GPa resulted in high photoresponsivity and external quantum efficiency.