热溶过滤法脱除煤焦油沥青中喹啉不溶物的研究

以5种煤焦油沥青为原料,喹啉为溶剂,研究了热溶过滤法脱除喹啉不溶物(QI)等杂质的效应,目的是制备QI含量较低的净化沥青。结果表明:热溶过滤法可以有效地脱除喹啉不溶物,QI脱除率随滤网网目增加而提高,但阻力增加,脱除时间变长。综合考虑脱除率和实际可操作性,采用1000目的滤布,QI含量可以降到0.3%以下,基本能达到要求。采用凝胶色谱对QI脱除后沥青的组成和分子量分布的研究表明,热溶过滤脱除了沥青中的大分子组分,分子量减小,分子量分布变窄。     

Wetting properties of polystyrene ionomers treated with plasma source ion implantation

The wetting properties of polystyrene‐based ionomers treated with plasma source ion implantation (PSII) were investigated by the measurement of water contact angles. When sulfonated ionomers were aged for a few days, the hydrophobic recovery for the ionomers became much slower than that for the nonionic polymers. However, when the samples were aged over 20 days, the water contact angle of the ionomers converged with that of the nonionic polymer. Thus, it was concluded that the ionic interaction between the ionic groups and the presence of ionic groups together resulted in the slow hydrophobic recovery and that the aging effect was significant for the ionomers. For the methacrylate ionomer of low ion content, on the other hand, it was found that the PSII treatment produced only a small change in hydrophobic recovery behavior. Thus, it was suggested that the low ionic content coupled with the small size of the ionic unit might cause changes only of a very insignificant degree in hydrophobic recovery behavior. © 2002 Wiley Periodicals, Inc. J Appl Polym Sci 83: 2500–2504, 2002     

表面处理对木粉增强PVC发泡复合板材性能的影响

研究表面处理的木粉对发泡聚氯乙烯(PVC)板材的增强改性效果。使用铝酸酯偶联剂、丙烯酸丁酯预聚物对木粉进行表面处理，将其混合到聚氯乙烯发泡板材配料中进行板材加工生产，结果表明，经处理的木粉能提高发泡PVC板材的拉伸强度和冲击强度。用铝酸酯偶联剂处理木粉的发泡板材力学性能好于用丙烯酸丁酯预聚物处理的板材；而用丙烯酸丁酯预聚物处理木粉的复合材料在流变加工性能优于用铝酸酯处理木粉的复合材料。     

单晶金刚石膜与多晶金刚石膜的制备工艺及性能

本文主要介绍了用微波等离子体化学气相沉积法(以下简称MP CVD法)以甲醇-氢气混合气和丙酮-氢气混合气为源气体,分别以单晶硅的(111)面和人造金刚石的(100)面为衬底材料,制备出了面积为20mm×20mm厚为10μm的多晶金刚石膜和面积为1.0mm×1.0mm厚为5μm的单晶金刚石膜。通过试验发现,源气体配比和衬底温度对薄膜质量起决定性作用。另外,衬底在反应腔中的位置对薄膜的生成也有很大影响。单晶金刚石膜制备过程中衬底金刚石的晶体取向与金刚石薄膜的生长及质量有密切的关系。在金刚石的(100),(110)和(111)面上分别获得了单晶金刚石膜和金刚石多晶粒子。选用扫描电镜、显微激光拉曼、反射电子衍射对多晶金刚石膜及单晶金刚石膜的性能进行了测试。     

Molecular dynamics simulations of the unfolding of {beta}2-microglobulin and its variants

In this study, we examined the unfolding processes of nativeß₂-microglobulin and two related variants, one withan N-terminal hexapeptide deletion     

Phase evolution and thermophysical properties of high-entropy RE2(Y0.2Yb0.2Nb0.2Ta0.2Ce0.2)2O7 oxides

Pursuing novel thermal barrier–coating materials with lower thermal conductivity and high-temperature stability can simultaneously improve the working efficiency and service temperature of a gas turbine. In this study, a series of high-entropy RE₂(Y_0.2Yb_0.2Nb_0.2Ta_0.2Ce_0.2)₂O₇ (RE = La, Nd, Sm, Gd, Dy, and Er) oxides were prepared though solid-state reaction. Through tuning the rare-earth cations, an order–disorder transition occurs from certain partially ordered weberite structure (C222₁) to disordered defective fluorite structure (Fm$\overline{3}$m). All the high-entropy RE₂(Y_0.2Yb_0.2Nb_0.2Ta_0.2Ce_0.2)₂O₇ oxides possess low thermal conductivity in the range of 0.91–1.34 W m⁻¹ K⁻¹ at room temperature, which can be attributed to increased lattice anharmonicity and disorder, resulting in additional phonon scattering. Herein, we proved that the incorporation of heterovalent cations at B-sites in high-entropy A₂B₂O₇ crystals is an effective strategy to reduce the thermal conductivity without compromising the decrease of oxygen vacancy. Moreover, the high-entropy RE₂(Y_0.2Yb_0.2Nb_0.2Ta_0.2Ce_0.2)₂O₇ oxides show the relatively higher thermal expansion coefficients of 10.3–10.7 × 10⁻⁶°C⁻¹ and excellent phase stability at elevated temperatures.     

微生物转化法合成L-酪氨酸

以对羟基苯甲醛、海因、氢氧化钠为原料 ,化学合成底物对羟基苯丙酮酸。采用来自大肠杆菌的天冬氨酸转氨酶对对羟基苯丙酮酸进行生物转化 ,并对转化条件进行了初步的研究 ,最终得到L-酪氨酸 ,转化率 75 %。     

Electrical properties of (Bi3.5La0.5)Ti3O12 thin-films prepared by liquid source misted chemical deposition

The ((Bi_3.5La_0.5)Ti₃O₁₂(BLT) thin-films used in this study were fabricated on a Pt(111)/SiO₂/Si(100) substrate by a Liquid Source Misted Chemical Deposition (LSMCD) technique. X-ray diffraction patterns showed that the BLT films were crystallized and no other phases were observed when annealed above 650 ‡C. Grain size and remnant polarizations increased with increase in the annealing temperature, while leakage current densities decreased. The remnant polarizations (Pr) increased from 2.0 to 4.8 and 19.0 μC/cm2 with increase in the annealing temperature from 650 to 700 and 750 ‡C, respectively. The BLT films annealed at 700 ‡C in O₂ showed a good fatigue resistance of reduced polarization by 10% after 10⁹ switching cycles when 9 V of bipolar voltage was applied at a frequency of 40 kHz.     

用于确定双吸离心泵Suter曲线的三维内特性法研究

水泵Suter曲线是泵站水锤分析的必备条件之一。现有用于获取双吸离心泵Suter曲线的实测法具有难度大、成本高的特点,而间接插值估算法的精度又比较低,本文提出了一种通过水泵流场三维数值计算确定双吸离心泵Suter曲线的新方法,简称三维内特性法。该方法采用计算流体力学(CFD)技术,对双吸离心泵的水力模型进行三维造型、工况离散、流场计算及结果转化,以快速、准确地获取双吸离心泵Suter曲线,在正水泵工况、正水轮机工况、反水轮机工况、反水泵工况等工况下,计算出相应流量、转速、扬程和转矩关系。定量分析表明,相比于间接插值估算法,采用三维内特性法获得的Suter曲线中,Wh(x)的计算精度平均提高了39.2%,Wb(x)的计算精度平均提高了26.3%;在将采用该方法获得的双吸离心泵Suter曲线用于事故停泵工况水锤分析时,计算得到的系统最大压力降低了15.0%,管线发生汽化压力的范围缩减了81.4%,双吸离心泵的最大倒流量增大了11.9%,最大倒转速降低了6.1%,与实际测试结果更为接近。该方法为提高双吸离心泵站水锤分析精度提供了一种新技术途径。     

聚四氟乙烯改性剂的制备及性能

介绍了隔膜法氯碱所用的聚四氟乙烯改性剂，即聚四氟乙烯乳液、聚四氟乙烯纤维（SM-1）、聚四氟乙烯类纤维（SM-2）的制造原理、制造方法以及在隔膜法氯碱上的应用效果。