Surface effects in nanocrystalline silicon

Exposure to ammonia (NH₃) increases the dark current (DC) in nanocrystalline silicon. Light soaking (LS) for short periods also enhances the dark current, which remains at a high value for a long time. Pumping alone is unable to restore the initial annealed state, but annealing brings it back. The final state obtained by LS and NH₃ exposure depends on the order in which they are performed. Evaporated selenium (Se) deposited on nanocrystalline silicon decreases the DC. These effects cannot be explained entirely by the presence of a-Si : H alone, in our sample. DC and photoluminescence (PL) measurements indicate the presence of two types of center in our sample, which behave differently when exposed to NH₃.     

Planar lightwave integrated circuits with embedded actives for board and substrate level optical signal distribution

This paper explores design options for planar optical interconnections integrated onto boards, discusses fabrication options for both beam turning and embedded interconnections to optoelectronic devices, describes integration processes for creating embedded planar optical interconnections, and discusses measurement results for a number of integration schemes that have been demonstrated by the authors. In the area of optical interconnections with beams coupled to and from the board, the topics covered include integrated metal-coated polymer mirrors and volume holographic gratings for optical beam turning perpendicular to the board. Optical interconnections that utilize active thin film (approximately 1-5 /spl mu/m thick) optoelectronic components embedded in the board are also discussed, using both Si and high temperature FR-4 substrates. Both direct and evanescent coupling of optical signals into and out of the waveguide are discussed using embedded optical lasers and photodetectors.     

Measurement and Identification of the Parameters of SPICE-Models of a Bipolar Transistor

A method of measuring and identifying the static parameters of a bipolar transistor is considered. The characteristic of the transistor, from which the parameters of the model are determined, is chosen depending on what group the calculated parameters belong to. The characteristics are measured in such a way that the equations of the model describing them can be reduced to the simplest form.     

Control of polishing of diamond films using microactuation and an atmospheric pressure plasma

In this work, the diamond deposited by hot filament chemical vapor deposition (CVD) is polished using an atmospheric pressure plasma. In order to position the film relative to the plasma, a microactuator system is designed using a stack of domed piezoelectric actuators. A dynamic model based on the physical system is developed and the model parameters are measured experimentally. A system based on laser triangulation is used to measure the position of the diamond film relative to the plasma. Control techniques are used to reduce the oscillations during actuation and to eliminate the steady state positioning error. With the application of feedback control, the overshoot is reduced to 2% and the settling time is reduced to 0.3 s. A preliminary set of experiments is performed to relate process parameters to the final surface roughness of the diamond film. The parameters studied include the film's time of exposure to the plasma, the height of the film relative to the plasma, and the distance from the film to the center of the plasma. It is found that the optimum exposure time is 15 min and the reduction of surface roughness is greatest when the distance between the film and the plasma is at a minimum. The best results are obtained when the top of the film is even in elevation with the tip of the top electrode. The diamond film is translated laterally along the plasma. When feedback control is not used, there is no change in the surface roughness. With feedback control implemented, the surface roughness of the diamond film is reduced by 33%.     

X-ray or UV adjustment of MOS threshold voltage: Analytical and numerical modeling

A model is formulated that describes how radiation-induced charge accumulates in the gate oxide of a MOS structure and how it decays through tunneling and thermal emission. The model is used in a numerical analysis of the x-ray or UV adjustment of threshold voltage in MOS-circuit manufacture. The limits of this process technique are evaluated.     

Second harmonic generation from a ferroelectric film

We derive an expression for transmittivity (T_SHG) of second harmonic generation (SHG) signals from a ferroelectric (FE) film. Intensities of up and down fields in the medium are investigated in relation to T_SHG. The derivations are made based on undepletion of input fields and nonlinear wave equation derived from the Maxwell equations. We present two cases: film without mirrors and with partial mirrors. Expressions for the newly derived nonlinear susceptibility coefficients of SHG for real crystal symmetry [J. Opt. Soc. Am. B 19 (2002) 2007] are used to get more realistic results. Variations in T_SHG with respect to film thickness are illustrated.     

1/f noise in large-area Hg<Subscript>1−x</Subscript>Cd<Subscript>x</Subscript>Te photodiodes

The 1/f noise in photovoltaic (PV) molecular-beam epitaxy (MBE)-grown Hg_1−xCd_xTe double-layer planar heterostructure (DLPH) large-area detectors is a critical noise component with the potential to limit sensitivity of the cross-track infrared sounder (CrIS) instrument. Therefore, an understanding of the origins and mechanisms of noise currents in these PV detectors is of great importance. Excess low-frequency noise has been measured on a number of 1000-μm-diameter active-area detectors of varying “quality” (i.e., having a wide range of I-V characteristics at 78 K). The 1/f noise was measured as a function of cut-off wavelength under illuminated conditions. For short-wave infrared (SWIR) detectors at 98 K, minimal 1/f noise was measured when the total current was dominated by diffusion with white noise spectral density in the mid-10⁻¹⁵A/Hz^1/2 range. For SWIR detectors dominated by other than diffusion current, the ratio, α, of the noise current in unit bandwidth i_n(f = 1 Hz, V_d = −60 mV, and Δf = 1 Hz) to dark current I_d(V_d = −60 mV) was α_SW-d = i_n/I_d ∼ 1 × 10⁻³. The SWIR detectors measured at 0 mV under illuminated conditions had median α_SW-P = i_n/I_ph ∼ 7 × 10⁻⁶. For mid-wave infrared (MWIR) detectors, α_MW-d = i_n/I_d ∼ 2 × 10⁻⁴, due to tunneling current contributions to the 1/f noise. Measurements on forty-nine 1000-μm-diameter MWIR detectors under illuminated conditions at 98 K and −60 mV bias resulted in α_MW-P = i_n/I_ph = 4.16 ± 1.69 × 10⁻⁶. A significant point to note is that the photo-induced noise spectra are nearly identical at 0 mV and 100 mV reverse bias, with a noise-current-to-photocurrent ratio, α_MW-P, in the mid 10⁻⁶ range. For long-wave infrared (LWIR) detectors measured at 78 K, the ratio, α_LW-d = i_n/I_d ∼ 6 × 10⁻⁶, for the best performers. The majority of the LWIR detectors exhibited α_LW-d on the order of 2 × 10⁻⁵. The photo-induced 1/f noise had α_LW-P = i_n/I_ph ∼ 5 × 10⁻⁶. The value of the noise-current-to-dark-current ratio, α appears to increase with increasing bandgap. It is not clear if this is due to different current mechanisms impacting 1/f noise performance. Measurements on detectors of different bandgaps are needed at temperatures where diffusion current is the dominant current. Excess low-frequency noise measurements made as a function of detector reverse bias indicate 1/f noise may result primarily from the dominant current mechanism at each particular bias. The 1/f noise was not a direct function of the applied bias.     

Effect of Sb implantation on copper silicides formation and morphology after annealing of Cu/Si structures

In this work, the solid state reaction between a thin film of copper and silicon has been studied using Rutherford backscattering spectroscopy, X-ray diffraction, scanning electron microscopy and microprobe analysis. Cu films of 400 and 900 Å thicknesses are thermally evaporated on Si(1 1 1) substrates, part of them had previously been implanted with antimony ions of 5×10¹⁴ or 5×10¹⁵ at. cm⁻² doses. The samples are heat-treated in vacuum at temperatures in the range 200–700 °C for various times. The results show the growth and formation of Cu₃Si and Cu₄Si silicides under crystallites shape dispatched on the sample surface, independently of the implantation dose. On the other hand, it is established that the copper layer is less and less consumed as the antimony dose increases, resulting in the accumulation of Sb⁺ ions at silicide/Si interface and in the silicide layer close to surface. The exposure of samples to air at room temperature shows the stability of Cu₄Si phase whereas the Cu₃Si silicide disappears to the benefit of the silicon dioxide formation. The observed phenomena are discussed.     

Evolution and structure of drying material bridges of pharmaceutical excipients: studies on a microscope slide

An experimental procedure was developed to study directly the process by which liquid bridges between small particles in a granule form and solidify. The evolution of saturated solutions of such pharmaceutical excipients as lactose and mannitol in a liquid bridge was studied on a system situated on a microscope slide. Solidification and crystallization kinetics and phase composition during and immediately following bridge formation were observed directly. It was shown that bridges on the microscope slide and in the granule behave very much the same regardless of the different length and diffusion-scales of the two systems.We found that solid bridge formation takes place in several consecutive but distinct steps. In the case of lactose, considerable shrinkage of the initial liquid bridge takes place prior to the onset of crystallization. Further bridge solidification at ambient conditions occurs via simultaneous crystallization and vitrification within minutes. As a result, a “solid” bridge usually contains both a crystalline and a non-crystalline phase, the crystalline phase being predominately α-lactose monohydrate. Most of the non-crystalline phase eventually converts to crystalline β-lactose but the process may take many hours or even days. Results for this process are compared for samples obtained from different manufacturers of commercially available lactose. In the case of mannitol, different polymorphic forms crystallize as the drying/crystallization process progresses. A formed “solid” bridge usually contains several polymorphs of mannitol. The relevance of the behavior of the two model systems (pure lactose and pure mannitol) to a real granulation and tabletting process is discussed.