研究了某种环氧树脂阻尼灌封胶在热氧老化的作用下分子结构、硬度、断面形貌以及动态力学性能随时间的变化．傅立叶红外光谱图表明，所制备的样品环氧基团反应比较完全，热氧老化后试样表面由仲胺和环氧基团形成的酯键发生了部分断裂和氧化；邵氏硬度的增加、瓦向高温区移动则表明在老化过程中复杂的固化反应仍然继续进行；最大损耗因子（tanδmax）波动较小表明试样老化后分子结构几乎保持不变；SEM图片显示试样的冲击断裂由老化前的韧性转变为老化后的脆性断裂．     

钻孔灌注桩施工中常见质量事故的控制和防治

介绍了钻孔灌注桩成孔质量的影响因素 ,详细叙述了钢筋笼的制作和吊放处理步骤 ,阐述了断桩发生的原因 ,提出了具体的防治措施 ,经实践效果良好     

聚丙烯酸钠类高吸水性树脂的研究

采用反相悬浮聚合法合成高吸水性树脂.将丙烯酸(单体,水相)用氢氧化钠部分中和,然后与环己烷(溶剂,油相)共混,用水溶性的过硫酸钾做引发剂,N,N-亚甲基双丙烯酰胺做交联剂,在一定的反应温度和时间下,得到聚丙烯酸钠高吸水性树脂.     

氩等离子体辐照反相乳液接枝改性涤纶织物的研究

首次提出了在等离子体辐照后再用反相乳液接枝改性涤纶织物的新方法,探讨了接枝颗粒特征以及织物各项物理力学性能.接枝织物的结构及性能的测试结果表明:接枝物的尺寸远小于纤维的直径,在提高织物吸湿性的同时,对织物透气性能和强力等无明显影响;实验也证实了乳液中未接枝单体可以再次聚合.     

Asymmetric Regulation System Fit for Chinese Telecom Market

After the new round of restructuring of Chinese telecom sector,it's pressing to formulate and implement asymmetric regulation policies so as to shape an effectively competitive market structure in a relatively short term.This paper reviewed the asymmetric regulation policies and practices carried out in foreign telecom market,and then according to the specific situations of Chinese telecom market,proposed the principles and corresponding policies for establishing an asymmetric regulation system fit for Chin...     

Formation of composites fabricated by exothermic dispersion reaction in A1-TiO2-B2O3 system

The formation of aluminum matrix composites fabricated by exothermic dispersion reaction in A1-TiO2-B2O3 system was investigated. The thermal analysis results show that the reactions are spontaneous and exothermic. The Gibbs free energy of α-Al2O3 is the lowest among all the combustion products, followed by TiB2 and Al3Ti. It is noted that when the B2O3/TiO2 mole ratio is below 1, the reaction products are composed of particle-like α-Al2O3, TiB2 and rod-like Al3Ti. The α-Al2O3 crystallites, resulting from the reaction between A1 and TiO2 or B2O3, are segregated at the grain boundaries due to a lower wettability with the matrix. SEM micrographs show that rod-like Al3Ti phase distributes uniformly in the matrix. When the BEO3/TiO2 mole ratio is around 1, the Al3Ti phase almost disappears in the composites, and the distribution of α-Al2O3 particulates is improved evidently.     

均匀设计法分析制备过程对钴钼硫化物催化剂机械强度的影响

建立了CoMoP/Al2O3加氢精制催化剂机械强度及其可靠性在制备过程中的数学模型,采用均匀设计考察了浸渍、干燥、煅烧、硫化4个制备过程中,浸渍时间、干燥温度、干燥时间、煅烧温度、煅烧时间、硫化温度和硫化升温速率7个实验因子对催化剂强度均值、Weibull模量的影响,同时考察了这些因素对颗粒密度的影响。方差分析表明所有模型都是充足的。实验结果表明,硫化过程是影响催化剂强度均值的主要过程。在实验范围内提高硫化温度、降低硫化时的升温速率有利于提高催化剂的强度。影响催化剂Weibull模量的因素主要为各个制备过程的交互效应。要提高催化剂强度的可靠性就必须全面考虑催化剂制备的各个过程,特别是各个制备过程的交互效应。