Use of polyethylene films photografted with 2‐(dimethylamino)ethyl methacrylate as a potential adsorbent for removal of chromium (VI) from aqueous medium

A new polymeric adsorbent material based on polyethylene (PE) was prepared by photografting of 2‐(dimethylamino)ethyl methacrylate (DMAEMA) as a positively chargeable monomer to a PE film. The effects of the experimental parameters, such as the pH value, temperature, and grafted amount on adsorption of chromium(VI) (Cr(VI)) ions were investigated for the DMAEMA‐grafted PE (PE‐g‐PDAMEMA) films. The maximum adsorption capacity was obtained at the initial pH value of 3.0 for a PE‐g‐PDMAEMA film with 1.8 mmol/g and the maximum adsorption capacity obtained was higher than or compatible to those of many of the other polymeric adsorbents prepared for Cr(VI) ions. The adsorption kinetics obeyed the mechanism of the pseudo‐second order kinetic model and adsorption of Cr(VI) ions on PE‐g‐PDMAEMA films was well expressed by the Langmuir isotherm model. A high Langmuir adsorption constant suggests that the adsorption of Cr(VI) ions occurs between protonated dimethylamino groups and ions mainly through the electrostatic interaction. Cr(VI) ions adsorbed were successfully desorbed from a PE‐g‐PDMAEMA film in solutions of NaCl, NH₄Cl, NH₄Cl containing NaOH, and NaOH and a PE‐g‐PDMAEMA film was regenerated and repeatedly used for adsorption of Cr(VI) ions without appreciable loss in the adsorption capacity. © 2016 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2016 , 133, 43360.     

Characterization of alternative plasticizers in poly(vinyl chloride) sheets for blood containers

This study aimed to optimize the ratio of dioctyl 4‐cyclohexene‐1,2‐dicarboxylate (DOTH) and di‐isononyl‐cyclohexane‐1,2‐dicarboxylate (DINCH^®) for use as plasticizers in poly(vinyl chloride) (PVC) sheets. We also evaluated the biological safety of DOTH for its potential to be part of a safe PVC‐based blood container. The suppression of hemolysis in mannitol‐adenine‐phosphate / red cell concentrates (MAP/RCC) with DOTH/(DINCH^®‐PVC) sheets and the elution of plasticizers from the sheets increased with higher DOTH compositions. The properties of the PVC sheet containing DOTH and DINCH^® in the ratio of 25:33 parts against PVC 100 parts as a weight were almost identical to the PVC sheet made of di(2‐ethylhexyl) phthalate. From a subchronic toxicity test, DOTH did not show any adverse effects on all organs, including the testes, epididymis, liver, and kidneys. The no‐observed‐adverse‐effect level was 300 mg/kg body weight/day in a rat. These results suggest that DOTH/DINCH^® (25:33) is a promising candidate for the replacement of di(2‐ethylhexyl) phthalate in blood containers. J. VINYL ADDIT. TECHNOL., 22:520–528, 2016. © 2015 Society of Plastics Engineers     

离子筛MnO_2·0.4H_2O的固相法制备及特性研究

以单水氢氧化锂和四氧化三锰为原料,用固相法制备出锂离子筛锰酸锂,改变n(锂)/n(锰)之后,用同样的方法制备出另一物质Li1.33Mn1.67O4,经硝酸洗涤脱锂后制备了锂离子筛MnO2·0.4H2O。测定了酸洗时前驱体的锂洗脱率、锰溶损率,研究了锂离子筛MnO2·0.4H2O的饱和吸附量、稳定性、pH滴定曲线。结果表明,前驱体Li1.33Mn1.67O4经硝酸二次酸洗后,锂洗脱率和锰溶损率分别为62.7%和6.0%。在含0.1 mol/L氢氧化钠和10 mmol/L氯化锂的溶液中,经固相法制备的锂离子筛MnO2·0.4H2O对锂离子的饱和吸附量达到24.6 mg/g,并且具有较好的稳定性,pH滴定曲线表明锂离子筛对锂离子具有很好的选择性。     

Additive Sintering,Postannealing, and Dielectric Properties of SrTaO2N

The maintaining of the chemical composition and electrical insulativity of SrTaO₂N ceramics was investigated during sintering and annealing, using powders prepared by the nitridation of Sr₂Ta₂O₇. Due to the low thermal stability of SrTaO₂N, the partial loss of SrO and nitrogen induced the formation of a TaO_0.9 impurity after heat‐treating at above 1100°C. The sintering additive SrCO₃ and postannealing in NH₃ were employed to compensate for the loss of SrO and nitrogen to obtain ceramics with the original chemical composition. The as‐sintered SrTaO₂N ceramics with various relative density (RD) were annealed in NH₃ to observe the recovery of color and electrical insulativity. It was found that the inner part of the well‐sintered samples with RD = 95.1% could not be recovered by annealing, and continued to exhibit semiconducting behavior and a black color. On the other hand, for the as‐sintered SrTaO₂N ceramics with RD < 84%, both the nitrogen content and electrically insulating behavior were completely recovered after annealing. The postannealed SrTaO₂N ceramics (RD = 83.3%) possessed a relatively large dielectric constant of 450 with a low dielectric loss of less than 0.1 at 100 Hz, almost independent of frequency and temperature.     

Dynamic mechanical properties of three‐component composites (acrylic polymer/epoxy/SiO2) in the glass‐transition region

In previous studies, we reported the linear and nonlinear rheological properties of three‐component composites consisting of acrylic polymer (AP), epoxy resin (EP), and various SiO₂ contents (AP/EP/SiO₂) in the molten state. In this study, the dynamic mechanical properties of AP/EP/SiO₂ composites with different particle sizes (0.5 and 8 μm) were investigated in the glass‐transition region. The EP consisted of three kinds of EP components. The α relaxation due to the glass transition shifted to a higher temperature with an increase in the volume fraction (?) for the AP/EP/SiO₂ composites having a particle size of 0.5 μm, but the α relaxation scarcely shifted for the composite having a particle size of 8 μm as a general result. This result suggested that the SiO₂ nanoparticles that were 0.5 μm in size adsorbed a lot of the low‐glass‐transition‐temperature (T_g) component because of their large surface area. The AP/SiO₂ composites did not exhibit a shift in T_g; this indicated that the composite did not adsorb any component. The modulus in the glassy state (E′_g) exhibited a very weak &phis; dependence for the AP/EP/SiO₂ composites having particle sizes of 0.5 and 8 μm, although E′_g of the AP/SiO₂ composites increased with &phis;. The AP/EP/SiO₂ composites exhibited a peculiar dynamic mechanical behavior, although the AP/SiO₂ composites showed the behavior of general two‐component composites. Scanning electron microscopic observations indicated that some components in the EP were adsorbed on the surface of the SiO₂ particles. We concluded that the peculiar behavior of the AP/EP/SiO₂ composites was due to the selective adsorption of the EP component. © 2014 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2014 , 131, 40409.     

Chain stiffness and chain conformation of poly(α-methylene-γ-butyrolactone) in dilute solutions

The chain stiffness and local chain conformation of atactic poly(α-methylene-γ-butyrolactone) (PMBL), which is a side chain cyclic structural analog of poly(methyl methacrylate) (PMMA), with a weight-average molecular weight (M_w) ranging from 2.8 × 10³ to 2.6 × 10⁶ in N,N-dimethylformamide (DMF) and γ-butyrolactone (GBL) were characterized by size exclusion chromatography with a multi-angle light-scattering detector (SEC-MALS) and synchrotron radiation small-angle X-ray scattering (SAXS). Based on the Kratky-Porod worm-like chain model, the scattering functions and the M_w dependence of z-average root-mean-square radius of gyration <S²>_z^1/2 yielded the Kuhn segment lengths λ⁻¹, the diameter of the PMBL chains d, and the excluded-volume strengths in DMF and GBL. The local conformation of atactic PMBL in DMF and GBL were slightly larger than those of atactic PMMA, due to the presence of the conformationally rigid lactone ring structure.     

Microbial synthesis and properties of poly(3-hydroxybutyrate-co-4-hydroxybutyrate)

Microbial synthesis of copolymers of [R]-3-hydroxybutyrate (3HB) and 4-hydroxybutyrate (4HB), P(3HB-co-4HB), by Alcaligenes eutrophus, Alcaligenes latus, and Comamonas acidovorans from various carbon sources has been studied. The copolyester compositions varied from 0 to 100 mol% 4HB, depending on the microorganism and the combination of carbon substrates supplied. The thermal and physical properties of compositions with 0–100 mol% 4HB were investigated. The copolyesters represented a wide variety of polymeric materials, from hard crystalline plastic to very elastic rubbers, depending on composition. The copolyester films with high 4HB fractions (64–100 mol% 4HB) exhibited the characteristics of a thermoplastic elastomer, and the tensile strength increased from 17 to 104 MPa as the 4HB fraction increased. The enzymatic degradation of P(3HB-co-4HB) films was studied in an aqueous solution of extracellular polyhydroxybutyrate (PHB) depolymerase from Alcaligenes faecalis or lipase from Rhizopus delemer. The erosion rate of P(3HB-co-4HB) films was strongly dependent on the copolymer composition. In addition, environmental degradation of P(3HB-co-4HB) films in sea water was investigated.     

影响啤酒酵母菌吸附铅离子条件的研究

采用啤酒酵母自制生物吸附剂用于吸附金属铅离子,考察了pH值、反应时间、酵母浓度及金属离子浓度对啤酒酵母吸附Pb2 的影响.单因素实验结果表明,当pH值为5.0、溶液初始Pb2 浓度为80 mg·L-1、啤酒酵母的浓度为1.0 g·L-1、反应时间为0.5 h时,吸附效果最佳.通过正交实验,确定初始Pb2 浓度为反应过程中的显著因素.     

Size-dependent separation of graphene oxide by deformation of packed-gel in a chromatographic column

ABSTRACT

A deformable gel-packed chromatographic column was used to separate as-synthesized graphite oxide with different sizes. The synthesized gel (56 µm) was deformed by pressure of the fluid flow and the gaps in the gels showed a range of sizes. A suspension of graphene oxide (0.1 g/L, 10 mL) was injected, and graphene oxide in the elution had a size at 0.56 μm and 0.14 μm, whereas in half upper and bottom domain of the gel layer graphene oxide had a size at 33 µm and 2.9 µm, respectively, demonstrating that graphene oxide suspension was separated by size through gel layer.     

Monitoring cure viscosity of epoxy composite

Viscosity is an important process variable that should be monitored and controlled to ensure the consistent and reliable production of graphite-fiber-reinforced composite parts by the autoclave/vacuum bag process. Unfortunately, no technique is currently known for the direct measurement of viscosity in this process. However, d.c. conductivity and a.c. phase lag appear to correlate quite well with viscosity, and either electrical property may be followed in order to indirectly monitor viscosity. As the method of measuring d.c. conductivity is so inexpensive, simple, and almost free of electrical interference compared to the method of measuring a.c. phase lag, it appears to be the method of first choice for application in an autoclave environment.