Determination of dislocation densities in HCP metals from X-ray diffraction line-broadening analysis

X-Ray diffraction (XRD) line-broadening analysis has been performed on highly textured Zr-2.5Nb specimens which had been deformed in tensile tests to produce well-controlled dislocation structures. An iterative deconvolution method has been applied to extract the broadening function for the material, using as standards, a Zr single crystal and a 0 pct deformed specimen. In both cases, for specific tensile tests, a significant contribution to the basal line braodening was observed, which was clearly not directly related to the dislocation structure generated by the deformation, i.e., so-called c-component dislocations having a component of their Burgers vectors perpendicular to the basal plane. Calculations showed that the extent of basal line broadening cannot be attributed to the secondary effect of strain from a-type dislocations, i.e., dislocations with Burgers vectors parallel with the basal plane. It is concluded that most of the line broadening observed was the result of intergranular strain distributions. These distributions are most prominent for grains oriented with their c-axes perpendicular to the tensile-deformation axis and resulted in basal-plane line broadening even when there were few, if any, c-component dislocations present. This article is based on a presentation made in the symposium entitled “Defect Properties and Mechanical Behavior of HCP Metals and Alloys” at the TMS Annual Meeting, February 11–15, 2001, in New Orleans, Louisiana, under the auspices of the following ASM committees: Materials Science and Critical Technology Sector, Structural Materials Division, Electronic, Magnetic & Photonic Materials Division, Chemistry & Physics of Materials Committee, Joint Nuclear Materials Committee, and Titanium Committee.     

Homogeneity characterisation of sintered (U,Gd)O2 pellets by X-ray diffraction

(U,Gd)O₂ sintered pellets are fabricated by different methods. The homogeneity characterisation of the Gd content seems to be necessary for a production control to qualify the process and the final product obtained. In this paper, we propose an analysis of the X-ray diffraction powder patterns through the Rietveld method, in which the differences between the experimental and the calculated data proposed from a crystalline structure model are evaluated. This result allows us to determine the cell parameters, that can be correlated with the Gd concentration, and the existence of other phases with different Gd contents.     

Interface characteristics and mechanical properties of carbon fibre reinforced copper composites

Interface characteristics of carbon fibre reinforced copper matrix composites materials with various interface states and their effect on the flexural strength of composites have been studied. Interfacial states are mechanical bonding, dissolution bonding and reaction bonding. To a certain extent, raising the interfacial strength enables an increase in the flexural strength due to prevention of carbon fibre being pulled out under low stress during fracture process of composites. Raising the interfacial bondage strength, causes the brittleness of composites to increase; the fracture surface of composites is converted from a fibre pull-out model to a fibre even model. While strengthening the interface bondage, the extent of chemical reaction and dissolution at the interface must be controlled to avoid degrading the carbon fibre.     

On the nonuniformity of a capillary flow

It is established that the capillary rise of a liquid has an oscillatory character, in contrast to the commonly accepted opinion that a vertical capillary is filled at a monotonically varying velocity. The value of the tangential shear stress arising in an ascending liquid is evaluated for ethyl alcohol and distilled water.     

Intraseptal scopolamine has differential effects on Pavlovian eye blink and heart rate conditioning.

Evaluated the effects of intraseptal scopolamine hydrobromide (40 μg) injections on Pavlovian (classical) conditioning, with tones used as the CS and a periorbital electric shock train as the UCS, using New Zealand albino rabbits. Eyeblink (EB) and heart rate (HTR) CRs were concomitantly recorded. Although injections of scopolamine into the medial septum impaired the acquisition of the Pavlovian conditioned eyelid reflex, these injections enhanced the magnitude of accompanying Pavlovian conditioned HTR decelerations. However, scopolamine applied to the lateral septal area had no effect on EB conditioning, relative to the vehicle; like medial injections, scopolamine also enhanced the magnitude of the accompanying HTR decelerations. Results are compatible with those of previous investigations indicating that medial septal dysfunction impairs somatomotor conditioning but leaves autonomic conditioning intact and that septal dysfunction produces a parasympathetic bias of the cardiovascular system. (49 ref) (PsycINFO Database Record (c) 2010 APA, all rights reserved)     

Specifying concurrent systems with TSL

The Task Sequencing Language (TSL), which lets programmers specify constraints on the behavior of concurrent programs, is described. The constraints, specified by high-level annotations to Ada programs, are monitored at runtime; when a violation is detected, control is returned to the user, along with information about the nature of the violation. It is argued that such a tool is a necessary crutch for human reasoning capabilities when dealing with the complexities of concurrent process interaction. The first large-scale application of TSL, the specification and validation of a distributed tasking supervisor for Ada, is described     

FATIGUE DAMAGE IN 1045 STEEL UNDER VARIABLE AMPLITUDE BIAXIAL LOADING

Abstract— During constant amplitude loading, two different types of crack systems have been reported In the high cycle fatigue (HCF) region, cracks nucleate on a small number of maxium shear strain amplitude planes One of these cracks becomes a dominant crack and leads to failure of the specimen In the low cycle fatigue (LCF) region, equally developed microcracks are observed over the entire gage section and grow during the majority of the life. The failure is due to a linking in which the microcracks join up during the last few cycles of the fatigue life.
To investigate the interaction of these two types of crack systems in biaxial fatigue, experiments were performed on thin-wall tubular specimens in tension, torsion and combined tension-torsion loading The test program included step loading and block loading in which two equivalent strain amplitudes were employed. One of the equivalent strain amplitudes is in the HCF region and the other was in the LCF region
Fatigue lives were predicted from constant amplitude damage curves when a single crack system dominated the fatigue process Two competitive crack systems were sometimes developed on the maximum shear strain amplitude planes in a single specimen under block loading This resulted in a conservative prediction of the fatigue life.     

Contextualizing is not nullifying: Reply to Mills (2005).

In omitting crucial words and sentencees, neglecting relevant citations, and overlooking important distinctions, Jon Mills' (see record 2005-04819-001) critique of relational psychoanalysis significantly misrepresents the authors' viewpoint. This viewpoint seeks to contextualize, but not to nullify, individual worlds of experience and their limiting horizons. (PsycINFO Database Record (c) 2010 APA, all rights reserved)