Migration of Point Defects in the Field of a Temperature Gradient

The influence of the temperature gradient over the thickness of the cladding of a fuel element of a fast-neutron reactor on the migration of point defects formed in the cladding material due to neutron irradiation has been studied. It has been shown that, under the action of the temperature gradient, the flux of vacancies onto the inner surface of the cladding is higher than the flux of interstitial atoms, which leads to the formation of a specific concentration profile in the cladding with a vacancy-depleted zone near the inner surface. The experimental results on the spatial distribution of pores over the cladding thickness have been presented with which the data on the concentration profiles and vacancy fluxes have been compared.     

A Giant Frequency Shift in the Raman Spectrum of Water Adsorbed on a Metallic Silver Surface

The Raman spectrum of water adsorbed on a metallic silver surface reveals an anomalously large shift of the vibrational frequency as compared to that in the bulk. The results are compared to data reported by other researchers, and possible interpretations of the observed phenomenon are discussed.     

Strain Concentration Effect in Cu–Al–Ni Single Crystals under a Longitudinal Bending Force

The behavior of a superelastic Cu?14.2% Al?4%Ni single crystal in the case of high reversible strains under a longitudinal bending force was investigated. The effect of strain confinement along the crystal length was revealed and studied. The highest reversible strains (up to 10%) were shown to be confined within the central part of the bent crystal.     

Role of Elastic Interphase Deformations in the Formation of Crystal Structure of β-Nb Particles Precipitating in a Zr–2.5% Nb Alloy

X-ray diffraction analysis has been used to study the structure of the α-Zr matrix phase and the precipitation of β-Nb particles upon the annealing of a Zr–2.5% Nb deformed alloy. It has been found that the process of the precipitation of the strengthening β-Nb particles in the alloy is accompanied by the appearance of fields of elastic interphase deformations in the matrix α phase of the alloy due to the difference in the specific atomic volumes of the crystal structures of the matrix and precipitated phases. It has been shown experimentally that, as a result of the presence of interphase deformations in the alloy, the bcc crystal structure of the precipitating β-Nb particles undergoes monoclinic distortions.     

Deformation of a surface layer and coating application using a flexible tool

The microstructure and properties of the functional coatings formed by impact friction processing of product surfaces with a flexible tool are studied. It is established that the processing produces a hard nanostructured surface layer with fragments up to 0.13 µm in size, as it is achieved by severe plastic deformation.     

Simulation of characteristics of double-junction solar cells based on ZnSiP2 heterostructures on silicon substrate

Design and operation modes of double-junction monolithic lattice-matched solar cells based on the ZnSiP₂/Si system of materials have been calculated. The effect of the photoactive region thickness and minority carrier lifetime in ZnSiP₂ layers on the efficiency of conversion of the incident solar light energy into electrical power was determined. It is shown that solar cells based on ZnSiP₂/Si heterostructures can provide efficiencies of 28.8% at AM1.5D, 100 mW/cm², and 33.3% at AM1.5D, 200 W/cm².     

Temperature cycling and its effect on mechanical behaviours of highporosity chalks

Temperature history can have a significant effect on the strength of water-saturated chalk.In this study,hydrostatic stress cycles are applied to understand the mechanical response of chalk samples exposed to temperature cycling between each stress cycle,compared to the samples tested at a constant temperature.The total accumulated strain during a stress cycle and the irreversible strain are reported.Chalk samples from Kansas(USA)and Mons(Belgium),with different degrees of induration(i.e.amount of contact cementation),were used.The samples were saturated with equilibrated water(polar)and nonpolar Isopar H oil to quantify water weakening.All samples tested during 10 stress cycles with varying temperature(i.e.temperature cycled in between each stress cycle)accumulated more strain than those tested at constant temperatures.All the stress cycles were performed at 30℃.The two chalk types behaved similarly when saturated with Isopar H oil,but differently when saturated with water.When saturated with water,the stronger Kansas chalk accumulated more total strain and more irreversible strain within each stress cycle than the weaker Mons chalk.     

Process and joint quality of ultrasonic vibration enhanced friction stir lap welding

In order to improve the process effectiveness and joint quality, ultrasonic vibrations were integrated with friction stir lap welding. Effect of ultrasonic exertion on the process and joint quality of AA 6061-T6 were investigated. Upon ultrasonic exertion, joints owned larger effective lap width, shorter hooks and improved strength. Weld fracture mode changed from a ductile–brittle mixed mode to a more ductile mode while the fracture path shifted from lap interface to beyond the stir zone. Material flow and interface defects were characterised using lap welded dissimilar aluminium alloy joints. Ultrasonic vibration improved the material flow and reduced the interfacial defects. Variations in failure load of joints were found in accordance with the variations in material flow and interfacial defects.