全文获取类型
收费全文 | 39篇 |
免费 | 4篇 |
专业分类
电工技术 | 2篇 |
化学工业 | 4篇 |
金属工艺 | 1篇 |
建筑科学 | 2篇 |
能源动力 | 13篇 |
轻工业 | 8篇 |
水利工程 | 1篇 |
一般工业技术 | 10篇 |
原子能技术 | 1篇 |
自动化技术 | 1篇 |
出版年
2020年 | 2篇 |
2018年 | 2篇 |
2017年 | 1篇 |
2016年 | 1篇 |
2015年 | 2篇 |
2014年 | 3篇 |
2012年 | 1篇 |
2010年 | 3篇 |
2009年 | 3篇 |
2008年 | 3篇 |
2007年 | 4篇 |
2006年 | 2篇 |
2005年 | 1篇 |
2004年 | 1篇 |
2003年 | 1篇 |
2001年 | 1篇 |
1999年 | 1篇 |
1997年 | 1篇 |
1991年 | 1篇 |
1989年 | 1篇 |
1987年 | 1篇 |
1979年 | 1篇 |
1977年 | 1篇 |
1976年 | 2篇 |
1963年 | 1篇 |
1961年 | 1篇 |
1959年 | 1篇 |
排序方式: 共有43条查询结果,搜索用时 0 毫秒
41.
Y. KONDO H. EDA M. KUBOTA 《Fatigue & Fracture of Engineering Materials & Structures》2009,32(9):736-743
It is usually regarded as a common understanding that fatigue failure would not occur if all stresses were kept within fatigue limit diagram. However, it was shown that fatigue failure occurred in some special cases of variable amplitude loading condition even when all stresses were kept within fatigue limit diagram in the case of small-notched specimen. The cause of such a phenomenon was examined using two-step stress pattern for low alloy steel SCM440H. In the case of constant stress amplitude loading, non-propagating crack was formed only at low mean stress and not formed at high mean stress. However, in the case of two-step stress pattern in which the first step stress was chosen as R =−1 and the second step stress was with high mean stress, a non-propagating crack was formed by the first step stress. This crack functioned as a pre-crack for the second step stress with high mean stress. Consequently, fatigue failure occurred by the stresses within fatigue limit diagram. In this study, the effect of notch size and shape were examined. The effect of absorbed hydrogen was also investigated. Absorption of 0.3 ppm hydrogen caused more reduction of fatigue limit. 相似文献
42.
43.
Y. KONDO C. SAKAE M. KUBOTA T. NAGASUE S. SATO 《Fatigue & Fracture of Engineering Materials & Structures》2004,27(5):361-368
This paper proposes a local stress concept to evaluate the fretting fatigue limit for contact edge cracks. A unique S–N curve based on the local stress could be obtained for a contact edge crack irrespective of mechanical factors such as contact pressure, relative slip, contact length, specimen size and loading type. The analytical background for the local stress concept was studied using FEM analysis. It was shown that the local stress uniquely determined the ΔK change due to crack growth as well as the stress distribution near the contact edge. The condition that determined the fretting fatigue limit was predicted by combining the ΔK change due to crack growth and the ΔKth for a short crack. The formation of a non‐propagating crack at the fatigue limit was predicted by the model and it was experimentally confirmed by a long‐life fretting fatigue test. 相似文献