Structural Control of NiO–YSZ/LSCF–YSZ Dual‐Layer Hollow Fiber Membrane for Potential Syngas Production

The objective of this study was to fabricate dual‐layer hollow fiber as a microreactor for potential syngas production via phase inversion‐based co‐extrusion/cosintering process. As the main challenge of phase inversion is the difficulty to obtain defect‐free fiber, this work focuses on the effect of the fabrication parameters, that is, nonsolvent content, sintering temperature and outer‐layer extrusion rate, on the macrostructure of the produced hollow fiber. SEM images confirm that the addition of nonsolvent has successfully minimized the finger‐like formation. At high sintering temperature, more dense hollow fiber was formed while outer‐layer extrusion rate affects the outer layer thickness.     

COSMO-RS:An ionic liquid prescreening tool for gas hydrate mitigation

Recently ionic liquids(ILs) are introduced as novel dual function gas hydrate inhibitors. However, no desired gas hydrate inhibition has been reported due to poor IL selection and/or tuning method. Trial error as well as selection based on existing literature are the methods currently employed for selecting and/or tuning ILs. These methods are probabilistic, time consuming, expensive and may not result in selecting high performance ILs for gas hydrate mitigation. In this work, COSMO-RS is considered as a prescreening tool of ILs for gas hydrate mitigation by predicting the hydrogen bonding energies(E_(HB)) of studied IL inhibitors and comparing the predicted E_(HB) to the depression temperature(?) and induction time. Results show that, predicted EHBand chain length of ILs strongly relate and significantly affect the gas hydrate inhibition depression temperature but correlate moderately(R = 0.70) with average induction time in literature. It is deduced from the results that, ? increases with increasing IL EHBand/or decreases with increasing chain length. However, the cation–anion pairing of ILs also affects IL gas hydrate inhibition performance. Furthermore, a visual and better understanding of IL/water behavior for gas hydrate inhibition in terms of hydrogen bond donor and acceptor interaction analysis is also presented by determining the sigma profile and sigma potential of studied IL cations and anions used for gas hydrate mitigation for easy IL selection.     

Evolution and stability of 2-mercaptobenzimidazole inhibitor film upon Al alloy 6061

Journal of Applied Electrochemistry - Organic corrosion inhibitors have become competent alternatives to hazardous chrome conversion coatings due to their rapid adsorption over metal surfaces in...     

Microbial fuel cell-based sensor for Enterobacter sp. KBH6958 activity monitoring during hydrogen production: the effects of pH and glucose concentration

Journal of Applied Electrochemistry - A microbial fuel cell (MFC) is an electricity-generating device utilising electrochemically active microorganisms as biocatalysts. Using MFC as a biosensor to...     

Selective formation of tungsten nanowires

We report on a process for fabricating self-aligned tungsten (W) nanowires with polycrystalline silicon core. Tungsten nanowires as thin as 10 nm were formed by utilizing polysilicon sidewall transfer technology followed by selective deposition of tungsten by chemical vapor deposition (CVD) using WF6 as the precursor. With selective CVD, the process is self-limiting whereby the tungsten formation is confined to the polysilicon regions; hence, the nanowires are formed without the need for lithography or for additional processing. The fabricated tungsten nanowires were observed to be perfectly aligned, showing 100% selectivity to polysilicon and can be made to be electrically isolated from one another. The electrical conductivity of the nanowires was characterized to determine the effect of its physical dimensions. The conductivity for the tungsten nanowires were found to be 40% higher when compared to doped polysilicon nanowires of similar dimensions.     

Use of a Reflectance Spectroscopy Accessory for Optical Characterization of ZnO-Bi(2)O(3)-TiO(2) Ceramics

The optical band-gap energy (E(g)) is an important feature of semiconductors which determines their applications in optoelectronics. Therefore, it is necessary to investigate the electronic states of ceramic ZnO and the effect of doped impurities under different processing conditions. E(g) of the ceramic ZnO + xBi(2)O(3) + xTiO(2), where x = 0.5 mol%, was determined using a UV-Vis spectrophotometer attached to a Reflectance Spectroscopy Accessory for powdered samples. The samples was prepared using the solid-state route and sintered at temperatures from 1140 to 1260 °C for 45 and 90 minutes. E(g) was observed to decrease with an increase of sintering temperature. XRD analysis indicated hexagonal ZnO and few small peaks of intergranular layers of secondary phases. The relative density of the sintered ceramics decreased and the average grain size increased with the increase of sintering temperature.     

Comparison of ionic liquid,acid and alkali pretreatments for sugarcane bagasse enzymatic saccharification

BACKGROUND: Much attention has been given to applying ionic liquids (ILs) as an alternative pretreatment method for lignocellulosic biomass. This study aims to select the most suitable type of IL for pretreating sugarcane bagasse (SCB). The potential of ILs for pretreatment was evaluated and compared with conventional pretreatment media, acids and alkalis. The performance of the pretreatment media was evaluated based on the amount of reducing sugar produced from enzymatic saccharification, the energy requirement, and changes in the chemical structure and crystallinity index of the pretreated bagasse. RESULTS: 1‐ethyl‐3‐methylimidazolium acetate [EMIM]oAc was selected as the most suitable IL for SCB pretreatment. The optimum yields of reducing sugar obtained from [EMIM]oAc‐, alkali‐, and acid‐pretreated SCB were 69.5%, 92.8% and 41.3%, respectively. Although a lower yield of reducing sugar was obtained, [EMIM]oAc pretreatment required the least energy to pretreat 1 kg of SCB. Moreover, the percentage of SCB loss during [EMIM]oAc pretreatment was the lowest. [EMIM]oAc‐pretreated SCB also had the lowest crystallinity index (CI) with the most amorphous structure. CONCLUSION: [EMIM]oAc appears to be another option for pretreating SCB, and other issues such as the recyclability of [EMIM]oAc is worth investigating. Copyright © 2011 Society of Chemical Industry     

Development of coating materials from liquid wax esters for wood top-based coating

Of late, UV-curable products are gaining attention in the wood industry because of the effectiveness and efficiency of this method. UV-curable surface coatings are widely used because of their excellent properties and because they are environmentally friendly products. In this study, immobilized Candida antarctica lipase B was used to catalyze formation of liquid wax esters, such as adipate esters, via a solvent-free process. The adipate esters formed were then used as UV-curable reactants in the wood coating formulations, consisting of epoxy acrylate, additives, and a photoinitiator. The performance of the products was evaluated by coating them onto glass tiles (using gel content, hardness, and scratch resistance tests) and wood panels (using adhesion, impact, and heat resistance tests). The coated film from this formulation performed well during the evaluation tests. The gel content exhibited more than 90% polymerization, while the pendulum hardness gave a value of 55.25%. Both analyses were significant in determining the effect of irradiation cycles. A scratch test was also carried out to verify the resistance of the coating. The maximum weight load which can be resisted by the wax esters formulation is 4.5 N.     

Direct Growth and Photoluminescence of SiO<Subscript>x</Subscript> Nanowires and Aligned Nanocakes by Simple Carbothermal Evaporation

The growth of SiO_x nanowires and nanocakes on an Au-coated n-type-Silicon (100) substrate was achieved via carbothermal evaporation. The effects of the Au layer thickness and the rapid heating rate on the morphology of obtained SiO_x nanowires were investigated. A broad emission band from 290 to 600 nm was observed in the photoluminescence (PL) spectrum of these nanowires. There are four PL peaks: one blue emission peak 485 nm (2.56 eV) two green bands centered at 502 nm (2.47 eV) and 524 nm (2.37 eV) for nanocakes and one ultraviolet emission peak at 350 nm (3.54 eV) and a hemisphere curve over the bluish green area taken for SiO_x nanowires. These emissions may be related to the various oxygen defects and twofold coordinated silicon lone pair centers.     

Water absorption and dimensional stability of short kenaf fiber‐filled polypropylene composites treated with maleated polypropylene

The purpose of this research was to investigate the water absorption behavior and associated dimensional stability of kenaf‐polypropylene‐filled (PP/KF) composites. Composites with different fiber loadings, ranging from 0 to 40 wt %, were prepared with a twin‐screw extruder followed by hot press molding. The influence of the compatibilizer was also studied for PP/KF composite with 5 wt % maleated PP (MAPP). Water absorption testing was carried out at room temperature for 7 weeks. Tensile, flexural, and impact tests were also performed on control, wet, and re‐dried specimens. Increasing the fiber content resulted in higher water absorption and thickness swelling. The inferior mechanical properties of the wet composites were attributed to the effect of water, which deteriorates the interfacial properties of composites. On re‐drying, all properties were almost recovered because of the recovery of interfacial area as evident in scanning electron micrographs. Incorporation of the MAPP significantly improved the compatibility between the fiber and matrix and the mechanical properties of the composites compared with those without MAPP. It also diminished the water absorption as well as the related thickness swelling in the composites. © 2010 Wiley Periodicals, Inc. J Appl Polym Sci, 2010