Effect of rotary direction and speed on mechanical properties in friction stir spot welding of A6061 sheets e

Friction stir spot welding of A6061 sheets was conducted using a tool with thread pin. The hook geometries, hook formation and mechanical properties of the joints welded with different rotary directions and speeds were investigated. The results show that the hook in the joint welded in clockwise was curved upwards and that in anticlockwise was curved downwards. The hook formation was related to the plastic material flow in the joint. With increasing the rotary speed in clockwise direction, the hook moved upwards and far way from the center of the keyhole, resulting in an increase in the effective weld width and a decrease in the effective sheet thickness. Three types of fractuces were observed and they were affected by the hook geometries. The tensile shear load increased firstly and then decreased when the rotary speed increased in clockwise direction, which was related to the hook geometries.     

城市电网规划的负荷预测方法探讨

在对城市电网电力负荷预测模型方法进行简单阐述后,对城市电网规划设计的电力负荷综合预测体系进行了详细分析研究。最后,结合当地电网规划设计实例,详细分析了空间负荷预测法在城市电网规划设计中的应用。     

用STM32触发捕捉实现高速高精度测频

介绍利用STM32F103单片机实现高速、高精度测频的原理及方法。利用16位定时器4(TIM4)产生1s的溢出触发脉冲复位定时器2(TIM2),同时清零前的计数值被捕捉到通道1的捕捉比较寄存器TIM2_CCR1中。为了提高整个程序的效率,可及时响应各个中断,采用了消息驱动的方式,当1s溢出中断时,投递消息完成对显示器缓冲区的定时刷新。该测频系统最高频率可测到288MHz,最低可测到4Hz,性能稳定。     

仿真软件在《电路》教学中的应用

本文介绍了仿真软件Multisim在电路教学中的应用,有效地使用该仿真软件,可以增加课堂容量,加强学生的动手能力和电路分析能力。实践表明,采用Multisim软件的电路仿真教学效果良好,有效地解决了电路教学中的一些问题。     

数字音频解码器的设计与分析

针对目前数字音频解码器不能对现有主流有线无线数字信号全部解码、信噪比不够等问题,通过蓝牙CSR8675、AK4113、PCM1795等硬件解码模块,设计制作集蓝牙、USB数字信号、数字同轴信号、数字平衡信号及数字光纤音频信号等于一体的解码器,一站式解决有线无线主流信号解码;通过串联稳压电源给解码器供电,减小电源纹波,提高信噪比;使用STC单片机实现数字音频解码器按键音源切换、显示等智能控制,具有较高的市场推广价值.     

用热塑性挤压合金化法制备钛铝系金属间化合物

本文以工业纯铝为基材、Ti粉为合金化添加粉末,试验用热塑性挤压合金化的方法制得钛铝金属间化合物.对热塑性挤压合金化制备Ti-Al金属间化合物进行了工艺研究,利用X射线衍射仪及Topas(2)X射线分析软件进行物相及晶粒尺寸分析,用金相显微镜对试样进行宏观及微观形貌分析,用显微硬度计对试样进行显微硬度测试.结果表明用热塑性挤压合金化方法可制得Ti-Al系金属间化合物;生成的金属间化合物相为Al3Ti,均匀分布于基体纯铝上,其质量百分比达44.5%;热塑性挤压合金化后挤压区硬度显著高于基材纯铝,最高达10倍;在整个挤压区,硬度分布比较均匀.     

La2O3含量对搅拌摩擦加工制备Ni /Al复合材料组织和性能的影响

采用搅拌摩擦加工方法在Al基体中添加不同La₂O₃含量的混合粉末(Ni+La₂O₃),制备 (Ni+La₂O₃)/Al复合材料。采用SEM、EDS、 EPMA及XRD对复合区微观结构及相组成进行分析,采用室温拉伸试验对 (Ni+La₂O₃)/Al复合材料力学性能进行了测试。结果表明,随着La₂O₃含量的增加,(Ni+La₂O₃)/Al复合材料的组织和性能先变好后变差。当La₂O₃添加量达到5%时,复合材料中Al₃Ni增强颗粒分布均匀、颗粒数量最多,块状的Ni粉团聚减少,其抗拉强度达到最大值215MPa,相比Ni/Al复合材料(抗拉强度176MPa),其抗拉强度提高了22%;当La₂O₃的添加量为7%时,复合材料中Al₃Ni增强颗粒含量减少,块状Ni粉团聚重新出现,抗拉强度下降至201MPa。     

激光立体成形和超声冲击混合制造Ti60合金的显微组织和性能（英文）

采用激光立体成形(LSF)和超声冲击处理(UIT)混合制造的方法，通过逐层强化表面，改善Ti60合金的结构和性能。采用SEM、TEM和XRD分析并比较UIT前后LSF处理Ti60样品的显微组织、力学性能和阻燃性能。结果表明，UIT后LSF处理Ti60合金的晶粒得到细化，冶金缺陷减少。同时，UIT后沉积层严重变形，并在表面形成纳米晶体。此外，沉积层表面显微硬度提高，残余应力由拉应力变为压应力。烧蚀坑面积减少了21%,Mo,Nb和Zr元素的比例增加。综上所述，LSF和UIT的混合制造可以改善LSF处理Ti60样品的显微组织和性能。     

谐波励磁无刷三相同步发电机的常见故障及处理方法

文章以SB-w系列谐波励磁无刷发电机配DTW5型自动电压调节器运行为例,叙述了谐波励磁无刷三相同步发电机的常见故障和处理方法。     

扫描方式对GH4169合金电子束熔丝增材修复组织与性能的影响

采用电子束熔丝增材工艺修复GH4169合金试样，研究扫描方式（包括扫描波形和扫描频率）对电子束熔丝增材修复GH4169合金试样组织与性能的影响。利用光学显微镜（OM）和扫描电子显微镜（SEM）观察修复试样的枝晶和Laves相形貌，并对室温拉伸性能进行分析。结果表明：不同扫描方式条件下的修复试样均成形良好，无气孔、未熔合等缺陷，修复区与母材之间为良好的冶金结合；无扫描、方形扫描、圆形扫描和S形扫描微观形貌均由外延生长的柱状晶组成；由于凝固速度和凝固方向的改变，Laves相尺寸变小，加入圆形扫描后Laves相由短链状和颗粒状转变为颗粒状分布，尺寸由11.39μm减小为4.34μm；半熔化区的宽度也由无扫描试样的45.46μm减小为圆形扫描方式的27.23μm。室温拉伸结果表明，与修复试样相比，母材试样的抗拉强度较低，但延伸率明显提高。加入扫描波形和扫描频率均能有效提高试样的力学性能，随着扫描频率增加，抗拉强度先是略有增加，然后急剧下降。在圆形扫描方式、 20 Hz条件下试样的抗拉强度最高，为932.42 MPa，较无扫描试样提高了87.51 MPa，延伸率达39.39%。