将复配的分散剂加入重油中制备得到重油纳米颗粒，采用氧弹热值对比法对所研制的纳米化重油进行实验室评价。研究结果表明，纳米化后的重油燃烧性能得到了改善，在掺水量为3％～12％时，重油的燃烧效率提高了2．5％～6．1％。通过TEM观察，纳米化后的重油呈水包油（O／W）型乳液结构，油水界面清晰，界面膜较厚，乳化油粒径约为20～50nm，油水分散均匀，并且分散后的重油粘度增幅小，掺水量在15％以内，粘度增幅不超过20％，并且随着掺水量的增加，乳化重油的粘度逐渐减少。另外，乳化重油稳定性好，室温下至少可保存6个月，在80℃下存放3天未发生破乳现象。     

Measurement System of Uniformity between Breech Horizontal Platform and Datum Tube Axis of Rocket Artillery

The purpose of this development is to detect the parallelism between the breech horizontal platform and the datum tube axis of the rocket artillery. The located aiming mechanism at the muzzle and located adjustment mechanism at the breech are designed in the system. Besides those, the system also uses an autocollimator with accuracy of 1″ and a collimating mirror together to determine the axis of the datum tube. An electronic level with accuracy of 2″ is employed to measure and display the value of the included angle and the parameter of the inclined direction. The entire accuracy of this system is σ≤± 9.1″. This paper describes the composition and the operating principle of the system and analyzes the accuracy. The development of this system supplies reliable measurement method for new rocket artilleries and artilleries, and this technology is of a good application prospect.     

非化学计量LaNi5型储氢合金的性能

采用富La混合稀土与Ni、Co、Mg等元素组合，获得了一种非化学计量LaNi5型储氢合金、用金相、XRD和SEM-EDX等方法分析了该合金的组织结构，研究了合金的气相储氢特性以及电化学性能，结果表明：在1.6MPa氢压和温度29℃下，该合金的储氢量达到1.58%（质量分数），该合金的放电容量为380mAh/g。经300次循环后容量保持率为55%，该合金的基体是CaCu5型结构的LaNi5相，但有第二相（LaMg)Ni3析出，这种第二相的形成是导致该合金大容量的关键。     

多媒体课件在开放实验室中的应用

介绍了制作多媒体课件的必要性，及所制作课件的特点。该课件与实验室管理系统配合起来，有利于实现实验室的全面开放。     

平纹织物复合材料的弹性模量预测

利用细观力学的代表体积元(RVE)法,预测了平纹织物复合材料的弹性模量。建立了表征RVE形态的数学模型,分析了细观结构与宏观性能之间的关系,编制了从组分材料的弹性性能推测复合材料的弹性性能的预测程序。对理论预测进行了实验验证,理论值与实测值在一定误差范围内能较好吻合,说明此预测方法具有一定的可靠性。     

In—situ Composite Based on Poly （ethylene terephthalate）,Polyamide and Polyethylene with Microfibres Formed through Extrusion and Hot Stretching

In-situ composites based on dispersed poly (ethylene terephthalate) (PET) or polyamide (PA),and continuous Polyethylene (PE) were prepared through a single screw extruder of Haake rheometer system with a rod-die relatively small in diameter.The extrudate was drawn at a drawing ratio of 3.1,and then quickly cooled in cold water.The specimens were obtained by injection molding at processing temperatures less than 190℃，far below the melting temperature of PET (265℃) and PA (230℃),which can maintain the solid state of PET and PA microfiber phase in the composites.Morphological observation with scanning electron microscopy (SEM) indicated that PET and PA can more or less form in-situ microfibers at compositions studied (0-20 wt pct PET or PA),and especially,PET and PA were almost deformed into fibers at the concentration of 15wt pct.Eensile strength and especially.PET and PA were almost deformed into fibers at the concentration of 15wt pct.Tensile strength and modulus of the blends reinforced by PET or PA microfibers showed to be increased from the tensile test results.The most noticeable improvement of the tensile properties occurred at 15wt pct of PET in PET/PE system,corresponding to the highest microfiber content,where the tensile strength reached 32.5 MPa,whereas only 19.5 MPa for the pure PE.     

一种升压式PFM DC-DC转换器的设计

讨论了一种PFM升压式DC－DC电压转称器的设计，重点对其关键的基准电压产生，振荡控制信号产生及比较器设计进行了分析，并采用3μmCOMOS工艺完成芯片的设计。     

一种高性能超宽带线性调频信号源

介绍一种VHF／UHF频段高性能超宽带线性调频信号源的设计与实现。首先简要阐述了高性能超宽带线性调频信号源的设计思想，然后依据基带数字产生结合倍频扩展带宽的思路提出了一种超宽带线性调频信号产生方案，并进行了设计实现研究。测试结果表明：按照本文阐述的指导思想和实现方案所设计的超宽带线性调频信号源达到 了相当高的性能。     

应用底饲回燃循环流化床技术改造东锅DG35/3.82-7型流化床锅炉

采用飞灰循环底饲回燃技术改造西南合成制药总厂热电分厂、天府矿务局磨心坡发电厂2台东方DG35/3.82-7型低倍率循环流化床锅炉。改造后运行结果表明,锅炉可长期、稳定运行,尾部飞灰可燃物含量大幅度降低,锅炉蒸发量提高20％左右,节煤效果明显。为燃用贫煤、无烟煤和煤矸石等劣质燃料且锅炉炉膛高度较低的电站技改,提供了一种切实可行的方法。     

活化铁矿粉技术及其效果评价

随勘探技术发展,高压超高压油气井日益增多,高密度、超高密度钻井液使用也越来越多.室内为配制密度大干2.4 g/cm3的超高密度钻井液,采用铁矿粉作为加重剂,并通过表面活化的原理对铁矿粉进行表面处理,以提高钻井液的固相容纳能力.该活化工艺借鉴了国内外相关产品的技术特点,以优选的表面活性剂为主要活化材料,并添加了无机盐和硅酸盐作为助吸附材料,提高了活化效果.室内实验表明,用活化铁矿粉加重的钻井液体系能保持良好的流变性和悬浮能力,能保证钻进时的正常循环,并且摩阻系数也低于常规铁矿粉加重钻井液.