2,6-二乙酰基吡啶合成方法的改进

优化了2，6—二乙酰基吡啶的合成工艺。以2，6—吡啶二羧酸为原料，经过醇化及克莱森酯缩合反应，合成了2，6—二乙酰基吡啶，2，6—吡啶二羧酸二乙醇和2，6—二乙酰基吡啶的分离收率分别为94．1％和88．9％，2，6—二乙酰基毗啶的质量分数大于99％。     

氯化聚丙烯改性胶粘剂的合成及粘附性能研究

以甲苯为溶剂，过氧化二苯甲酰(BP0)为引发剂，通过自由基聚合，采用甲基丙烯酸羟乙酯(HEMA)和苯乙烯(St)接枝改性氯化聚丙烯(CPP)。研究了不同苯乙烯用量、不同反应温度、不同反应时间、不同引发剂用量对改性氯化聚丙烯胶粘剂粘附性能的影响，得出较佳的工艺条件为反应温度90℃，反应时问2h，原料配比m(CPP)：m(HEMA)：m(St)：m(BPO)=50：0．5：0．6：0．15。     

Low-Temperature Aging of t-ZrO2 Polycrystals with 3 mol% Y2O3

A kinetic study of the aging behavior of tetragonal zirconia polycrystals (TZPs) from 100° to 500°C suggests that there exists a cricital grain size of 0.52 μm below which the tetragonal symmetry can be retained. Property degradation of TZPs at low temperatures is connected with transformation-induced microcracking. It is reported here that the temperature range of 100° to 400°C in which degradation occurs could be explained by an infinite incubation time for the lower limit and by the martensite starting temperature for the upper limit.     

合成氢化松香乙酯的新工艺研究

以DRC为催化剂,在无溶剂条件下,通过氢化松香与乙醇的直接酯化反应合成氢化松香乙酯。探索了反应温度、催化剂用量、反应时间、物料配比等因素对反应酯化率的影响,确定最佳反应条件为:反应温度180℃,催化剂用量为原料氢化松香质量的6%,反应时间6h,醇与酸的摩尔比为3∶1。在最佳条件下酯化率达92.2%。还探讨了用阴离子交换树脂柱层析分离纯化氢化松香乙酯粗产物的方法。此外,利用红外光谱对氢化松香乙酯精制产物进行了表征;用GC-MS分别对氢化松香乙酯粗产物及其精制产物进行了定性和定量分析,比较了柱层析前后化学组成的变化。     

扎实推进规划工作 培植绿色发展理念——湖北省中小河流水能资源开发规划工作情况介绍

本文介绍了湖北省中小河流水能资源开发规划工作进展,规划工作在树立绿色发展理念、摸清水能资源开发状况等方面取得的成效,以及湖北省为推动规划工作采取的主要做法。     

Cu2O/Cu Cermet as a Candidate Inert Anode for Al Production

Cu₂O/ x Cu ( x =0–25 wt%) cermets were evaluated as a novel partially inert anode for aluminum (Al) production. The physical and mechanical properties, including the compressive strength, flexural strength, thermal expansion coefficient, thermal conductivity, and dc electrical conductivity were tested at room temperature and at temperatures up to 950°C. The coefficient of thermal expansion, compressive strength, flexural strength, thermal conductivity, and electrical conductivity of Cu₂O/Cu cermets increased with increasing Cu content. High-temperature electrical conductivity measurements showed that with increasing temperature, the electrical conductivity increased when the Cu content was below the percolation threshold, while it decreased when the Cu content was above the percolation threshold. A relatively stable CuAlO₂ layer formed on the cermet surface during electrochemical testing, and the corrosion rate of this anode was estimated to be about 1.8–1.9 cm/year in Al production.     

2,6-萘二甲酸二甲酯与一些二甲基萘所形成的激基复合物

2,6-萘二甲酸二甲酯与一些二甲基萘可以形成激基复合物。本文通过稳态和动态荧光光谱研究了这类激基复合物的形成与分子结构的关系。结果表明,尽管这些二甲基萘的电离能基本相同,但因取代基位置不同使分子中电荷分布不同,从而影响了激基复合物的形成能力。     

石油钻采机械用橡胶气囊的研制

橡胶气囊是石油钻采设备上常用的一种刹车装置。介绍了橡胶气囊的模具设计、铜气嘴的处理、排气槽的加工布置等整个研制过程。经试验，生产制作的橡胶气囊完全达到设计要求。     

纳米碳酸钙的表面活化改性研究

本文主要介绍通过加入特定的表面改性剂,制得了表面改性的活性碳酸钙.并对活化过程中的一系列影响因素,如活化温度、活化时间、碳酸钙悬浊液浓度、表面改性剂用量进行了研究.     

氟硅唑微乳剂的研制

对国内外文献未见报道的8％氟硅唑微乳剂制剂进行了研制，测定了其冷贮和热贮稳定性等理化性状及生物活性。对黄瓜自粉病室内毒力测定和田间药效试验结果表明，药效与40％乳油相当，对黄瓜安全。