FATIGUE DAMAGE IN 1045 STEEL UNDER VARIABLE AMPLITUDE BIAXIAL LOADING

Abstract— During constant amplitude loading, two different types of crack systems have been reported In the high cycle fatigue (HCF) region, cracks nucleate on a small number of maxium shear strain amplitude planes One of these cracks becomes a dominant crack and leads to failure of the specimen In the low cycle fatigue (LCF) region, equally developed microcracks are observed over the entire gage section and grow during the majority of the life. The failure is due to a linking in which the microcracks join up during the last few cycles of the fatigue life.
To investigate the interaction of these two types of crack systems in biaxial fatigue, experiments were performed on thin-wall tubular specimens in tension, torsion and combined tension-torsion loading The test program included step loading and block loading in which two equivalent strain amplitudes were employed. One of the equivalent strain amplitudes is in the HCF region and the other was in the LCF region
Fatigue lives were predicted from constant amplitude damage curves when a single crack system dominated the fatigue process Two competitive crack systems were sometimes developed on the maximum shear strain amplitude planes in a single specimen under block loading This resulted in a conservative prediction of the fatigue life.     

High-resolution electron microscopy of the twinning and intergrowth in Ca4Al6SO16 and Ca3SrAl6SO16

The microstructures of unhydrated calcium aluminosulphate Ca₄Al₆SO₁₆ and Ca₃SrAl₆SO₁₆ have been studied by high-resolution electron microscopy (HREM). The results showed that twinning and twinned slabs could be introduced taking the [1 1 2] direction as the twin axis so that it seems to be coincident with the law of twinning formed in body-centred cubic structures. A previously reported superlattice with a repeat period twice that of the fundamental structure along the 〈1 1 0〉 direction has also been found in both matrix and twin variants. The close intergrowth of Ca₃SrAl₆SO₁₆ and another phase, possibly Sr₃Al₂O₆ existing as an inclusion between these two twin variants, was determined and clearly revealed by electron diffraction and HREM images. The coherent interphase boundaries and orientation relationship between them can also be deduced.     

Determination of molecular weight distributions of tert-octylphenol ethoxylate surfactant polymers by laser desorption Fourier transform ion cyclotron resonance mass spectrometry and high-performance liquid chromatography

Triton polymers are commercial surfactants whose molecular weight distributions are conventionally determined by means of high-performance liquid chromatography (HPLC). However, in the case of the important octylphenol ethoxylates [p-C8H17-C6H4-O-(CH2CH2O)n-H], HPLC cannot resolve individual oligomers of high molecular weight Triton surfactants (e.g., greater than 2000 u or so; u = unified atomic mass unit). In this paper, we show that laser desorption Fourier transform ion cyclotron resonance mass spectrometry (LD/FT/ICR/MS) provides a simple and accurate measure of such Triton surfactant molecular weight distributions up to at least 3500 u, based on a single-shot laser pulse measurement of a few seconds duration. Comparison of LD/FT/ICR/MS and HPLC molecular weight distributions of low molecular weight surfactants shows that laser desorption/ionization produces minimal fragmentation and thus offers an accurate measure of the relative abundances of the neutral oligomers, without the need for prior chromatographic separation of the components. Moreover, for all Triton polymer molecular weight distributions (700-3000 u), LD/FT/ICR/MS provides much more highly resolved profiles of oligomer relative abundances. Finally, LD/FT/ICR/MS reveals the presence of poly(ethylene oxide) side products of the polymerization process, which are not observed by HPLC with conventional ultraviolet absorption detection.     

Uncooled DBR laser directly Modulated at 3.125 gb/s as athermal transmitter for low-cost WDM systems

An uncooled three-section tunable distributed Bragg reflector laser is demonstrated as an athermal transmitter for low-cost uncooled wavelength-division-multiplexing (WDM) systems with tight channel spacing. A /spl plusmn/0.02-nm thermal wavelength drift is achieved under continuous-wave operation up to 70/spl deg/C. Dynamic sidemode suppression ratio of greater than 35 dB is consistently obtained under 3.125-Gb/s direct modulation over a 20/spl deg/C-70/spl deg/C temperature range, with wavelength variation of as low as /spl plusmn/0.2 nm. This indicates that more than an order of magnitude reduction in coarse WDM channel spacing is possible using this source.     

Widely tunable bottom-emitting vertical-cavity SOAs

We present bottom-emitting tunable vertical-cavity semiconductor optical amplifiers (VCSOAs) with an effective wavelength tuning range of >20 nm. These devices utilize a high reflectivity micromechanically tunable Bragg mirror as the back reflector. Compared with our first generation tunable VCSOAs, the bottom-emitting devices exhibit a two-fold increase in the effective tuning range as well as a five-fold reduction in the required tuning voltage.     

VLSI Implementation of Forward Error Control Technique for ATM Networks

In asynchronous transfer mode (ATM) networks, fixed length cells of 53 bytes are transmitted. A cell may be discarded during transmission due to buffer overflow or a detection of errors. Cell discarding seriously degrades transmission quality. The quality degradation can be reduced by employing efficient forward error control (FEC) to recover discarded cells. In this paper, we present the design and implementation of decoding equipment for FEC in ATM networks based on a single parity check (SPC) product code using very‐large‐scale integration (VLSI) technology. FEC allows the destination to reconstruct missing data cells by using redundant parity cells that the source adds to each block of data cells. The functionality of the design has been tested using the Model Sim 5.7cXE Simulation Package. The design has been implemented for a 5 ° 5 matrix of data cells in a Virtex‐E XCV 3200E FG1156 device. The simulation and synthesis results show that the decoding function can be completed in 81 clock cycles with an optimum clock of 56.8 MHz. A test bench was written to study the performance of the decoder, and the results are presented.     

Trellis and convolutional precoding for transmitter-based interference presubtraction

This paper studies the combination of practical trellis and convolution codes with Tomlinson-Harashima precoding (THP) for the presubtraction of multiuser interference that is known at the transmitter but not known at the receiver. It is well known that a straightforward application of THP suffers power, modulo, and shaping losses. This paper proposes generalizations of THP that recover some of these losses. At a high signal-to-noise ratio (SNR), the precoding loss is dominated by the shaping loss, which is about 1.53 dB. To recover shaping loss, a trellis-shaping technique is developed that takes into account the knowledge of a noncausal interfering sequence, rather than just the instantaneous interference. At rates of 2 and 3 bits per transmission, trellis shaping is shown to be able to recover almost all of the 1.53-dB shaping loss. At a low SNR, the precoding loss is dominated by power and modulo losses, which can be as large as 3-4 dB. To recover these losses, a technique that incorporates partial interference presubtraction (PIP) within convolutional decoding is developed. At rates of 0.5 and 0.25 bits per transmission, PIP is able to recover 1-1.5 dB of the power loss. For intermediate SNR channels, a combination of the two schemes is shown to recover both power and shaping losses.     

Contextualizing is not nullifying: Reply to Mills (2005).

In omitting crucial words and sentencees, neglecting relevant citations, and overlooking important distinctions, Jon Mills' (see record 2005-04819-001) critique of relational psychoanalysis significantly misrepresents the authors' viewpoint. This viewpoint seeks to contextualize, but not to nullify, individual worlds of experience and their limiting horizons. (PsycINFO Database Record (c) 2010 APA, all rights reserved)     

Revamping of the process condensate treatment unit. G-43-107M/1 unit at LiNOS Ltd

Increasing attention at oil refineries is being focused on solving environmental problems caused by stiffening of the requirements for emissions of harmful substances into air and water. Advanced technologies that reduce the effect of industrial enterprises on the environment to the minimum are becoming increasingly in demand. Treatment of process wastewaters to remove hydrogen sulfide and ammonia is one such problem of the modern refinery with cat crackers. __________ Translated from Khimiya i Tekhnologiya Topliv i Masel, No. 3, pp. 52–55, May–June, 2006.     

A Distributed State Estimator Utilizing Synchronized Phasor Measurements

With the creation of balancing authorities by the North American Reliability Council that span large portions of the North American interconnection, and stringent requirements for real time monitoring of power system evolution, faster and more accurate state estimation algorithms that can efficiently handle systems of very large sizes are needed in the present environment. This paper presents a distributed state estimation algorithm suitable for large-scale power systems. Synchronized phasor measurements are applied to aggregate the voltage phase angles of each decomposed subsystem in the distributed state estimation solution. The aggregated state estimation solution is obtained from the distributed solution using a sensitivity analysis based update at chosen boundary buses. Placement of synchronized phasor measurements in the decomposed subsystems is also investigated in this paper. Test results on the IEEE 118-bus test bed are provided