Effect of ZnO layer thickness upon optoelectrical properties of NiO/ ZnO heterojunction prepared at room temperature

In this work, p-NiO/n-ZnO heterostructures were successfully prepared at room temperature using RF sputtering technique. The influence of ZnO layer thickness on the performance of the heterojunction was investigated. The deposited ZnO layers have a hexagonal Wurtzite structure with preferable growth orientations along (002) and (103) for thinner films. Increasing the thickness results in more crystallographic orientation randomness. The current–voltage measurements of the realized heterojunctions showed a clear rectifying behavior. The measured ideality factor varies from 2.5 to 1.6 according to the thickness of ZnO layer. The series resistance of the device is enlarged with increasing ZnO thickness. The deduced parameters from the I–V characteristics suggest that 200 nm is the optimal thickness of the ZnO layer according to our experimental conditions. We attribute the relatively better performance of this thickness to achieving reasonable compensation between serial resistance and ideality factor. The best heterojunction was tested and successfully used as a UV detector.     

Cross-Layer Optimization of Dynamic Packet Assignment for Video Transmission Over IEEE 802.11e Networks

Video transmission over IEEE 802.11e wireless networks still shows poor performance for large bandwidth demand and frequently changed environments. Thus, several enhancements of IEEE 802.11e were proposed. On the other hand, big frames and simultaneous sending of adjacent frames always cause packet dropping for buffer overflow. In the past, we proposed an IEEE 802.11e enhancement named DFAA and a content aware mechanism to solve the above problems. The motivation of this paper is to find a proper way to integrate these two mechanisms. A DFAA enhancement (DFAA-E) is proposed to make up the insufficiency of content aware mechanism. Experiments results show that the combination of DFAA-E and content aware mechanism improves the video decoded quality greatly. And its performance can be further enhanced by selecting the suitable settings of certain parameters.     

Reoptimization framework and policy analysis for maritime inventory routing under uncertainty

We study a maritime inventory routing problem, in which shipments between production and consumption nodes are carried out by a fleet of vessels. The vessels have specific capacities and can be chartered under different agreements. The inventory levels of all consumption nodes and some production nodes should be maintained within specified bounds; for the remaining production nodes, orders should be picked up within pre-defined time windows. We propose a discrete-time mixed-integer programming model. In the face of new information and uncertainty, this optimization model has to be re-solved, as the horizon is rolled forward. We discuss how to account for different sources of uncertainty. We present a rolling-horizon reoptimization framework that allows us to study different policies that impact the quality of the implemented solution, so we can identify the optimal set of policies.     

Popular biorthogonal wavelet filters via a lifting scheme and its application in image compression

A technique using a lifting scheme is presented for constructing compactly supported wavelets whose coefficients are composed of free variables locating in an interval. An efficient approach-based wavelet for image compression is developed by selecting the coefficients of the 9-7 wavelet filter and associated lifting scheme. Furthermore, the rationalised coefficients wavelet filter that can be implemented with simple integer arithmetic is achieved and its characteristic is close to the well known original irrational coefficients 9-7 wavelet filters developed by A. Cohen et al. (Commun. Pure Appl. Maths., vol.45, no.1, p.485-560, 1992). To reduce the computational cost of image coding applications further, an acceleration technique is proposed for the lifting steps. Software and hardware simulations show that the new method has very low complexity, and simultaneously preserves the high quality of the compressed image.     

Cover Picture: Arresting,Fixing, and Separating Dimers Composed of Uniform Silica Colloidal Spheres (Adv. Funct. Mater. 12/2006)

In colloidal suspensions of silica, particles undergo constant collisions. By controlling various parameters, the repulsive barrier can be reduced, thereby substantially increasing the number of collision‐induced dimerization events. Xia and co‐workers report on p. 1627 that the dimers could be arrested and then permanently fixed by introducing a small amount of fresh tetraethylorthosilicate into the colloidal suspension, with monodisperse dimer yields of up to 50 %. This yield could be increased to 80 % by centrifugation in a density gradient medium. When fresh tetraethylorthosilicate is introduced into a colloidal suspension of silica spheres, it hydrolyzes and condenses in situ to arrest and fix the dimers resulting from constant collisions between the spheres. By optimizing the experimental parameters (including the length of aging time) and the diameter of the silica spheres, as well as the concentrations of counterions, water, and ammonia, it is possible to routinely produce monodisperse dimers with a yield as high as 50 %. When combined with centrifugation using a density gradient medium, the yield of such dimers could be further increased to 80 %. It is believed that this method will provide a simple and versatile approach to the high‐volume production of dimers from spherical colloids composed of different materials. These dimers may find widespread use in a range of applications such as fabrication of photonic crystals and fundamental studies related to colloidal science.     

Synthesis and characterization of biocompatible hydroxyapatite coated ferrite

Ferrite particles coated with biocompatible phases can be used for hyperthermia treatment of cancer. We have synthesized substituted calcium hexaferrite, which is not stable on its own but is stabilized with small substitution of La. Hexaferrite of chemical composition (CaO)_0.75(La₂0₃)_0.20(Fe₂O₃)₆ was prepared using citrate gel method. Hydroxyapatite was prepared by precipitating it from aqueous solution of Ca(NO₃)₂ and (NH₄)₂HPO₄ maintaining pH above 11. Four different methods were used for coating of hydroxyapatite on ferrite particles. SEM with EDX and X-ray diffraction analysis shows clear evidence of coating of hydroxyapatite on ferrite particles. These coated ferrite particles exhibited coercive field up to 2 kOe, which could be made useful for hysteresis heating in hyperthermia. Studies by culturing BHK-21 cells and WBC over the samples show evidence of biocompatibility. SEM micrographs and cell counts give clear indication of cell growth on the surface of the sample. Finally coated ferrite particle was implanted in Kasaulli mouse to test its biocompatibility. The magnetic properties and biocompatibility studies show that these hydroxyapatite coated ferrites could be useful for hyperthermia.     

Electrochemical synthesis and characterization of chloride doped polyaniline

Chloride doped polyaniline conducting polymer films have been prepared in a protic acid medium (HCl) by potentiodynamic method in an electrochemical cell and studied by cyclic voltammetry and FTIR techniques. The FTIR spectra confirmed Cl^- ion doping in the polymers. The polymerization rate was found to increase with increasing concentration of aniline monomer. But the films obtained at high monomer concentration were rough having a nonuniform flaky polyaniline distribution. Results showed that the polymerization rate did not increase beyond a critical HCl concentration. Cyclic voltammetry suggested that, the oxidation-reduction current increased with an increase in scan rate and that the undoped polyaniline films were not hygroscopic whereas chloride doped polyaniline films were found to be highly hygroscopic.     

Pack cementation process for the formation of refractory metal modified aluminide coatings on nickel-base superalloys

The vapour phase compositions of a series of pack powder mixtures containing elemental Al and Hf or W powders as depositing sources and CrCl₃·6H₂O or AlF₃or CrF₃as activators were analysed in an attempt to further develop the pack cementation process to codeposit Al and Hf or W to form diffusion coatings on nickel base superalloys. The results suggested that Al could be codeposited with Hf, but not with W, from the vapour phase. Compared with both AlF₃and CrF₃, CrCl₃·6H₂O has been shown to be a more suitable activator for codepositing Al with Hf. The optimum coating temperature was identified to be in the range of 1050°C to 1150°C. Based on the thermochemical analysis, a series of coating deposition studies were undertaken, which confirmed that codeposition of Al and Hf could be achieved at a deposition temperature of 1100°C in the CrCl₃·6H₂O activated packs containing elemental Al and Hf powders. The coating obtained had a multilayer structure consisting of a Ni₇Hf₆Al₁₆top layer and a NiAl layer underneath, followed by a diffusion zone, which revealed that the coating was formed by the outward Ni diffusion. It is suggested that the compositions suitable for codeposition of Al and Hf could be effectively identified by comparing the vapour pressures of HfCl₄and HfCl₃with that of AlCl in the packs activated by chloride salts. It has also been experimentally demonstrated that, although W could not be deposited from the vapour phase, a high volume of fine W particles can be entrapped into the outer NiAl coating layer formed by the outward Ni diffusion using a modified pack configuration. This leads to the formation of a composite coating layer with W particles evenly distributed in a matrix of NiAl. It is suggested that this modified pack process could be similarly applied to develop nickel aluminide coatings containing other refractory metals that may not be codeposited with Al from the vapour phase.     

Analysis of the Scattering Characteristic of Several Waveguide Components Using Boundary Element Method

Several kinds of waveguide components such as curved waveguide bends, arbitrary angle waveguide bends and T-junctions have been analyzed with boundary element method in this paper. A new discretization method for the boundary element method to solve the waveguide discontinuities has been given. The numerical results obtained agree well with the experimental results and numerical results in other literature. Especially, the scattering characteristics of Forded E-, H-plane T-junctions in 3mm band have been analyzed using boundary element method and the calculation results are presented.