Strain-induced corrosion cracking of low-alloy steels in LWR systems — case histories and identification of conditions leading to susceptibility

The term “strain-induced corrosion cracking” (SICC) is introduced to describe crack formation involving dynamic straining, but in the absence of obvious, cyclic loading. Its origins in slow-strain-rate testing and in corrosion failures in boiler systems are described and the links with “classical” stress corrosion cracking and low-cycle corrosion fatigue are identified. Four areas, in which SICC of low-alloy steels in LWR systems has occurred, are described in detail and the typical features are used, together with literature data from laboratory testing, to identify conditions leading to susceptibility. Indications are given of remedial measures and of areas in which further work is necessary.     

Consolidation of Long-Term Memory: Evidence and Alternatives.

Memory loss in retrograde amnesia has long been held to be larger for recent periods than for remote periods, a pattern usually referred to as the Ribot gradient. One explanation for this gradient is consolidation of long-term memories. Several computational models of such a process have shown how consolidation can explain characteristics of amnesia, but they have not elucidated how consolidation must be envisaged. Here findings are reviewed that shed light on how consolidation may be implemented in the brain. Moreover, consolidation is contrasted with alternative theories of the Ribot gradient. Consolidation theory, multiple trace theory, and semantization can all handle some findings well but not others. Conclusive evidence for or against consolidation thus remains to be found. (PsycINFO Database Record (c) 2010 APA, all rights reserved)     

The role of interparticle forces in colloidal aggregates: local investigations and modelling of restructuring during filtration.

Industrial solid-liquid separation processes, such as pressure filtration or membrane processes, involve the application of pressure to suspensions. In response, some water is extracted, the suspension volume is reduced, and the dispersed aggregates start to form a network. In recent works, we aimed to make a prediction for the response of aggregates to stress which occurs during a filtration. We chose model systems made of aggregated silica nanoparticles. Some of these systems offer a strong resistance to applied stresses, and retain their permeability; others yield and collapse. We used small angle neutron scattering by which we can locally quantify the particle distribution withi the network to determine the processes by which particles reorganise during collapse: we found that reordering processes at the scale of 1 to 10 particle diameters control the course of collapse and the loss of permeability. Finally we constructed a numerical model for describing the processes by which colloidal aggregates are compressed. This model predicts that the response of such networks to pressure follows some scaling laws, which depend only on the elastic vs. dissipative nature of interparticle bonds.     

Microstructural development and mechanical properties of interrupted aged Al-Mg-Si-Cu alloy

The effects of a recently developed interrupted aging procedure on the microstructural development and mechanical properties of the commercial Al-Mg-Si-Cu alloy 6061 have been studied using transmission electron microscopy (TEM), differential scanning calorimetry (DSC), and mechanical testing. This so-called T6I6 temper involves partially aging the alloy at a typical T6 temperature (the underaging stage), quenching, then holding at a reduced temperature (in this case 65 °C) to facilitate further hardening (the secondary aging stage), prior to final aging to peak properties at, or close to, the initial aging (T6) temperature (the reaging stage). The T6I6 aging treatment produces simultaneous increases in tensile properties, hardness, and toughness, as compared with conventional T6. The overall improvement in the mechanical properties of 6061 T6I6 is associated with the formation of a greater number of finer, and more densely dispersed, β″ precipitates in the final microstructure. Secondary precipitation took place during the interrupted aging stage of the T6I6 temper, resulting in the formation of a large number of Guinier-Preston (GP) zones that served as precursors to the needlelike β″ precipitates when elevated temperature aging was resumed.     

Photoreactivation of Escherichia coli following medium-pressure ultraviolet disinfection and its control using chloramination.

Ultraviolet (UV) disinfection is becoming increasingly popular as an alternative disinfection technology to chlorination in recent years. In this study, we investigated the photoreactivation of Escherichia coli following medium-pressure (MP) UV disinfection of synthetic water by a bench-scale collimated beam apparatus. The UV doses ranged from 1.6 -19.7 mWs/cm2 and photoreactivation was investigated for 6 hours under fluorescent light. In addition, chloramination was applied after UV disinfection to investigate its ability to control photoreactivation. It was found that photoreactivation occurred for all UV doses tested and the increase in bacteria numbers ranged from 0.04 to 1.35 log10. However, the degree of photoreactivation decreased with increased UV doses. Chloramination experiments revealed that the addition of 0.5 mg/l of monochloramine resulted in suppression of photoreactivation for 1 hour only. An increased monochloramine dose of 1 mg/l was found to prevent photoreactivation for the entire duration of the experiment. The results of this study have shown that photoreactivation occurs even after MP UV disinfection, although it is of a lesser extent at higher UV doses. This study has also established that secondary chloramination can effectively suppress and eliminate photoreactivation with a chloramine dose of 1 mg/l.     

Reliability of structures in high dimensions, part I: algorithms and applications

The present paper is concerned with the estimation of structural reliability when a large number of random variables is present. A sampling technique which uses lines in order to probe the failure domain, is presented. The latter is employed in conjunction with a stepwise procedure which makes use of Markov Chains. The resulting algorithm exhibits accelerated convergence.     

Successful Aging

This issue's Works in Progress department presents six abstracts for projects that are developing interesting solutions to the elderly's quality of life challenges. The first two abstracts discuss projects that will help provide the elderly with freedom and independence by instrumenting their environments with supportive technology. The next two abstracts discuss projects building specialized user interfaces for addressing some of the challenges associated with aging, such as vision impairment. The final two abstracts present projects that will aid independence for the elderly by providing remote monitoring and assistance.     

Drying of Uncoated Paper with Gas-Fired Infrared Emitters—Optimum Emitters' Location Within a Paper Machine Drying Section

This article theoretically investigates the drying of uncoated paper with gas-fired infrared (IR) emitters installed within the drying section of a given commercial paper machine. Specifically, it presents the ideal location of two opposing IR emitters within the drying section. The ideal location of the two opposing IR emitters corresponds to the highest machine speed with specified average moisture content of paper sheet at the end of the drying section. This article also presents the average evaporation rate, temperature, and moisture content of the paper sheet as it travels through the drying section with the two opposing IR emitters operating at the optimum location. In addition, the temperature and moisture profiles in the sheet thickness direction, before and after the IR emitters, are provided. This article is not concerned with the potential effects of drying with IR emitters on paper sheet properties and machine runnability issues.     

Hydrogen limitation--a method for controlling the performance of membrane biofilm reactor for autotrophic denitrification of wastewater.

Hydrogen-driven denitrification using the fiber membrane biofilm reactor (MBfR) was evaluated for consistent operation in tertiary wastewater treatment. The possibility of controlling the process rates, as well as biofilm parameters by supplying limited amounts of electron donor (hydrogen), was tested. Limiting the hydrogen supply proved to be efficient in controlling the biofilm growth and performance of the MBfR. Denitrification rates remained unchanged for both synthetic wastewater (SWW) and real municipal wastewater (MWW) effluent as well through the fluctuations in the substrate (NO3-N) concentration. The average denitrification rates were 0.50 (+/- 0.02) g NO3-N per day per m2 for SWW and 0.59 (+/- 0.04) g NO3-N per day per m2 for MWW. Biofilm density rather than thickness was the determining factor in substrate diffusion and biofilm sloughing, ultimately determining operating stability. Limited hydrogen supply assured constant volatile solids (VS) concentration in the biofilm. It was determined that VS/TS ratio higher than 0.25 assured stable biofilm operation. Decrease of VS/TS ratio below 0.25 led to shearing of the nonbiological outer layers of the biofilm. The values of chemical oxygen demand (COD), volatile suspended solids (VSS) and total suspended solids (TSS) in the final effluent were stable and well below wastewater effluent guidelines. Substitutions of bicarbonate with gaseous carbon dioxide as the carbon source did not affect denitrification rates despite lower than optimum pH conditions.     

Enhance Cyanide Recovery by UsingAir‐Sparged Hydrocyclone

Human health and environmental concerns dictate that industrial processes be improved or replaced. Recovery or recycling is an important activity that allows cyanide residue from the industrial processes to be re‐used, reducing its production cost and disposal problems. In this regard, the air‐sparged hydrocyclone (ASH) has been used as a reactor for the treatment of cyanide solutions for cyanide recycling by acidification/volatilization using the Mexican modification of the Mills‐Crowe process. Aqueous cyanide‐ion concentration can be reduced from 250 ppm to below 20 ppm in the ASH with recoveries greater than 80 % in a single stage.