Nano fibrillated cellulose-based foam by Pickering emulsion: Preparation,characterizations, and application as dye adsorbent

An ecofriendly and biodegradable porous structure was prepared from drying aqueous foams based on nano fibrillated cellulose (NFC), extracted from softwood pulp by subcritical water/CO₂ treatment (SC-NFC). The primary aim of this work was to use the modified SC-NFC as stabilizer for a water-based Pickering emulsion which upon drying, yielded porous cellulosic materials, a good dye adsorbent. In order to exploit the carboxymethylated SC-NFC (CMSC-NFC, with a degree of substitution of 0.35 and a charge density of 649 μeqv/g) as a stabilizer for water-based Pickering emulsion in subsequent step, an optimized quantity of octyl amine (30 mg/g of SC-NFC) was added to make them partially hydrophobic. A series of dry foam structures were prepared by varying the concentrations of treated CMSC-NFCs and 4 wt% was found to be the optimum concentration to yield foam with high porosity (99%) and low density (0.038 g/cc) along with high compression strength (0.24 MPa), superior to the conventionally extracted NFC. The foams were applied to capture as high as 98% of methylene blue dyes, making them a potential green candidate for treating industrial effluent. In addition, the dye adsorption kinetics and isotherms were found to be well suited with second order kinetics and Langmuir isotherm models.     

Protective effect of the fruits of Terminalia arjuna against cadmium-induced oxidant stress and hepatic cell injury via MAPK activation and mitochondria dependent pathway

Cadmium (Cd), a highly toxic environmental pollutant, induces hepatic disorders. The present study has been undertaken to investigate the protective role of the fruit extract of Terminalia arjuna (AE) against Cd-induced oxidative liver impairment using a murine model. Cadmium reduced hepatocytes viability, activated MAPKs, disturbed Bcl-2 family protein balance, increased reactive oxygen species (ROS) production and induced apoptotic cell death by mitochondria dependent caspases-3 activation. AE treatment, however, suppressed all the apoptotic actions of cadmium. Similarly, mice treated with cadmium altered a number biomarkers related to hepatic oxidative stress and other apoptotic indices. Oral administration of AE both pre and post prevented all the Cd-induced hepatic damages.     

Direct Amide Synthesis from Alcohols and Amines by Phosphine‐Free Ruthenium Catalyst Systems

Amides are synthesized directly from alcohols and amines in high yields using an in situ generated catalyst from easily available ruthenium complexes such as the (p‐cymene)ruthenium dichloride dimer, [Ru(p‐cymeme)Cl₂]₂, or the (benzene)ruthenium dichloride dimer, [Ru(benzene)Cl₂]₂, an N‐heterocyclic carbene (NHC) ligand, and a nitrogen containing L‐type ligand such as acetonitrile. The phosphine‐free catalyst systems showed improved or comparable activity compared to previous phosphine‐based catalytic systems. The in situ generated catalyst from [Ru(benzene)Cl₂]₂, an NHC ligand, and acetonitrile showed excellent activity toward reactions with cyclic secondary amines such as piperidine and morpholine.     

Coalescence of bubbles and stability of foams in aqueous solutions of Tween surfactants

Coalescence of air bubbles and stability of foams in aqueous solutions of Tween 20, 40, 60 and 80 are reported in this work. Adsorption of the surfactants at air–water interface was studied by measuring the surface tension of the surfactant solutions. The surface tension profiles were fitted using a surface equation of state derived from the Gibbs and Langmuir adsorption equations. The critical micelle concentration and surface tension at this concentration were determined. The effect of surfactant concentration on coalescence of air bubbles at flat air–water interface was studied. The role of steric force on coalescence time was investigated. The coalescence time distributions were fitted by the stochastic model. The mean values of the distributions were compared with the predictions of seven film-drainage models. Stability of foams was analyzed by the Ross–Miles test. The initial and residual foam heights were measured at different surfactant concentrations. The stability of foams was compared with the coalescence time of the bubbles.     

Enhanced near band edge luminescence of Ti/ZnO nanorod heterostructures due to the surface diffusion of Ti

Information on the mechanistic differences in the luminescence properties of Ti/ZnO nanorods (NRs) has been obtained through the preparation of heterostructures by (a) varying the thickness of Ti from 1 nm to 20 nm keeping the substrate temperature at 400 °C, (b) varying the substrate temperature from room temperature (RT) to 500 °C while keeping the metal thickness constant at 10 nm and (c) annealing the RT Ti sputtered NRs at temperatures of 400 °C and 500 °C. The photoluminescence (PL) spectra show that the near band edge luminescence of ZnO in the ultraviolet (UV) region is enhanced as the thickness of Ti increases up to 5 nm and, thereafter, it falls. Sputtering of Ti on ZnO NRs at RT does not cause any UV enhancement but when sputtered at and above 400 °C, the UV intensity is enhanced. Annealing of RT Ti sputtered NRs at and above 400 °C also results in the enhancement of the UV peak, although with a lesser magnitude. Analysis of the PL results, supported by X-ray diffraction, field emission scanning electron microscopy, elemental mapping, high resolution transmission electron microscopy, Fourier transform infrared spectroscopy and electrical I-V measurement results, show a clear indication that the surface diffusion of Ti causes a reduction in the surface defects.     

Influence of grain boundary sliding on diffusion in yttria doped zirconia

Grain boundary sliding during high temperature deformation can lead to stress concentrations and an enhancement of diffusion in mobile boundaries. Experiments were conducted on a fine grained 3 mol% yttria stabilized tetragonal zirconia, under conditions associated with superplastic flow involving grain boundary sliding. Tracer diffusion studies under creep conditions and without load indicate that there is no enhancement in either the lattice or grain boundary diffusivities. The experimental creep data are consistent with an interface controlled diffusion creep mechanism.     

Frequency dependent stiffness and damping coefficients of orifice compensated multi-recess hydrostatic journal bearings

Frequency dependent stiffness and damping characteristics of an orifice compensated multi-recess hydrostatic journal bearing has been presented incorporating recess volume fluid compressibility effects into it. The theory is based on linearising the Reynolds' equation for finite bearings and the recess flow continuity equation using first order perturbations. A new dimensionless recess volume fluid compressibility parameter (γ) has been introduced. Results for stiffness and damping characteristics have been presented for various frequency of vibration or squeeze parameters (σ) and recess volume parameters (γ) in addition to the usual bearing design parameters.     

Environmental tobacco smoke removal capability of activated carbon

Removal of gaseous and vapor constituents of environmental tobacco smoke (ETS) by activated carbons in a packed bed arrangement was studied under dynamic conditions and was compared with that by silica gel and molecular sieve 13X. ETS is a mixture of sidestream smoke and exhaled mainstream smoke, and it consists of various organic and inorganic compounds, trace heavy metals, and particulate matters. Due to the complex nature of ETS-air mixture, its removal from indoors is a challenging task. For experimentation in a laboratory, the ETS was produced from a specially designed smoking apparatus that simulated the puffng of a cigarette by a person. Air containing ETS was passed through a bed containing about 25 grams of activated carbon at room temperature. The flow rate of air-ETS mixture through the bed was 4000 cm3/min. The relative humidity of the air was 50% and contained about 35 to 40 ppm of hydrocarbons as measured as methane-equivalent. The number of particles in the inlet air stream were in the range of 30,000 to 35,000 particles/cm3. About 60% of hydrocarbons present in ETS were removed at these operating conditions for a period of about 70 hours. Based on 15 adsorption and regeneration cycles, it was noted that the carbon bed did not loose its capacity for ETS significantly as indicated by the BET surface area and water adsorption data. At the beginning of an adsorption cycle, the carbon bed captured a significant number of particles. However, the bed rapidly lost its particle capture effciency as the experiment progressed. The number of particles in the outlet air stream was found to be the same as that of the inlet stream within five minutes.     

Transformation of sputtered calcium copper titanate thin film into nanorods by sequential annealing

Rapid synthesis of long calcium copper titanate (CCTO) nanorods was carried out by sequential annealing. CCTO thin films have been deposited on p-Si substrate by RF sputtering technique and afterwards, the samples were thermally treated using a preheated furnace by varying the annealing temperature from 850 °C to 1100 °C. CCTO nanorods of 12 µm lengths and 400–600 nm diameters were synthesized at 1100 °C. Based on the FESEM observations, a plausible growth mechanism has been proposed to explain the formation of nanorods. The (220) XRD peak of the CCTO film became prominent for the annealing temperature of 950 °C. The presence of nanoscale crystals in amorphous matrix has been observed by HRTEM studies. The elemental mapping of CCTO nanorod has shown a spatial variation of elements throughout the nanorod. The oxide and interface charge density was found to be increased with the rise in annealing temperature.     

Effect of Alumina Reactivity on the Densification and Properties of Al2O3–Cr2O3 Refractories

Alumina‐chrome (Al₂O₃–Cr₂O₃) refractories with Al₂O₃:Cr₂O₃ molar ratio 1:1 were synthesized in the temperature range of 1400–1700°C by conventional solid–oxide reaction route. The effect of different aluminas (viz., hydrated and calcined) on the densification, microstructure, and properties of Al₂O₃–Cr₂O₃ refractories was investigated without changing the Cr₂O₃ source. The starting materials were analyzed to determine the chemical composition, mineralogy, density, surface area, and particle size. Sintered materials were characterized in terms of densification, phase assemblage, and mechanical strength at room temperature and at higher temperatures. Microstructural evolution at different sintering temperature was correlated with sintering characteristics. It can be concluded that the Al₂O₃–Cr₂O₃ refractories prepared with hydrated alumina as Al₂O₃ source show better densification and hot mechanical strength than corresponding calcined variety.