Silver-plated polyamide fabrics with high electromagnetic shielding effectiveness performance prepared by in situ reduction of polydopamine and chemical silvering

In this article, the silver-plated polyamide fabrics (SPPAFs) with high electroconductibility and shielding effectiveness were fabricated by using in situ reduction of polydopamine and chemical silvering. The effects of SPPAFs dopamine (C₈H₁₁O₂N) and silver nitrate (AgNO₃) concentration on surface resistivity and electromagnetic interference shielding effectiveness were studied. The results showed that the surface resistivity of SPPAFs can reach a minimum value of 0.06 ± 0.014 Ω cm⁻¹, when C₈H₁₁O₂N concentration is 4 g L⁻¹ and the AgNO₃ concentration is 120 g L⁻¹. The shielding effectiveness of SPPAFs in the wide frequency range of 10–3000 MHz increases with the increase in the concentration of AgNO₃, and increases first and stabilizes afterward with increasing C₈H₁₁O₂N concentration. When the concentration of C₈H₁₁O₂N and AgNO₃ is 3 and 120 g L⁻¹, respectively, mean shielding effectiveness values in the low-, medium-, and high-frequency bands are 71.3, 73.8, and 76.1 dB, respectively. Moreover, the mean shielding effectiveness values is 83.79 dB in the frequency range of 1.2–2.3 GHz. The dominant shielding mechanism of SPPAFs is the reflected electromagnetic waves and the absorption shielding effectiveness is less than 2 dB. The average electromagnetic shielding values of SPPAFs are above 67 dB after 16 weeks of storage, when C₈H₁₁O₂N concentration is 4 g L⁻¹ and the AgNO₃ concentration is 80 and 100 g L⁻¹. The prepared SPPAFs show promising applications in military textiles and smart wearable clothing. © 2019 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2019 , 136, 48227.     

A new perspective of co-doping and Nd segregation effect on proton stability and transportation in Y and Nd co-doped BaCeO3

Bulk and surface properties of proton stability and transportation in Y and Nd co-doped BaCeO₃ (BCYN), especially the effect of Nd segregation, were investigated by first-principles calculations. Since the structure of doped BaCeO₃ at the operating temperature of proton-conducting has been unclear for a long time, we have summarized the latest experimental results and calculated the structure of the asymmetric BCYN for the first time. The results show that compared with Y, Nd doping promotes oxygen vacancy formation, however reduces proton stability. Our calculation can also provide a possible explanation for the formation of space charge layer at the grain boundary of doped BaCeO₃ in experiment. Unlike the stable Y in BCYN, Nd is calculated to be easily segregated, which can facilitate both proton hydration and proton transportation near the surface. Moreover, Nd segregation at the grain boundary is predicted to be beneficial for proton transportation between grains.     

高职生物化工专业"微生物学实验"的思政教学探索

为了响应"全员育人、全程育人、全方位育人"三全育人的重要举措,以及体现专业课程在立德树人方面的重要作用和对生物化工专业的认同,文中旨将专业知识与社会主义核心价值观有机的融合,润物细无声的对学生进行思政教育,积极探索微生物学实验中能够与思政元素相融合的切入点,一方面激发了学生的学习兴趣和自学潜能,提升了课堂教学效果和效率,另一方面达成了生物化工行业对高质量人才的需求.     

Synergistic flame retardant effects of activated carbon and molybdenum oxide in poly(vinyl chloride)

The synergistic effects of activated carbon (AC) and molybdenum oxide (MoO₃) in improving the flame retardancy of poly(vinyl chloride) (PVC) were investigated. The effects of AC, MoO₃ and their mixture with a mass ratio of 1:1 on the flame retardancy and smoke suppression properties of PVC were studied using the limiting oxygen index and cone calorimeter tests. It was found that the flame retardancy of the relatively cheaper AC was slightly weaker than that of MoO₃. In addition, the incorporation of AC and MoO₃ greatly reduced the total heat release and improved smoke suppressant property of PVC composites. When the total content of AC and MoO₃ was 10 phr, PVC/AC/MoO₃ had the lowest peak heat release rate and peak smoke production rate values of 173.80 kW m^?2 and 0.1472 m² s^?1, which represented reductions of 47.3 and 59.9%, respectively, compared with those of PVC. Furthermore, thermogravimetric analysis and gel content tests were used to analyze the flame retardant mechanism of AC and MoO₃, with results showing that AC could promote early crosslinking in PVC. Char residue left after heating at 500 °C was analyzed using scanning electron microscopy and Raman spectroscopy, and the results showed that MoO₃ produced the most compact char, with the smallest and most organized carbonaceous microstructures. © 2017 Society of Chemical Industry     

A facile method for preparation of PGS@ZB‐N and gas‐sol alternating synergistic effect for fire resistance of EVA

Through the simple precipitation of palygorskite (PGS) by zinc borate (ZB) (to make PGS@ZB) and the decoration of PGS@ZB by dodecylamine (N), a novel organic‐inorganic@inorganic hybrid flame retardant of PGS@ZB‐N was prepared and was incorporated with ethylene vinyl acetate copolymer (EVA) to improve its flame retardance. The structure and morphology of PGS@ZB‐N were characterized by Fourier transform infrared (FTIR) spectroscopy, X‐ray diffraction (XRD), and scanning electron microscopy (SEM), and it was confirmed that the PGS@ZB‐N hybrid had been successfully prepared. The flame retardancy and burning behavior of EVA/PGS@ZB‐N/EG (EG = expandable graphite) composite were studied through thermogravimetric analysis (TGA), limiting oxygen index (LOI), UL‐94 (by the vertical burning test), and cone calorimeter test (CCT) characterizations. The prepared EVA/PGS@ZB‐N/EG composite obtained an LOI value of 41.2% with the addition of 30 wt% PGS@ZB‐N/EG. It was found that EVA/PGS@ZB‐N/EG was protected through a gas phase and condensed phase alternating synergistic effect mechanism.