Phytoremediation has been proposed for the elimination of toxic metals in soil, yet little attention has been given to the performance of insects that feed on contaminant-tolerant plants. We tested the performance of two herbivores with different feeding behaviors, the cabbage looper, Trichoplusia ni, and the green peach aphid, Myzus persicae, reared on cadmium-tolerant Brassica juncea plants that contained different concentrations of cadmium. We also tested the performance of the aphid parasitoid Aphidius colemani developing in aphids reared on plants with different levels of cadmium. The hypothesis tested was that the chewing insect would be more negatively affected than the sucking insect, because of the localization of cadmium within the host plant, and that the aphid parasitoid would not be affected. We also compared the performance of T. ni on artificial diet with different levels of cadmium. Neither the phloem-feeding aphid nor its parasitoid was affected by cadmium in the host plant. The effects of cadmium on the foliage-feeding cabbage looper varied, with negative effects on development observed in experiments with artificial diet but not in those using natural host plants. These data, together with information available in the literature, support the idea that the effects of toxic metals present in a host plant may be influenced by a herbivore’s feeding strategy. However, a wide range of chewing and sucking species needs to be tested to confirm this hypothesis.     

Degradation behavior of mechanically fastened joints of glass-reinforced crosslinked polyester immersed in hot water

This study deals with the degradation of mechanically-fastened GFRP joints immersed in hot water (80°C). The material used was randomly oriented E-glass fiber continuous strand mat with a crosslinked polyester. Three kinds of joint geometries were adopted; thickness was 3 mm, hole diameter was 6 mm, the distance from hole center to top-edge was 18 mm (3e), and specimen widths were 18 (3w), 30 (5w), and 42 mm (7w). Failure modes of original dry specimens were a function of joint geometry, The dominant failure mode of 3w3e joints was net-tension, whereas 5w3e and 7w3e joints displayed bearing failure. As degradation progressed, the dominant failure mode gradually shifted from net-tension to bearing failure. Strength reduction was marked in 5w3e and 7w3e joints, in which the dominant failure mode was bearing. Joint strength and failure mode were predicted from the combination of a macroscopic failure criterion and characteristic curves obtained from tensile testing of rectangular specimens with holes, bearing tests, and finite element analysis. Predictions agreed with experiment.