Synthesis of amphiphilic magnetic microspheres by dispersion copolymerization of styrene and poly(ethylene oxide) macromonomer

Amphiphilic magnetic microspheres ranging in diameter from 5 to 100 µm were prepared by dispersion copolymerization of styrene and poly(ethylene oxide) vinylbenzyl (PEO‐VB) macromonomer (MPEO) in the presence of Fe₃O₄ magnetic fluid. The effects of various polymerization parameters on the average particle size were systematically investigated. The average particle size was found to increase with increasing styrene concentration and initiator concentration. It also increased with decreasing stabilizer concentration and molecular weight of MPEO. The content of the hydroxyl groups localized in the microspheres ranged from 0.01 to 0.2 mmol g^?1. © 2003 Society of Chemical Industry     

High-performance MIM capacitor using ALD high-k HfO/sub 2/-Al/sub 2/O/sub 3/ laminate dielectrics

For the first time, we successfully fabricated and demonstrated high performance metal-insulator-metal (MIM) capacitors with HfO/sub 2/-Al/sub 2/O/sub 3/ laminate dielectric using atomic layer deposition (ALD) technique. Our data indicates that the laminate MIM capacitor can provide high capacitance density of 12.8 fF//spl mu/m/sup 2/ from 10 kHz up to 20 GHz, very low leakage current of 3.2 /spl times/ 10/sup -8/ A/cm/sup 2/ at 3.3 V, small linear voltage coefficient of capacitance of 240 ppm/V together with quadratic one of 1830 ppm/V/sup 2/, temperature coefficient of capacitance of 182 ppm//spl deg/C, and high breakdown field of /spl sim/6 MV/cm as well as promising reliability. As a result, the HfO/sub 2/-Al/sub 2/O/sub 3/ laminate is a very promising candidate for next generation MIM capacitor for radio frequency and mixed signal integrated circuit applications.     

High-resolution photonics-based interference suppression filter with wide passband

A new topology for a photonic signal processor, which overcomes the basic recursive frequency response problem that limits the passband range, is presented. The structure is based on a new multiple-wavelength offset-cavity structure that is cascaded with a series of unbalanced delay line structures. This not only can synthesize a very narrow notch response with good shape factor but also permits a multifold extension of the free spectral range (FSR) and passband width. Results on the interference mitigation filter demonstrate a stopband of 1% of center frequency and a fourfold increase in the FSR and passband width, while also having a very small shape factor, in excellent agreement with predictions.     

Phosphorus‐containing polyaryloxydiphenylsilanes with high flame retardance arising from a phosphorus–silicon synergistic effect

Polyaryloxydiphenylsilanes were prepared from phosphorus‐containing diols and diphenydichlorolsilane through solution polymerization. With a stoichiometric imbalance in feed monomers, the resulting polymers exhibited moderate melting points and good processing properties. The polymers prepared showed initial decomposition temperatures above 340 °C, excellent thermal stability, high char yields at 850 °C and very high limited oxygen index values of 56–59. The polymers' char yields and their (P + Si) contents showed linear relationships. © 2003 Society of Chemical Industry     

Cure of malignant ascites and generation of protective immunity by monoclonal antibody-targeted activation of a glucuronide prodrug in rats

We examined the in vivo efficacy of targeting beta-glucuronidase (betaG) to activate a glucuronide prodrug (BHAMG) of p-hydroxyaniline mustard (pHAM) at hepatoma ascites in Sprague-Dawley rats. Injection i.p. of 500 microg RH1-betaG, a conjugate formed between recombinant betaG and monoclonal antibody RH1 with specificity for an antigen expressed on AS-30D rat hepatoma cells, into rats bearing AS-30D ascites resulted in the accumulation of 54 microg conjugate per 10(9) tumor cells after 2 hr. Ascites fluid and serum contained 0.53 and 0 microg/ml, respectively, RH1-betaG 2 hr after injection of the conjugate. Conjugate binding to AS-30D cells was heterogeneous and non-saturated, as determined by flow cytometry. BHAMG was less toxic than pHAM to SD rats based on measures of animal mortality, weight loss and hematological toxicity. Treatment of rats bearing established hepatoma ascites with 500 microg RH1-betaG followed 2 hr later with a single i.p. injection of 30 mg/kg BHAMG or 3 i.p. injections of 10 mg/kg BHAMG 2, 3 and 4 hr later resulted in the cure of 6/8 and 8/8 animals, respectively. Treatment with BHAMG or pHAM alone did not produce cures, whereas treatment with a control antibody-betaG conjugate and BHAMG produced significantly greater hematological toxicity compared to treatment with RH1-betaG and BHAMG. All cured rats were completely protected from rechallenge with 2 x 10(7) AS-30D cells, indicating that successful treatment of animals induced protective immunity.     

Epidermal growth factor induces terminal differentiation in human epidermoid carcinoma cells

In this study, spermatogenesis in the adult Djungarian hamster is described. Undifferentiated spermatogonia topographically arranged as Asingle (A(s)), Apaired (Apr), and Aaligned (Aal) spermatogonia were observed, as were six generations of differentiating spermatogonia (A1, A2, A3, intermediate, B1, and B2). The differentiating spermatogonia divided at regular intervals during the cycle of the seminiferous epithelium. Mitosis of these cells was observed at the transition from stage IX to stage X (mitosis of A1 into A2 spermatogonia), at the transition from stage XII to stage I, at the transition from stage II to stage III, at the transition from stage IV to stage V, at the end of stage VI, and at approximately the middle of stage VII. Cellular associations in the cycle of the seminiferous epithelium are described. The seminiferous epithelium was divided into 12 stages, based upon the developmental steps in spermiogenesis, and the frequency of these stages was determined. The duration of the cycle of the seminiferous epithelium, determined by [3H]thymidine incorporation, was shown to be 7.90 +/- 0.01 (mean +/- SEM) days.     

Effect of misalignment on electrical characteristics of ACF joints for flip chip on flex applications

The effect of misalignment on the electrical properties of anisotropic conductive film (ACF) joints is investigated in this work. It is found that along with the increase of misalignment, the connection resistance of ACF joints increases. When the misalignment in x-direction is less than 5 μm, the increase rate of connection resistance is quite large. Then, along with the severity of misalignment, the increase rate becomes smaller. Finally, when the misalignment is close to 20 μm, the increase rate rises again. The Holm's electric contact theory is used for understanding the connection resistance variation. On the other hand, with the increase of misalignment in x-direction, the insulation resistance between ACF joints decreases. If the misalignment exceeded 10 μm, the decrease is prominent for the Ni particle ACF joints. This phenomenon can be explained by the effect of dielectric damage of the epoxy.Computer programs are also developed to calculate the variation of the probability of open and shorting after misalignment and predicate the maximum misalignment tolerance. The results show that the open and shorting probability increase abruptly after misalignment. On the view of pad parameters, the open probability is mainly related to the pad area, while the pads gap is critical to the shorting probability. Large pads gap (small pad width) can reduce the shorting probability obviously. On the other hand, enlarging the pad area by increasing pad length decreases the open probability significantly. So comparing to square shape pad, rectangle shape pad can reduce the failure probability greatly.     

High temperature controlled atmosphere experiments for catalysts in a transmission electron microscope

A new transmission electron microscopy (TEM) specimen preparation procedure for high temperature experiments using a controlled atmosphere specimen holder (HTCASH) has been developed. It is designed for studying the microstructure of catalyst specimens before and after treatments in various gases. The procedure involved (1) finding a new formula for the embedding material, (2) devising a new method of making specimen supports, and (3) developing a method for removing the embedding material after the specimen has been microtomed. These techniques were then brought together to produce the ideal specimens for the HTCASH experiments. As an extra benefit, this procedure is also suitable for preparing specimens for ultrahigh resolution imaging experiments. The application of the new procedure in HTCASH experiments is illustrated through a high temperature reduction of a Co/SiO₂-923 catalyst.