利用2、4和14mm的X60钢紧凑拉伸试样进行同样应力水平、固定应力比（R＝0．1）的疲劳裂纹扩展试验，揭示出高韧性管道钢的疲劳裂纹扩展存在显著的厚度效应。由于应力水平低，相应的离面应力也低，不足以导致分层开裂，因此，裂纹端部的三维应力约束随厚度增加而增大。4mm试样的疲劳裂纹速率远高于2mm试样，但厚度再增大，裂纹扩展速率不再有显著变化。进一步对表面裂纹试样进行疲劳裂纹扩展试验，并用勾线法纪录裂纹扩展情况，利用穿透裂纹的da/dN-ΔK曲线预测表面裂纹扩展，用2mm厚试样的数据控制裂纹表面长度的扩展，用14mm厚试样的数据控制裂纹底部沿厚度方面的扩展，得到了与表面裂纹扩展实验吻合很好的预测结果。     

联产供冷与电力供冷能耗比较分析

文中将两种供冷能耗比较分解成用电煤耗差、用热煤耗量、增加产汽用电煤耗量三部分进行分析，按照热量法得出在目前一般情况下联产供冷比电力供冷通常费能和定性定量结论，为全面研究比较热电冷联产与分产的能耗奠定一个基础。     

Trace elements in particles of motor vehicle exhaust in Shanghai

A nuclear microprobe with high spatial resolution and high analytical sensitivity was applied to analyze trace elements,especially lead,in vehicle exhaust of Shanghai city.The result shows that the chemical composition and its corresponding x-ray relative intensity are different among different vehicle exhausts.There are many kinds of metal elements in particles of vehicle exhaust.most are harmful to people,such as Ti,Cr,Mn,Pb,etc.We found that the lead concentration was 6820μg/g and the bromine concentration was 5300μg/g in the exhaust from Santana using leaded gasoline(SULG).which is higher than any other kinds of vehicle exhausts.We have also detected the minimum lead in the particles of unleaded gasoline and its content varies from one to another.Its mean concentration was 450μg/g and the highest reached 6210μg/g.The unleaded gasoline‘s Pb existed in the whole particle while the leaded gasoline‘s enriched in the surface of the particle and was more harmful to the human beings.     

JOINING MECHANISMS OF β''''-Al2O3 CERAMIC AND PYREX GLASS TO Al MATRIX COMPOSITE

The bonding of β'-Al2O3 and pyrex glass to Al matrix composites by anodic bonding process is achieved. The microstructure of the bonded interface and the joining mechanisms are analyzed with scanning electron microscope (SEM), energy dispersive X-ray fluorescence spectrometer (EDX). It is observed that the bonding region across the interface consists of the metal layer, oxide transitional layer and the ceramic layer, with the transitional layer composed of surface region and sub-surface region. The bonding process can mainly be categorized into anodic bonding process and solid state diffusing process. The pile-up of the ions and its drift in the interface area are the main reasons for anode oxidation and joining of the interface. The temperature, voltage and the drift ions in the ceramic or glass during the bonding process are the essential conditions to solid state diffusing and oxide bonding at the interface. The voltages, temperature, pressure as well as the surface state are the main factors that influence the anodic bonding.     

交联透明质酸的降解及其释药性能

用己二酸二酰肼（ADH）对透明质酸（HA）进行化学修饰，制备交联透明质酸（HA-ADH）薄膜。粘度法测试表明HA-ADH是一种可降解的生物材料，并且与HA相比，HA．ADH的降解速率减慢。在此基础上，研究了以疏水性的替硝唑（TDZ）和亲水性的头孢唑啉钠（CEZ）为模拟药物的HA-ADH药物载体薄膜的释药性能。紫外-可见（UV-Vis）吸收光谱检测表明，HA-ADH是一种疏水性药物TDZ的优良缓释制荆，这是由于TDZ的疏水性和HA-ADH薄膜的缓慢溶胀和降解性能的结合而得到的，药物的释放主要受扩散机制控制。     

Preparation and Compressive Stress Effect of Polymer Matrix RE-Fe Giant Magnetostrictive Composite

Polymer matrix RE-Fe giant magnetostrictire composite （GMPC） was prepared using bonding and magnetic field forming technique, and magnetostriction of samples was measured for different compressive stress. The experimental results show thai there is certain compressive effect in GMPC. And the influence of compressive stress on magnetostriction of sample was investigated. It offers essential reference for application and device design of GMPC.     

碳酸盐岩气藏加砂压裂重复改造试验效果分析

针对碳酸盐岩气藏部分气井生产效能低的状况，决定在长庆气田下古生界尝试开展加砂压裂重复改造试验，以期提高低产、低效气井的产量，延长气田稳产期。通过潜心研究、精细设计及现场质检监控，优选了4口老井进行加砂压裂重复改造现场试验。从试验结果来看，虽然只有1口井取得明显的改造效果，但4口井加砂压裂施工都是成功的，说明对碳酸盐岩气藏实施加砂压裂是可以实现的，但在选井思路和压裂工艺方面还有待探索和研究。     

PURIFICATION AND PROPERTIES OF TRANSGLUTAMINASE FROM STREPTOVERTICILLIUM MOBARAENSE

Transglutaminase (TGase) was separated from the culture broth of an isolated strain of Streptoverticillium mobaraense. The crude enzyme was prepared by centrifugation, ultrafiltration, precipitation by alcohol, centrifugation and freeze‐drying. The yield after these processes was 65–70%. Then the enzyme was purified to homogeneity by chromatography on CM‐cellulose and Sephadex G‐75 on which the yields were about 70% and 80%, respectively; the purified folds reached 2.5–4.7 and 1.08–2.06, respectively. The molecular weight of this TGase was 39,500–40,100 Da by gel filtration chromatography. Optimum enzyme activity was observed in the pH range of 5.0–7.0, and it was maintained stable at 20–40C. The optimal temperature and pH was 52C and 6.0, respectively. At 1 mM and 5 mM metal ion or inhibitors concentration, TGase activity was strongly inhibited by Zn²⁺ and NEM, and not affected obviously by Ba²⁺, Ca²⁺, Co²⁺, Cu²⁺, Fe²⁺, Fe³⁺, Mg²⁺, Mn²⁺, Na⁺ as well as PMSF and EDTA. The effects of these additions on this TGase were compared with those of other microbial TGases.     

公司大门工程建设施工

大门小品建筑属多项目综合性工程。本文作者从管理者的角度 ,通过对公司大门及附属工程施工质量控制的总结 ,说明了质量控制应贯穿于工程施工的全过程     

透反液晶显示器

兼有透射型和反射型液晶显示优点的透反液晶显示可工作于透射和反射两种显示模式，它将广泛应用于手机、PDA等通讯领域。透反液晶显示可分为单盒厚和双盒厚两大类。又可分为扭曲型和非扭曲型两种。为了研制出高性能透反液晶显示器，需解决透反两个显示区的响应时间、光效率、色饱和度的差异以及视角等问题。文中介绍了Sharp公司开发的2种基本的透反液晶显示。以及3种新近开发的高性能透反液晶显示。随着应用市场的扩大和技术的进步，透反液晶显示将会进一步得到发展。