Techniques for microstructural characterization of powder-processed nickel-based superalloys

Methods are described for sample preparation of polycrystalline Ni-based superalloys in order to perform a detailed microstructural characterization. Specific techniques for the precise definition of the various phases present are outlined and these are shown to be useful for the measurement of size, volume fractions and distribution. A number of optical, scanning and transmission microscopy techniques are used to provide the necessary information.     

Wear and Creep Characteristics of a Carbon‐Derived Si3N4/SiC Micro/Nanocomposite

In the presented work some properties of a recently developed Si₃N₄/SiC micro/nanocomposite have been investigated. The material was tested using a pin on disc configuration. Under unlubricated sliding conditions using Si₃N₄ pin at 50 % humidity, the friction coefficient was in the range of 0,6 ‐ 0,7. The reduction of humidity resulted in a lower coefficient of friction, in vacuum the coefficient of friction had a value of about 0,6. The wear resistance in vacuum was significantly lower then that in air. The wear patterns on the Si₃N₄+SiC disc revealed that mechanical fracture was the wear controlling mechanism. Creep tests were realized in four point bending configuration in the temperature interval 1200‐1400 °C at stresses 50,100 and 150 MPa and the minimal creep deformation rate was established for each stress level. The activation energy, established from the minimal creep deformation had a value of about 360 kJ/mol and the stress exponent values were in the range of 0.8‐1.28. From the achieved stress exponents it can be assumed that under the studied load/temperature conditions the diffusion creep was the most probable creep controlling mechanism.     

Thin microwire with negative magnetostriction in a zero magnetic field

The effect of residual mechanical stresses on the distribution of magnetization in thin metal microwires with negative magnetostriction has been studied in a zero magnetic field. It is established that the microwire has a nonzero residual magnetization in the absence of twisting and bulging rotational modes.     

Problems of Wastewater Treatment and Methods of Solving Them

The studies show that in the combined use of biological and chemisorption stages of treatment, a deeper degree of removal of industrial pollutants from wastewaters is attained. The chemisorption stage allows stabilizing the treatment process in different concentration-temperature drops and increasing the degree of removal of synthetic surfactants (SSF), petroleum products, and nitrogen compounds. The possibility of regulating the selectivity of the treatment process by varying the composition of the chemisorption material is demonstrated.     

Hf-doped and NH/sub 3/-nitrided high-K gate dielectric thin film with least drain current degradation and flatband voltage shift

A novel technique to form high-K dielectric of HfSiON by doping base oxide with Hf and nitridation with NH/sub 3/, sequentially, is proposed. The HfSiON gate dielectric demonstrates excellent device performances such as only 10% degradation of saturation drain current and almost 45 times of magnitude reduction in gate leakage compared with conventional SiO/sub 2/ gate at the approximately same equivalent oxide thickness. Additionally, negligible flatband voltage shift is achieved with this technique. Time-dependent dielectric breakdown tests indicate that the lifetime of HfSiON is longer than 10 years at V/sub dd/=2 V.     

X-Ray Study of the Effect of Heat on the Structural Parameters of Armos Fibres

In studying a series of fibre samples spun in steady-state conditions, the following was found: as a function of the conditions of processing Armos fibre, two structural modifications of the polymer can form; intensive crystallization of the modification corresponding to the 28.7° reflection begins in heat treatment above 220°C; above 320°C, intensive crystallization of the modification corresponding to the 14.25° reflection is observed; at 360°C, symbatic enhancement of the intensities of both reflections with a weak change in the other structural parameters of the fibre is observed.     

Development of a Continuous Segmented Flow Tubular Reactor and the “Scale‐out” Concept – In Search of Perfect Powders

The synthesis of powders with controlled shape and narrow particle size distributions is still a major challenge for many industries. A continuous Segmented Flow Tubular Reactor (SFTR) has been developed to overcome homogeneity and scale‐up problems encountered when using batch reactors. Supersaturation is created by mixing the co‐reactants in a micromixer inducing precipitation; the suspension is then segmented into identical micro‐volumes by a non‐miscible fluid and sent through a tube. These micro‐volumes are more homogeneous when compared to large batch reactors leading to narrower size distributions, better particle morphology, polymorph selectivity and stoichiometry. All these features have been demonstrated on single tube SFTR for different chemical systems. To increase productivity for commercial application the SFTR is being “scaled‐out” by multiplying the number of tubes running in parallel instead of scaling‐up by increasing their size. The versatility of the multi‐tube unit will allow changes in type of precipitate with a minimum of new investment as new chemistry can be researched, developed and optimised in a single tube SFTR and then transferred to the multi‐tube unit for powder production.     

Reliability investigation of 0.07-/spl mu/m InGaAs-InAlAs-InP HEMT MMICs with pseudomorphic In/sub 0.75/Ga/sub 0.25/As channel

The authors have investigated the reliability performance of G-band (183 GHz) monolithic microwave integrated circuit (MMIC) amplifiers fabricated using 0.07-/spl mu/m T-gate InGaAs-InAlAs-InP HEMTs with pseudomorphic In/sub 0.75/Ga/sub 0.25/As channel on 3-in wafers. Life test was performed at two temperatures (T/sub 1/ = 200 /spl deg/C and T/sub 2/ = 215 /spl deg/C), and the amplifiers were stressed at V/sub ds/ of 1 V and I/sub ds/ of 250 mA/mm in a N/sub 2/ ambient. The activation energy is as high as 1.7 eV, achieving a projected median-time-to-failure (MTTF) /spl ap/ 2 /spl times/ 10/sup 6/ h at a junction temperature of 125 /spl deg/C. MTTF was determined by 2-temperature constant current stress using /spl Delta/G/sub mp/ = -20% as the failure criteria. The difference of reliability performance between 0.07-/spl mu/m InGaAs-InAlAs-InP HEMT MMICs with pseudomorphic In/sub 0.75/Ga/sub 0.25/As channel and 0.1-/spl mu/m InGaAs-InAlAs-InP HEMT MMICs with In/sub 0.6/Ga/sub 0.4/As channel is also discussed. The achieved high-reliability result demonstrates a robust 0.07-/spl mu/m pseudomorphic InGaAs-InAlAs-InP HEMT MMICs production technology for G-band applications.