Mechanism of Magnetite Seam Formation and its Role for FeO Scale Transformation

The phase transformation behavior of a thermally grown oxide scale of FeO on pure-Fe and an Fe–2wt%Au alloy was investigated. Particular attention was paid to formation of a magnetite seam, which is the Fe₃O₄ layer formed at the FeO/alloy interface at an initial stage of the phase transformation, since it has important effects on the overall phase transformation of FeO scale. A thin Au(Fe) layer was found to develop on the Fe–Au alloy at the FeO/alloy interface after 32 min of oxidation at 750 °C in air. This Au(Fe) layer prevented formation of a magnetite seam and accelerated the FeO eutectoid reaction. The Au(Fe) layer acted as a “chemical diffusion barrier” for inward diffusion of Fe from the FeO to the alloy substrate across the FeO/alloy interface and prevented magnetite seam formation.     

Nanostructured poly(3-hexylthiophene-2,5-diyl) films with tunable dimensions through self-assembly with polystyrene

Poly(3-hexylthiophene-2,5-diyl) is among the most widely used conjugated polymers for opto-electronic applications. To enhance its properties, researchers have attempted to nanostructure this polymer using various processes including breath figure arrays, nanolithography and elaborated organic synthesis. We here demonstrate a simple process to nanostructure the conjugated polymer using self-assembly with polystyrene and selective removal of one of the phases. The influence of the molecular weight of each polymer on the thin film morphology was systematically studied by atomic force microscopy. Using this approach, we observe two types of nanostructure, namely, nanoporous and nanoisland structures, of which the dimensions can be tuned by modifying the molecular weight of each polymer in the blend. This simple process introduces a cost-effective alternative to produce thin films of conjugated polymer with average nano-features from 100 nm up to 500 nm which could be used in a wide range of applications.     

The Complete Loss of p53 Expression Uniquely Predicts Worse Prognosis in Colorectal Cancer

p53 immunohistochemistry is considered an accurate surrogate marker reflecting the underlying TP53 mutation status and has utility in tumor diagnostics. In the present study, 269 primary CRCs were immunohistochemically evaluated for p53 expression to assess its utility in diagnostic pathology and prognostication. p53 expression was wild-type in 59 cases (23%), overexpressed in 143 cases (55%), completely lost in 50 cases (19%), and cytoplasmic in 10 cases (4%). p53 immunoreactivity was associated with tumor size (p = 0.0056), mucus production (p = 0.0015), and mismatch repair (MMR) system status (p < 0.0001). Furthermore, among CRCs with wild-type p53 expression, a significantly higher number of cases had decreased CDX2 than those with p53 overexpression (p = 0.012) or complete p53 loss (p = 0.043). In contrast, among CRCs with p53 overexpression, there were significantly fewer ALCAM-positive cases than p53 wild-type cases (p = 0.0045). However, no significant association was detected between p53 immunoreactivity and the “stem-like” immunophenotype defined by CDX2 downregulation and ALCAM-positivity. Multivariate Cox hazards regression analysis identified tubular-forming histology (hazard ratio [HR] = 0.17, p < 0.0001), younger age (HR = 0.52, p = 0.021), and female sex (HR = 0.55, p = 0.046) as potential favorable factors. The analysis also revealed complete p53 loss (HR = 2.16, p = 0.0087), incomplete resection (HR = 2.65, p = 0.0068), and peritoneal metastasis (HR = 5.32, p < 0.0001) as potential independent risk factors for patients with CRC. The sub-cohort survival analyses classified according to chemotherapy after surgery revealed that CRC patients with wild-type p53 expression tended to have better survival than those with overexpression or complete loss after chemotherapy. Thus, immunohistochemistry for p53 could be used for the prognostication and chemotherapy target selection of patients with CRC.     

黄土包气带土壤水特征曲线研究

本文主要介绍在中国辐射防护研究院野我试验场从地表到潜水ｍ深范围内４６个土芯样的水特征曲线的测量方法及测量结果。     

Aging and Clonal Behavior of Hematopoietic Stem Cells

Hematopoietic stem cells (HSCs) are the only cell population that possesses both a self-renewing capacity and multipotency, and can give rise to all lineages of blood cells throughout an organism’s life. However, the self-renewal capacity of HSCs is not infinite, and cumulative evidence suggests that HSCs alter their function and become less active during organismal aging, leading ultimately to the disruption of hematopoietic homeostasis, such as anemia, perturbed immunity and increased propensity to hematological malignancies. Thus, understanding how HSCs alter their function during aging is a matter of critical importance to prevent or overcome these age-related changes in the blood system. Recent advances in clonal analysis have revealed the functional heterogeneity of murine HSC pools that is established upon development and skewed toward the clonal expansion of functionally poised HSCs during aging. In humans, next-generation sequencing has revealed age-related clonal hematopoiesis that originates from HSC subsets with acquired somatic mutations, and has highlighted it as a significant risk factor for hematological malignancies and cardiovascular diseases. In this review, we summarize the current fate-mapping strategies that are used to track and visualize HSC clonal behavior during development or after stress. We then review the age-related changes in HSCs that can be inherited by daughter cells and act as a cellular memory to form functionally distinct clones. Altogether, we link aging of the hematopoietic system to HSC clonal evolution and discuss how HSC clones with myeloid skewing and low regenerative potential can be expanded during aging.     

Experimental study of impingement cooling by heat sinks with thin longitudinal fins for LSI packages

This paper reports on the impingement cooling characteristics of a heat sink with thin longitudinal fins of 0.2 mm thickness, which are spaced with a fin-pitch in the range 0.5 mm to 2.0 mm. The air cooling of the heat sink comes from a slot-shaped orifice positioned above the heat-sink center. The breadth of the gap between the fin tops and the inlet orifice is in the range 0 mm to 10 mm. The thermal resistance of the thin longitudinal fins used is about 50% to 57% that of the thick longitudinal fins now in commercial use. The cooling performance of the thin-plate fins is almost the same as that of optimally arranged pin-fins with the same total surface area. A maximum value of six times the heat transfer rate of a single flat plate having the same base area was observed for the thin-plate fins. A comparison of cooling performance between impingement and channel flow systems was conducted. The performance of impingement cooling systems is almost unaffected by the breadth of the gap between the fin tops and the inlet orifice (or, for channel cooling, the upper wall). On the other hand, the performance of channel-cooling systems decreases significantly as the gap widens. © 1997 Scripta Technica, Inc. Heat Trans Jpn Res, 25(7): 449–459, 1996     

Effect of morphology on shear viscosity for binary blends of polycarbonate and polystyrene

The structure and rheological properties of binary blends of polycarbonate (PC) and polystyrene (PS) were investigated using various PS samples with different molecular weights, namely PS1k (M_w = 1,000), PS53k (M_w = 53,000), and PS240k (M_w = 240,000). The blends with PS53k and PS240k show phase-separated structures, whereas the blend with PS1k is miscible. The shear viscosity decreases greatly on addition of PS53k and PS240k, especially at high shear rates, which would be a great advantage at processing operations. Because the nonlinear response occurs in the small strain region for multilayered films of PC and PS240k, the origin of the significant viscosity drop for the phase-separated system is interfacial slippage at the phase boundary.     

Surface improvement on water and oil affinities and absorption rate of PVA/Tung oil-coated paperboard and fiberboard

A novel coating material on paperboard and fiberboard from poly(vinyl alcohol) (PVA) modified with Tung oil was developed. The PVA/Tung oil coating was cured at several conditions: 25, 40, 50, and 60°C, in the presence of two types of catalysts, i.e., thermal catalyst using potassium persulfate (KPS) and redox catalyst using KPS and sodium thiosulfate. The chemical crosslinked structure of PVA/Tung oil-coating films was confirmed by FTIR. The result indicated the decrease in the double bonds of Tung oil by crosslinking reaction, especially at 60°C. In comparison with the same curing temperature, the films with redox catalyst showed more reduction in the number of double bonds of Tung oil. DMA results of the PVA/Tung oil-coating materials with redox catalyst showed the lowering of the heights of both β transition peak of Tung oil and α transition peak of PVA. FTIR and DMA results confirmed the more efficient crosslinking reaction of redox catalytic system than that of the thermal catalytic system. The water resistance and mechanical properties of these coating materials exhibited better values as projected to higher curing temperature and redox catalyst. SEM images showed the smooth surface of PVA/Tung oil covered on the paperboards with ~72 µm in thickness. The contact angle of water or oil drop and dynamic change in contact angle on the surfaces of PVA/Tung oil-coated paperboards and fiberboards were investigated. The results show the contact angles for both water and oil were lower than those of the uncoated ones, indicating the improvement of water and oil affinities of the PVA/Tung oil-coating materials. The dynamic changes in contact angle of the coated ones also decreased, suggesting the reduction in water and oil absorption rates of these coated substrates.     

Optical Properties of Dysprosium-Doped Low-Phonon-Energy Glasses for a Potential 1.3 μm Optical Amplifier

Dysprosium-doped glasses were prepared in the system of gallium-based sulfide, tellurite, zirconium-baed and indium-based fluorides and their optical properties were studied. From the absorption cross sections of five f-f bands, three Judd-Ofelt parameters, ω _t ( t = 2, 4, 6), of Dy³⁺ ion were determined. The compositional variaton of the ω₂value showed the order sulfide > tellurite > fluorozirconate > fluoroindate, whereas the ω₆ value showed the opposite tendency. Compositional variaton of the fluorescence intensity ratio of the (⁴F_9/2⁶H_13/2)/(⁴F_9/2)→⁶H_15/2) is explained by the ratio of ω₂/ω₆ of doped Dy³⁺. The emission probabilities A and the branching ratio β from ⁶H_9/2 and ⁶F_11/2 levels, which are the doublet initial level of the 1.3 μm luminescence, were calculated for the glasses, and it was found that both values showed a tendency similar to that of ω₂ against the glass composition. In the sulfide glass, A was 2.6 × 10³S^-1 and β was 93%, both the highest in all of the glasses investigated. By 1.06 μm pumping of a Nd: YAG laser, the sulfide glass showed strong 1.3 μm emission and the lifetime was 25 μs, resulting in a quantum efficiency of 7%. This value is higher than that of the Pr³⁺:¹G₄ level in ZBLAN glass with β= 60%.