Cyclic thermal shock resistance of h-BN composite ceramics with La2O3–Al2O3–SiO2 addition

The effects of La₂O₃–Al₂O₃–SiO₂ addition on the thermal conductivity, coefficient of thermal expansion (CTE), Young's modulus and cyclic thermal shock resistance of hot-pressed h-BN composite ceramics were investigated. The samples were heated to 1000 °C and then quenched to room temperature with 1–50 cycles, and the residual flexural strength was used to evaluate cyclic thermal shock resistance. h-BN composite ceramics containing 10 vol% La₂O₃–Al₂O₃ and 20 vol% SiO₂ addition exhibited the highest flexural strength, thermal conductivity and relatively low CTE, which were beneficial to the excellent thermal shock resistance. In addition, the viscous amorphous phase of ternary La₂O₃–Al₂O₃–SiO₂ system could accommodate and relax thermal stress contributing to the high thermal shock resistance. Therefore, the residual flexural strength still maintained the value of 234.3 MPa (86.9% of initial strength) after 50 cycles of thermal shock.     

Association of solid fuel use with risk of stunting in children living in China

Stunting adversely affects physical and mental outcomes of children. It has not been examined whether household air pollution from solid fuel combustion is a risk factor for stunting in children. In a total of 41,439 children aged 6-17 across China, height was measured using a unified protocol. Multivariable linear regression models and logistic regression models were used to assess the associations of solid fuel use for cooking/heating with stunting in children. Adjusted for covariates, cooking/heating with solid fuel was significantly associated with a lower z-score for height for age and sex (β = −0.21 [−0.32 to −0.09] and −0.17 [−0.31 to −0.03], respectively) and an increased risk of stunting with an estimated ORs of 1.34 [1.07~1.68] and 1.37 [1.02~1.83], respectively. The risk of stunting associated with solid fuel use was statistically significant in high-age children. And the effect was greater on girls than on boys, though the difference was not statistically significant. Our study suggested that Chinese children living in households using solid fuel had a significantly higher risk of stunting than those living in households using cleaner fuel.     

裂缝性孔隙介质频变AVAZ反演方法研究进展

由于尺度的限制,利用地震方法进行裂缝参数定量表征一直是地球科学的难题。基于裂缝性孔隙介质动态等效理论的频变AVAZ反演方法给出了研究思路。首先介绍了裂缝性孔隙介质的等效介质理论研究进展,分析比较了各种裂缝性储层岩石静态等效介质模型和动态等效介质模型;然后给出了基于Chapman模型的裂缝参数和渗透率定量表征的正问题数学模型以及反演问题求解的方法和策略,以及基于模型数据的数值计算结果;最后讨论了频变AVAZ反演方法目前存在的问题和进一步研究方向。     

A dense and compact laser cladding layer with solid metallurgical bonding significantly improved corrosion resistance of Mg alloy for engineering applications

Although Mg alloy attracts great attention for engineering applications because of high specific strength and low density, low corrosion resistance limits its extensive use. In this study, Mg–Al–Zn–Mn alloy was treated via a laser cladding process to generate a dense and compact laser cladding layer with solid metallurgical bonding on the substrate for improving corrosion resistance, effectively hindering the corrosion pervasion into Mg alloy. The corrosion current density declined from 103 μA/cm² for Mg alloy to 13 μA/cm² for the laser cladding layer in NaCl aqueous solution. Moreover, the laser cladding layer was slightly corroded in comparison with Mg alloy in NaCl aqueous solution. Besides, the microhardness of the cladding layer reached a mean value of 170.5 HV, 3.1 times of Mg alloy (56.8 HV) due to the in situ formation of hardening intermetallic phases. Wear resistance of laser cladding layer was also obviously improved. These results demonstrated that the laser cladding layer obviously enhanced anticorrosion property of Mg alloy for engineering applications.     

Formation of a protective layer against corrosion on Mg alloy via alkali pretreatment followed by vanillic acid treatment

Although Mg alloy possesses high specific strength, low density, and good biocompatibility, poor corrosion resistance hinders its further applications. In the present study, an innovative protective layer against corrosion was prepared on the AZ31 Mg alloy via alkali pretreatment followed by vanillic acid treatment. The alkali pretreatment supplied –OH for the AZ31 Mg alloy surface to react with vanillic acid. The vanillic acid treatment played a crucial role in enhancing the corrosion resistance due to the excellent ability to act as a barrier and retard aqueous solution penetration, which effectively isolated the underlying Mg alloy from the corrosive environment. The corrosion current density of alkali and vanillic acid-treated Mg alloy (AZ31V) almost showed two orders of magnitude lower values in comparison with that of the AZ31 Mg alloy, and the corrosion potential of AZ31V Mg alloy increased from −1.41 to −1.25 V. The immersion tests proved that there was no occurrence of severe corrosion. Hence, the alkali pretreatment and vanillic acid treatment may represent a promising method to improve the corrosion resistance of Mg alloy.     

小像元红外探测器读出电路设计研究

介绍了基于SMIC 0.18 μm 3.3 V工艺设计研究的第一款小像元红外探测器读出电路,间距10 μm,规模1024×1024。文章详细介绍了像素输入级以及列级、输出级运放的设计,为提高线性摆伏,设计选用了低阈值NMOS管nmvt 33,仿真分析证明低阈值管nmvt 33的噪声性能优于普通管n 33；版图设计对关键信号线和敏感点采取隔离处理措施,对像元间串扰进行了仿真分析,有效控制了信号串扰。电路经测试使用各项功能正常,最大电荷处理能力达到4.3 Me-,动态范围≥65 dB,读出速率达到10 MHz,性能指标满足设计要求。     

Anchoring single Pt atoms on hollow Ag3VO4 spheres for improved activity towards photocatalytic H2 evolution reaction

The high cost of noble metal catalysts has been a great bottleneck for the catalyst industry. Using the noble metal at a single-atom level for catalytic applications could dramatically decrease the cost. The impacts of single Pt atoms on the photocatalytic performance of Ag₃VO₄ have been investigated and reported. In this report, single Pt atoms were anchored on the surface of Ag₃VO₄ (AVO) as a cocatalyst, and the resultant composite photocatalyst has been studied for photocatalytic H₂ production from water driven by visible light. The as-prepared AVO particles are hollow nanospheres in the monoclinic phase with a bandgap of 2.20 eV. The light absorption edge of AVO/Pt is slightly red-shifted compared to that of the pristine AVO, indicating more visible light absorption of AVO/Pt. The XPS peaks of Ag, V, and Pt exhibit a significant shift after AVO and Pt get into contact, suggesting the strong interaction between the surface Ag and V atoms, and single Pt atoms. After 3-h illumination, the photocatalytic H₂ evolution amount from AVO/Pt is improved up to 1400 μmol, which is 2.8 times that on the bare AVO. Such efficient photocatalytic H₂ evolution on AVO/Pt is still maintained after five reaction cycles. The better photocatalytic performance of AVO/Pt has been attributed to the more efficient visible light utilization and the lower interfacial charge transfer resistance, as demonstrated in the DRS and EIS spectra. The presence of the surface Pt atoms also leads to a higher amount of reactive radicals, which could efficiently promote the surface redox reactions.